This study investigated the properties and microstructures of EH46 microalloyed steel following double-sided friction stir welding. The partially welded material was reversed, completing the weld. Yield strength, elongation and toughness of the weld were similar to those of the base material. During welding, the ferrite-pearlite in the base material transformed to mainly upper bainite, but the overlap or interference zone in the centre of the weld consisted predominantly of 0.5–3 µm recrystallised ferrite grains. The microhardness increased from 240 HV in the base material to 350 HV in bainite but decreased 200–240 HV in the overlap zone. These substantially differing microstructures suggest that the overlap or interference zone was processed at a lower temperature than the remainder of the weld, probably in ferrite.
ThomasW. M., NicholasE. D., NeedhamJ. C., MurchM. G., Temple-SmithP. and DawesC. J., Improvements relating to friction stir welding: International Patent application no. PCT/GB92/02203 and GB Patent application No. 9125978·8 and US Patent application no. 5,460,317, December 1991.
2.
ThomasW. M. and DawesC. J.: ‘Friction stir process welds aluminum alloys’, Weld. J., 1996, 75, 41–45.
RootJ. M., FieldD. P. and NelsonT. W.: ‘Crystallographic texture in the friction-stir-welded metal matrix composite Al6061 with 10 Vol Pct Al2O3’, Metall. Mater. Trans. A, 2009, 40A, 2109–2014. doi: 10.1007/s11661-009-9883-4
5.
SatoY. S., NelsonT. W. and SterlingC. J.: ‘Recrystallization in type 304L stainless steel during friction stirring’, Acta Mater., 2005, 53, 637–645. doi: 10.1016/j.actamat.2004.10.017
6.
MironovS., SatoY. S., KokawaH., InoueH. and TsugeS.: ‘Structural response of superaustenitic stainless steel to friction stir welding’, Acta Mater., 2011, 59, 5472–5481. doi:10.1016/j.actamat.2011.05.021
7.
LienertT. J., StellwagW. L., GrimmettB. B. and WarkeR. W.: ‘Friction stir welding studies on mild steel – process results, microstructures, and mechanical properties are reported’, Suppl. Weld. J., 2003, 82, 1S–9S. doi: 10.1179/136217103225008847
8.
GoshM., KumarK. and MishraR. S.: ‘Analysis of microstructural evolution during friction stir welding of ultrahigh strength steels’, Scr. Mater., 2010, 63, 851–854. doi: 10.1016/j.scriptamat.2010.06.032
9.
YoungJ., FieldD. P. and NelsonT. W.: ‘Material flow during friction stir welding of HSLA 65 steel’, Metall. Mater. Trans. A, 2013, 44A, 3167–3175. doi: 10.1007/s11661-013-1684-0
10.
JafarzadeganM., Abdollah-zadehA., FengA. H., SaeidT., ShenJ. and AssadiH.: ‘Microstructure and mechanical properties of a dissimilar friction stir weld between austenitic stainless steel and low carbon steel’, J. Mater. Sci. Technol., 2013, 29, 367–372. doi: 10.1016/j.jmst.2013.02.008
11.
KonolP. J., MathersJ. A., JohnsonR. and PickensJ. R.: ‘Friction stir welding of HSLA-65 steel for shipbuilding’, J. Ship Prod., 2003, 19, 159–164.
12.
BarnesS. J., SteuwerA., MahawishS., JohnsonR. and WithersP. J.: ‘Residual strains and microstructure development in single and sequential double sided friction stir welds in RQT-701 steel’, Mater. Sci. Eng. A, 2008, 492, 35–44. doi:10.1016/j.msea.2008.02.049
13.
McPhersonN. A., GallowayA. M., CaterS. R. and OsmanM. M.: ‘A comparison between single and double sided friction stir welded 8mm thick DN36 steel plate, in Trends in welding research’, Proc. 19th Int. Conf., 2013, 284–290.
14.
MercierG. P. and ReikM.: ‘Optimizated HSLA-65 welding procedures for fabrication of naval surface ships-joint performance verification – fracture toughness and structural element performance of welding consumables’, Concurrent Technologies Corporation, NCEMT Rpt.TR no.00-12, 2000, March 29.
15.
ManoharP. A., FerryM. and ChandraT.: ‘Five decades of the Zener equation’, ISIJ Int., 1998, 38, 913–924. doi: 10.2355/isijinternational.38.913
16.
