Carbon partitioning was applied to treat high-carbon high-alloy steel. Equilibrium concentration of carbon was studied by constrained carbon equilibrium (CCE) criterion and modified model (CCEA) which took the effect of alloying elements on the carbon activity into account. The results of X-ray diffraction (XRD) analyses showed that the carbon concentration of retained austenite increased first and then decreased with the holding time, and the approximate equilibrium concentration of carbon was closer to the predicted results by CCEA. Simultaneously, the results of XRD analyses represented that the structure of martensite in quenched and partitioned steel was body-centred tetragonal. Carbide precipitation was observed in specimens during the partitioning step by scanning electron microscope and high-resolution transmission electron microscopy.
MatasS. and HehemannR. F.: ‘Retained austenite and the tempering of martensite[J]’, Nature, 1960, 187, 685–686. doi: 10.1038/187685a0
2.
SpeerJ., MatlockD. K., De CoomanB. C. and SchrothJ. G.: ‘Carbon partitioning into austenite after martensite transformation[J]’, Acta Mater., 2003, 51, 2611–2622. doi: 10.1016/S1359-6454(03)00059-4
3.
SpeerJ. G., EdmondsD. V., RizzoF. C. and MatlockD. K.: ‘Partitioning of carbon from supersaturated plates of ferrite, with application to steel processing and fundamentals of the bainite transformation[J]’, Curr. Opin. Solid STM, 2004, 8, 219–237. doi: 10.1016/j.cossms.2004.09.003
4.
HillertM. and AgrenJ.: ‘Reply to comments on “On the definition of paraequilibrium and orthoequilibrium” by J.G. Speer et al.[J]’, Scripta Mater., 2005, 52, 83–85. doi: 10.1016/j.scriptamat.2004.08.029
5.
SeoE. J., ChoL. and De CoomanB. C.: ‘Application of quenching and partitioning processing to medium Mn steel[J]’, Metall. Mater. Trans. A, 2015, 46, 27–30. doi: 10.1007/s11661-014-2657-7
6.
GaoG. H., ZhangH., TanZ. L., LiuW. B. and BaiB. Z.: ‘A carbide-free bainite/martensite/austenite triplex steel with enhanced mechanical properties treated by a novel quenching-partitioning-tempering process[J]’, Mater. Sci. Eng. A, 2013, 559, 165–169. doi: 10.1016/j.msea.2012.08.064
7.
GaoG. H., ZhangH., GuiX. L., LuoP., TanZ. L. and BaiB. Z.: ‘Enhanced ductility and toughness in an ultrahigh-strength Mn-Si-Cr-C steel: the great potential of ultrafine filmy retained austenite[J]’, Acta Mater., 2014, 76, 425–433. doi: 10.1016/j.actamat.2014.05.055
8.
SantofimiaM. J., ZhaoL., PetrovR., KwakernaakC., SloofW. G. and SietsmaJ.: ‘Microstructural development during the quenching and partitioning process in a newly designed low-carbon steel[J]’, Acta Mater., 2011, 59, 6059–6068. doi: 10.1016/j.actamat.2011.06.014
9.
HuangX. F., LiuW. L., HuangY. Y., ChenH. and HuangW. H.: ‘Effect of a quenching-long partitioning treatment on the microstructure and mechanical properties of a 0.2C% bainitic steel[J]’, J Mater. Process. Technol., 2015, 222, 181–187. doi: 10.1016/j.jmatprotec.2015.03.010
10.
ZhangJ., DingH. and MisraR. D. K.: ‘Enhanced strain hardening and microstructural characterization in a low carbon quenching and partitioning steel with partial austenization[J]’, Mater. Sci. Eng. A, 2015, 636, 53–59. doi: 10.1016/j.msea.2015.03.095
11.
TariqF. and BalochR. A.: ‘One-step quenching and partitioning heat treatment of medium carbon low alloy steel[J]’, J. Mater. Eng. Perform., 2014, 23, 1726–1729. doi: 10.1007/s11665-014-0902-2
12.
MoorE. D., LacroixS., ClarkeA. J., PenningJ. and SpeerJ. G.. ‘Effect of retained austenite stabilized via quench and partitioning on the strain hardening of martensitic steels[J]’, Metall. Mater. Trans. A, 2008, 39A, 2586–2595. doi: 10.1007/s11661-008-9609-z
13.
