The influence of milling parameters on the characteristics of milled and spray-dried NiCoCrAlY–Al 2 O 3 composite powders

Spray-drying process was selected to agglomerate ball milled NiCoCrAlY–Al₂O₃ composite powders. The effect of the starting alloy powder size on the morphology of composite powder was studied. The parameters of milling were optimised by orthogonal experiment to improve the powder's flowability and apparent density. Then the optimised powder was sprayed by air plasma spray to prepare NiCoCrAlY–Al₂O₃ composite coating. The results showed that the size distribution of starting particles decided the deformation of alloy particles and the characteristics of agglomerated powders eventually. With the decreasing size range of the starting alloy particles, the sphericity of agglomerated powders increased. The optimised milling parameters were as follows: solid content, 60 wt-%; BPR, 4:1; the rotating speed, 350 rev min⁻¹; and milling time, 5 h. And the contribution of solid content was the largest. The Al₂O₃ splats showed good adhesion with alloy matrix when the composite powder melted in good condition.