MedinaS. F., QuispeA. and GomezM.: ‘Influence of temperature on strain induced precipitation kinetics in microalloyed steels’, Mater. Sci. Forum., 2012, 706–709, 2176–2180. doi:10.4028/www.scientific.net/MSF.706-709.2176
17.
VervyncktS., VerbekenK., LopezB. and JonasJ. J.: ‘Modern HSLA steels and role of non-recrystallisation temperature’, Int. Mater. Rev., 2012, 57, 187–207. doi: 10.1179/1743280411Y.0000000013
18.
AhmedM. M. Z., WynneB. P., RainforthW. M. and ThreadgillP. L.: ‘Quantifying crystallographic texture in the probe-dominated region of thick-section friction-stir-welded aluminium’, Scr. Mater., 2008, 59, 07–510. doi: 10.1016/j.scriptamat.2008.04.047
19.
RahimiS., WynneB. P. and BakerT. N.: ‘The microstructure of double- sided friction stir welded microalloyed steel’, AFRC Rpt.430, University of Strathclyde, January 2016.
NandanR., DebRoyT. and BhadeshiaH. K. D. H.: ‘Recent advances in friction stir welding-process, weldment structure and properties’, Progr. Mater. Sci., 2008, 53, 980–1023. doi: 10.1016/j.pmatsci.2008.05.001
22.
AydinH.: ‘Relationship between a bainitic structure and the hardness in the weld zone of the friction-stir welded X80 API-grade pipe-line steel’, Mater. Technol., 2014, 48, 15–22.
EghbaliB., Abdollah-ZahehA., BeladiH. and HodgsonP. D.: ‘Characterization on ferrite microstructure evolution during large strain warm torsion testing of plain low carbon steel’, Mater. Sci. Eng., 2006, A435–436, 499–503. doi: 10.1016/j.msea.2006.07.026
25.
WanX. L., WuK. M., NuneK. C., LiY. and ChengL.: ‘ In situ observation of acicular ferrite formation and grain refinement in simulated heat affected zone of high strength alloy steel’, Sci. Technol. Weld. Join., 2015, 20, 254–263. doi: 10.1179/1362171815Y.0000000008
26.
ChoH-W., KangS. H., KimS-H., OhK. H., KimH. J., ChangW-S and HamH. N.: ‘Microstructural evolution in friction stir welding of high-strength linepipe steel’, Mater. Des., 2012, 34, 258–267. doi: 10.1016/j.matdes.2011.08.010
27.
OzekcinA., JinH. W., KooJ. Y., BangaruN. V., AyerR., VaugnG., SteelR. and PackerS.: ‘A microstructural study of friction stir welded joints of carbon steels’, Int. J. Offshore Polar Eng., 2004, 14, 284–288.
28.
ToumpisA., GallowayA. M., McPhersonN. A. and CaterS. R.: ‘Development of a process envelope for friction stir welding of DH36 steel: a step change’, Mater. Des., 2014, 62, 64–75. doi: 10.1016/j.matdes.2014.04.066
29.
DeA., BhadeshiaH. K. D. H. and DebRoyT.: ‘Friction stir welding of mild steel: tool durability and steel microstructure’, Mater. Sci. Technol., 2014, 30, 1050–1056. doi: 10.1179/1743284714Y.0000000534
30.
PatelP., MridhaS. and BakerT. N.: ‘Influence of shielding gases on preheat produced in surface coatings incorporating SiC particulates into microalloy steel using TIG technique’, Mater. Sci. Technol., 2014, 30, 1506–1514. doi: 10.1179/1743284713Y.0000000481
31.
ToumpisA. L., GallowayA. M., CaterS. R., MicallefD., CamilleriD., PoletzN. and ArbaouiL.: ‘Advances in friction stir welding of steel : Project HILDA’, Proc. ASME 2015 IMECE 2015-51249, 1–11, November 13–19, Houston Texas.
SantosT. F. A., HermenegildoT. F. C., AfonsoC. R. M., MarinhoR. R., PaesM. T. P. and RamirezA. J.: ‘Fracture toughness of ISO 3183 X80M(API 5l X80) steel friction stir welds’, Eng. Frac. Mech., 2010, 77, 2937–2945. doi: 10.1016/j.engfracmech.2010.07.022