The abrasion wear resistance and wear mechanism of super bainitic steel austempered at different temperatures and time have been investigated by two-body abrasion testings, scanning electron microscopy, X-ray diffraction, transformation electron microscopy and electron backscattering diffraction. The results show that the two-body abrasion wear mechanism is predominantly micro-ploughing abrasion, and the wear resistance is decreased with increasing isothermal temperature which is attributed to the decreased hardness caused by a higher retained austenite content and the coarsening of the microstructure. The sample austempered at 230°C for 2 h with the higher amount of retained austenite and lower carbon concentration exhibits excellent wear resistance, and the transformation induced plasticity effect is observed during wear process which is beneficial for the improving of hardness and wear resistance.
El-MahallawiI., Abdel-KarimR. and NaguibA.: ‘Evaluation of effect of chromium on wear performance of high manganese steel’, Mater. Sci. Technol., 2001, 17, 1385–1390. doi: 10.1179/026708301101509340
2.
LeiroA., KankanalaA., VuorinenE. and PrakashB.: ‘Tribological behaviour of carbide-free bainitic steel under dry rolling/sliding conditions’, Wear, 2011, 273, 2–8. doi: 10.1016/j.wear.2011.03.025
3.
CaballeroF. G., BhadeshiaH. K. D. H., MawellaK. J. A., JonesD. G. and BrownP.: ‘Very strong low temperature bainite’, Mater. Sci. Technol., 2002, 18, 279–284. doi: 10.1179/026708301225000725
4.
RementeriaR., ArandaM. M., Garcia-MateoC. and CaballeroF. G.: ‘Improving wear resistance of steels through nanocrystalline structures obtained by bainitic transformation’, Mater. Sci. Technol., 2016, 32, 308–312. doi: 10.1080/02670836.2015.1132048
5.
WangT. S., YangJ., ShangC. J., LiX. Y., LvB., ZhangM. and ZhangF. C.: ‘Sliding friction surface microstructure and wear resistance of 9SiCr steel with low-temperature austempering treatment’, Surf. Coat. Technol., 2008, 202, 4036–4040. doi: 10.1016/j.surfcoat.2008.02.013
6.
YangJ., WangT. S., ZhangB. and ZhangF. C.: ‘Sliding wear resistance and worn surface microstructure of nanostructured bainitic steel’, Wear, 2012, s282–s283, 81–84. doi: 10.1016/j.wear.2012.02.008
7.
ZhangP., ZhangF. C., YanZ. G., WangT. S. and QianL. H.: ‘Wear property of low-temperature bainite in the surface layer of a carburized low carbon steel’, Wear, 2011, 271, 697–704. doi: 10.1016/j.wear.2010.12.025
8.
RementeriaR., GarcíaI., ArandaM. M. and CaballeroF. G.: ‘Reciprocating-sliding wear behavior of nanostructured and ultra-fine high-silicon bainitic steels’, Wear, 2015, 338–339, 202–209. doi: 10.1016/j.wear.2015.06.011
9.
ZhangF. C., LongX. Y., KangJ., CaoD. and LvB.: ‘Cyclic deformation behaviors of a high strength carbide-free bainitic steel’, Mater. Des., 2016, 94, 1–8.
10.
SourmailT., CaballeroF. G., Garcia-MateoC., SmanioV., ZieglerC. and KuntzM.: ‘Evaluation of potential of high Si high C steel nanostructured bainite for wear and fatigue applications’, Mater. Sci. Technol., 2013, 29, 1166–1173. doi: 10.1179/1743284713Y.0000000242
11.
BakshiS. D., LeiroA., PrakashB. and BhadeshiaH. K. D. H.: ‘Dry rolling/sliding wear of nanostructured bainite’, Wear, 2014, 316, 70–78. doi: 10.1016/j.wear.2014.04.020
12.
LeiroA., VuorinenE., SundinK. G., PrakashB., SourmailT. and SmanioV.: ‘Wear of nano-structured carbide-free bainitic steels under dry rolling–sliding conditions’, Wear, 2013, 298–299, 42–47. doi: 10.1016/j.wear.2012.11.064
13.
Solano-AlvarezW., PickeringE. J. and BhadeshiaH. K. D. H.: ‘Degradation of nanostructured bainitic steel under rolling contact fatigue’, Mater. Sci. Eng. A, 2014, 617, 156–164. doi: 10.1016/j.msea.2014.08.071
14.
BakshiS. D., ShipwayP. H. and BhadeshiaH. K. D. H.: ‘Three-body abrasive wear of fine pearlite, nanostructured bainite and martensite’, Wear, 2013, 308, 46–53. doi: 10.1016/j.wear.2013.09.008
15.
ZhiC., ZhaoA. M., HeJ. G., ZhaoF. Q. and CheY. J.: ‘Thermodynamic analysis and strength toughness research of nanobainite’, Chin. J. Eng., 2013, 38, 691–698(in Chinese)
YoozbashiM. N. and YazdaniS.: ‘Mechanical properties of nanostructured, low temperature bainitic steel designed using a thermodynamic model’, Mater. Sci. Eng. A, 2010, 527, 3200–3205. doi: 10.1016/j.msea.2010.01.080
18.
Garcia-MateoC., CaballeroF. G., SourmailT., KuntzM., CornideJ. and SmanioV.: ‘Tensile behaviour of a nanocrystalline bainitic steel containing 3wt% silicon’, Mater. Sci. Eng. A, 2012, 549, 185–192. doi: 10.1016/j.msea.2012.04.031
19.
Garcia-MateoC., CaballeroF. G. and BhadeshiaH. K. D. H.: ‘Acceleration of low-temperature bainite’, ISIJ Int., 2003, 43, 1821–1825. doi: 10.2355/isijinternational.43.1821
20.
ZhaoJ., WangT. S., LvB. and ZhangF. C.: ‘Microstructures and mechanical properties of a modified high-C-Cr bearing steel with nano-scaled bainite’, Mater. Sci. Eng. A, 2015, 628, 327–331. doi: 10.1016/j.msea.2014.12.121
21.
GoreG. J. and GatesJ. D.: ‘Effect of hardness on three very different forms of wear’, Wear, 1997, 203–204, 544–563. doi: 10.1016/S0043-1648(96)07414-5
22.
BowdenF. P. and TaborD. (eds.): ‘Fraction: an introduction to tribology’; 1973, New York, RE Krieger Publishing Company.
23.
Larsen-BasseJ.: ‘Role of microstructure and mechanical properties in abrasion’, Scr. Mater., 1990, 24, 821–826. doi: 10.1016/0956-716X(90)90119-2
24.
NarayanaswamyB., HodgsonP., TimokhinaI. and BeladiH.: ‘The impact of retained austenite characteristics on the two-body abrasive wear behavior of ultrahigh strength Bainitic steels’, Metall. Mater. Trans. A, 2016, 47, 4883–4895. doi: 10.1007/s11661-016-3690-5