Dissimilar Al–Li alloys (2198 and 2060) were laser welded without the addition of filler material. The effects of welding parameters on the formation of the welded joints, microstructure evolution, solute segregation, porosity and their relationships with the mechanical properties of the joint were investigated. It was found that reducing the weld heat input can effectively prevent grain coarsening, while decreasing porosity and reducing the tendency for hot cracking, thereby enhancing the properties of the joint. The dissolution of precipitates such as the T1 phase and θ′ phase in the base metal, and the variations in Cu and Mg content between grain interiors and boundaries, resulted from solute segregation during welding, leading to reductions in the strength of the weld.
YangDX, LiXY, HeDY, Study on microstructure and mechanical properties of Al-Mg-Mn-Er alloy joints welded by TIG and laser beam. Mater Design. 2012;40:117–123. doi: 10.1016/j.matdes.2012.03.041
2.
LeeHK, ParkSH, KangCY.Effect of plasma current on surface defects of plasma-MIG welding in cryogenic aluminum alloys. J Mater Process Technol. 2015;223:203–215. doi: 10.1016/j.jmatprotec.2015.04.008
3.
XiaoRS, ZhangXY.Problems and issues in laser beam welding of aluminum–lithium alloys. J Manuf Process. 2014;16:166–175. doi: 10.1016/j.jmapro.2013.10.005
4.
PickensJR.Recent developments in the weldability of lithium-containing aluminium alloys. J Mater Sci. 1990;25:3035–3047. doi: 10.1007/BF00587647
5.
CuiL, LiXY, HeDY, Effect of Nd:YAG laser welding on microstructure and hardness of an Al–Li based alloy. Mater Charact. 2012;71:95–102. doi: 10.1016/j.matchar.2012.06.011
6.
YangWX, ZhangXY, XiaoRS.Dual-beam laser welding of T-Joint of aluminum-lithium alloy 2060-T8/2099-T83. Chin J Lasers. 2013;40:89–93.
7.
EnzJ, RiekehrS, VentzkeV, Influence of the local chemical composition on the mechanical properties of laser beam welded Al-Li alloys. Phys Proc. 2012;39:51–58. doi: 10.1016/j.phpro.2012.10.013
8.
MridhaS, BakerTN.Characteristic features of laser-nitrided surfaces of two titanium alloys. Mater Sci Eng A. 1991;142:115–124. doi: 10.1016/0921-5093(91)90760-K
9.
MridhaS, BakerTN.Surface cracking in laser nitrided titanium of commercial purity and possible ways of reducing these defects. J Process Adv Mater. 1994;4:85–94.
10.
AnN, ZhangXY, WangQM, Fiber laser welding of 2060 aluminum-lithium alloy with filler wire. Chin J Lasers. 2014;41:1003009-1–1003009-6.
11.
MolianPA, SrivatsanTS.Weldability of aluminium-lithium alloy 2090 using laser welding. J Mater Sci. 1990;25:3347–3358. doi: 10.1007/BF00587697
12.
FuBL, QinGL, MengXM, Microstructure and mechanical properties of newly developed aluminum-lithium alloy 2A97 welded by fiber laser. Mater Sci Eng A. 2014;617:1–11. doi: 10.1016/j.msea.2014.08.038
13.
XuF, ChenL, GongSL, Microstructure and mechanical properties of Al-Li alloy by laser welding with filler wire. Rare Metal Mater Eng. 2011;40:1775–1779.
14.
LinDC, HeY, HeYJ, Solidification structures of fusion zone in Al-Li alloy weld metal. Mater Mech Eng. 1996;20:10–12+42.
15.
YuEJ, HaoCY, YingHY, Peculiarities of solidification structure of aluminum-lithium alloy welds. Trans China Weld Ins. 1996;17:1–6.
16.
WitzendorffP, KaierleS, SuttmannO, Using pulse shaping to control temporal strain development and solidification cracking in pulsed laser welding of 6082 aluminum alloys. J Mater Process Technol. 2015;225:162–169. doi: 10.1016/j.jmatprotec.2015.06.007
17.
HouKH, BaeslackWA.Effect of solute segregation on the weld fusion zone microstructure in CO2 laser beam and gas tungsten arc welds in Al-Li-Cu alloy 2195. J Mater Sci Lett. 1996;15:208–213. doi: 10.1007/BF00274453
18.
ZhangXY, YangWX, XiaoRS.Microstructure and mechanical properties of laser beam welded Al–Li alloy 2060 with Al–Mg filler wire. Mater Design. 2015;88:446–450. doi: 10.1016/j.matdes.2015.08.144
19.
LeeTH, HwangIS, KimHD, Techniques for intergranular crack formation and assessment in alloy 600 base and alloy 182 weld metals. Nucl Eng Technol. 2015;47:102–114. doi: 10.1016/j.net.2014.08.002
20.
Jefferson Lab [internet]. Virginia ( VA): Thomas Jefferson National Accelerator Facility - Office of Science Education; [cited 2017 Aug 01]. Available from: http://education.jlab.org/itselemental/ele012.html
21.
Jefferson Lab [internet]. Virginia ( VA): Thomas Jefferson National Accelerator Facility - Office of Science Education; [cited 2017 Aug 01]. Available from: http://education.jlab.org/itselemental/ele003.html