ClarkeA. J., SpeerJ. G., MillerM. K., HackenbergR. E., EdmondsD. V., MatlockD. K., RizzoF. C., ClarkeK. D. and MoorE. D.: ‘Carbon partitioning to austenite from martensite or bainite during the quench and partition (Q&P) process: a critical assessment[J]’, Acta Mater., 2008, 56, 16–22. doi: 10.1016/j.actamat.2007.08.051
14.
HongS. C., AhnJ. C., NamS. Y., KimS. J., YangH. C., SpeerJ. G., DavidK. M.: ‘Mechanical properties of high-Si plate steel produced by the quenching and partitioning process[J]’, Met. Mater. Int., 2007, 13, 439–445. doi: 10.3365/MMI.2007.12.439
15.
TojiY., MiyamotoG. and RaabeD.: ‘Carbon partitioning during quenching and partitioning heat treatment accompanied by carbide precipitation[J]’, Acta Mater., 2015, 86, 137–147. doi: 10.1016/j.actamat.2014.11.049
16.
LoboJ. A. and GeigerG. H.: ‘Thermodynamics and solubility of carbon in ferrite and ferritic Fe-Mo alloys[J]’, Metall. Trans. A, 1976, 7A, 1347–1357. doi: 10.1007/BF02658820
17.
LoboJ. A. and GeigerG. H.: ‘Thermodynamics of carbon in austenite and Fe-Mo austenite[J]’, Metall. Trans. A, 1976, 7A, 1359–1364. doi: 10.1007/BF02658821
18.
MiettinenJ.: ‘Simple semiempirical model for prediction of austenite decomposition and related heat release during cooling of low alloyed steels[J]’, Ironmak. Steelmak., 1996, 23, 346–356.
19.
HuangY. Y. and ZhouM. R: ‘Study on carbides in Cr4Mo4V high temperature bearing steel[J]’, Bearing, 1980, 4, 33–40. (in Chinese).
20.
DijkN. H. V., ButtA. M., ZhaoL., SietsmaJ., OffermanS. E., WrightJ. P. and ZwaagS. V. D.: ‘Thermal stability of retained austenite in TRIP steels studied by synchrotron X-ray diffraction during cooling[J]’, Acta Mater., 2005, 53, 5439–5447. doi: 10.1016/j.actamat.2005.08.017
21.
DysonD. J. and HolmesB.: ‘Effect of alloying on the lattice parameter of austenite[J]’, J. Iron steel Inst., 1970, 208, 469–474.
22.
ZwaagS. V. D., ZhaoL., KruijveS. O. and SietsmaJ.: ‘Thermal and mechanical stability of retained austenite in aluminum-containing multiphase TRIP steels[J]’, ISIJ Int., 2002, 42, 1565–1570. doi: 10.2355/isijinternational.42.1565
23.
ZhouS., ZhangK., WangY., GuaJ. F. and RongY. H.: ‘High strength-elongation product of Nb-microalloyed low-carbon steel by a novel quenching-partitioning-tempering process[J]’, Mater. Sci. Eng. A, 2011, 528, 8006–8012. doi: 10.1016/j.msea.2011.07.008
24.
NayakaS. S., AnumoluaR., KmisraaR. D., KimK. H. and LeeD. L.: ‘Microstructure-hardness relationship in quenched and partitioned medium-carbon and high-carbon steels containing silicon[J]’, Mater. Sci. Eng. A, 2008, 498, 442–456. doi: 10.1016/j.msea.2008.08.028
25.
KurdjumovG. V., KhachaturyanA. G.: ‘Nature of axial ratio anomalies of the martensite lattice and mechanism of diffusionless γ → α transformation[J]’, Acta Metall., 1975, 23, 1077. doi: 10.1016/0001-6160(75)90112-1
26.
EdwinB. J., GunvantN. M. and ThoniV. P.: ‘Carbides in M50 high speed steel[J]’, Metall. Trans., 1971, 2, 2209–2214. doi: 10.1007/BF02917552
27.
XiongX. C., ChenB., HuangM. X., WangJ. F. and WangL.: ‘The effect of morphology on the stability of retained austenite in a quenched and partitioned steel[J]’, Scripta Mater., 2013, 68, 321–324. doi: 10.1016/j.scriptamat.2012.11.003
28.
JacquesP. J., DelannayF. and LadrièreJ.: ‘On the influence of interactions between phases on the mechanical stability of retained austenite in transformation-induced plasticity multiphase steels[J]’, Metall. Mater. Trans. A, 2001, 32, 2759–2768. doi: 10.1007/s11661-001-1027-4