The aim of this research is to study the pore structure as well as to assess the liquid phase sintering behaviour of Cu-28Zn powder specimens at different green density levels and temperatures. For this purpose, samples were compacted to obtain six different green densities and then sintered at 870°C, 890°C and in part at 930°C for 30 min. The results revealed that the spherical pores which are formed inside the grains can be swept by grain boundaries due to grain growth and join to primary pores so that secondary intragranular pores are eliminated and intergranular pores enlarged at higher temperatures. Also, the pores move upwards to the top of sample due to buoyancy forces. The role of pore structure in distortion is more tangible at higher temperatures (930°C) so that O-shape and X-shape distortions were observed at high and low green density samples, respectively.
EverhartJL.Copper and copper alloy powder metallurgy: properties and applications. Princeton (NJ): Metal Powder Industries Federation; 1975.
2.
MitraR.Structural intermetallics and intermetallic-matrix composites: an introduction. In: Intermetallic matrix composites, Woodhead Publishing; 2018. p. 1–18.
3.
HausnerHH, TaubenblatPV.Modern developments in powder metallurgy: PM special materials and applications. Princeton (NJ): Metal Powder Industries Federation; 1977.
4.
TakajoS, NittaM.Observation of liquid phase sintering of a high speed steel powder. In: Sintering 85. Boston (MA): Springer, 1987. p. 189–196.
5.
MovchanAV, BachurinAP, ChernoivanenkoEA.Transformations with liquid phase presence in sintering of powder high-speed steel. Metall Min Ind. 2017;1:58–64.
6.
SaninAF, KarpinosDM, KalinichenkoVI, Special features of the structure of powdered high-speed steel after sintering in the presence of liquid phase. Sov Powder Metall Metal Ceram. 1986;25(3):202–206.
7.
LevasseurD, BrochuM.Supersolidus liquid phase sintering modeling of Inconel 718 superalloy. Metall Mater Trans A. 2016;47(2):869–876.
8.
JiaS, XiaoZ, WangJ, Microstructure and mechanical properties of nonmagnetic Fe-25Mn-xCu-C steels by super solidus liquid phase sintering. Mater Res Express. 2016;3(11):116502.
9.
WrightCS, OgelB, LemoissonF, Supersolidus sintering of high Speed Steels: part 2: sintering of Tungsten based alloys. Powder Metall. 1995;38(3):221–229.
10.
MomeniH, ShabestariSG, RazaviH.Rheology of Al-Cu-Mg pre-alloyed powder in supersolidus liquid phase sintering process. Can Metall Quart. 2017;56(4):442–449.
11.
GermanRM.A quantitative theory for supersolidus liquid phase sintering. Powder Metall. 1991;34(2):101–107.
12.
MousapourM, AzadbehM, DanningerH.Effect of compacting pressure on shape retention during supersolidus liquid phase sintering of Cu base alloys. Powder Metall. 2017;60(5):393–403.
13.
BlaineDC, BollinaR, ParkSJ, Critical use of video-imaging to rationalize computer sintering simulation models. Comput Ind. 2005;56:867–875.
14.
GermanRM.Supersolidus liquid phase sintering. I: process review. Int J Powder Metall. 1990;26(1):23–34.
15.
GermanRM.Supersolidus liquid phase sintering. II: densification theory. Int J Powder Metall. 1990;26(1):35–43.
16.
GermanRM.Sintering theory and practice. Solar-Terr Phys. 1996:568.
17.
AzadbehM, DanningerH, Gierl-MayerC.Particle rearrangement during liquid phase sintering of Cu–20Zn and Cu–10Sn–10Pb prepared from prealloyed powder. Powder Metall. 2013;56(5):342–346.
18.
GermanRM.Supersolidus liquid-phase sintering of prealloyed powders. Metall Mater Trans A. 1997;28(7):1553–1567.
19.
LiuY, TandonR, GermanRM.Modeling of supersolidus liquid phase sintering: II. Densification. Metall Mater Trans A. 1995;26(9):2423–2430.
20.
LalA, IacoccaRG, GermanRM.Densification during the supersolidus liquid-phase sintering of nickel-based prealloyed powder mixtures. Metall Mater Trans A. 1999;30(8):2201–2208.
21.
MohammadzadehA, AzadbehM, Sabahi NaminiA.Densification and volumetric change during Supersolidus liquid phase sintering of prealloyed brass Cu28Zn powder: modeling and optimization. Sci Sinter. 2014;46:23–35.
22.
MohammadzadehA, AzadbehM, DanningerH.New concept in analysis of supersolidus liquid phase sintering of alpha brass. Powder Metall. 2015;58:123–132.
23.
MousapourM, AzadbehM, MohammadzadehA, On the deflection behaviour of prealloyed alpha brass during sintering: in-situ bending technique and modeling. Powder Metall. 2020;63:134–141.
24.
MousapourM, AzadbehM, DanningerH.Feasibility study of “elephant foot” phenomenon during liquid phase sintering of systems with volatile components. Powder Metall. 2016;59:321–328.
25.
AzadbehM, DanningerH, MohammadzadehA, Macroscopic illustration of Zn evaporation during liquid phase sintering of Cu-28Zn prepared from prealloyed powder. Powder Metall. 2015;58:91–94.
26.
GermanRM.An update on the theory of supersolidus liquid phase sintering. In: Proceedings Sintering 2003, Materials Research Institute Pennsylvania State University; University Park (PA); 2003.
27.
LiuJ, LalA, GermanRM.Densification and shape retention in supersolidus liquid phase sintering. Acta Mater. 1999;47(18):4615–4626.
28.
GermanRM, GriffoA, LiuY.Gravitational effects on grain coarsening during liquid-phase sintering. Metall Mater Trans A. 1997;28(1):215–221.
29.
GermanRM.Sintering: from empirical observations to scientific principles. Oxford: Elsevier; 2014.