A continuous solid/liquid bonding method was successfully developed to fabricate Cu–10wt-%Ni–1wt-%Fe (nickel bronze) clad steel with a good metallurgical bonding in the present study. The results indicated that the diffusion distance of interface is about 1.90–2.18 µm. The average tensile shear strength of centre composite strip at as-cast state is 228 ± 5 MPa, while that of edge is 202 ± 6 MPa, and the interface strength is higher than that of bronze since the fracture always occurs on the nickel bronze side. After the rolling process, the tensile shear strength increases with the increasing rolling reduction. The reason can be ascribed to the strengthening of the nickel bronze whose strength is still lower than the interface.
BaeJH, RaoAKP, KimKH, Cladding of Mg alloy with Al by twin-roll casting. Scripta Mater. 2011;64(9):836–839. doi: 10.1016/j.scriptamat.2011.01.013
2.
DavisJR, Handbook VolASM.02 properties and selection: nonferrous alloys and special-purpose materials 2. Ohio: ASM International; 1990.
3.
MingG, MeiS, LiX, Characterization and formation mechanism of laser-welded Mg and Al alloys using Ti interlayer. Scripta Mater. 2012;67(2):193–196. doi: 10.1016/j.scriptamat.2012.04.015
4.
LloydDJ.Recent developments in controlling the architecture for property optimization in Al-based materials. Scripta Mater. 2013;68(1):13–16. doi: 10.1016/j.scriptamat.2012.05.040
5.
GloverTJ.Copper–nickel alloy for the construction of ship and boat hulls. Br Corros J. 2013;17(4):155–158. doi: 10.1179/000705982798274228
6.
FuY, YanZ, LiT, Study on plastic behaviours of CuNi10Fe1Mn alloy tubes under cast-roll process. Mater. Des. 2009;30(10):4478–4482. doi: 10.1016/j.matdes.2009.06.003
7.
LeedyKD, StubbinsJF.Copper alloy–stainless steel bonded laminates for fusion reactor applications: tensile strength and microstructure. Mater Sci Eng A. 2001;297(1):10–18. doi: 10.1016/S0921-5093(00)01273-9
8.
BinaMH, DehghaniF, SalimiM.Effect of heat treatment on bonding interface in explosive welded copper/stainless steel. Mater Des. 2013;45(none):504–509. doi: 10.1016/j.matdes.2012.09.037
9.
DurgutluA, GülençB, FindikF.Examination of copper/stainless steel joints formed by explosive welding. Mater Des. 2005;26(6):497–507. doi: 10.1016/j.matdes.2004.07.021
10.
ZhangH, KeXJ, JianLZ, Microstructure and mechanical properties investigations of copper-steel composite fabricated by explosive welding. Mater Sci Eng A. 2018;731:278–287. doi: 10.1016/j.msea.2018.06.051
11.
ShiX, HussainG, ButtSI, The state of residual stresses in the Cu/steel bonded laminates after ISF deformation: an experimental analysis. J Manuf Process. 2017;30:14–26. doi: 10.1016/j.jmapro.2017.09.009
12.
Al-GhamdiKA, HussainG.On the comparison of formability of roll-bonded steel-Cu composite sheet metal in incremental forming and stamping processes. Int J Adv Manuf. 2016;87(1–4):1–12. doi: 10.1007/s00170-016-8488-5
13.
ChangH, ZhengMY, GanWM, Texture evolution of the Mg/Al laminated composite fabricated by the accumulative roll bonding. Scripta Mater. 2009;61(7):717–720. doi: 10.1016/j.scriptamat.2009.06.014
14.
EchrifSBM, HrairiM.Research and progress in incremental sheet forming processes. Adv Manuf Process. 2011;26(11):1404–1414. doi: 10.1080/10426914.2010.544817
15.
LeacockA.The future of sheet metal forming research. Adv Manuf Process. 2012;27(4):366–369. doi: 10.1080/10426914.2011.551960
16.
XuGM, CuiJZ.Producing composite material by liquid-solid roll-bonding. Trans Inst Met Finish. 2004;82(3–4):129–131. doi: 10.1080/00202967.2004.11871574
17.
HuangHG, ChenP, JiC.Solid-liquid cast-rolling bonding (SLCRB) and annealing of Ti/Al cladding strip. Mater Des. 2017;118:233–244. doi: 10.1016/j.matdes.2017.01.042
18.
MishraSRMA, Friction stir welding and processing. Mater Sci Eng R. 2010;50(1):1–78.
19.
KraetzschM, StandfussJ, KlotzbachA, Laser beam welding with high-frequency beam oscillation: welding of dissimilar materials with brilliant fiber lasers. Phys Procedia. 2011;12(1):142–149. doi: 10.1016/j.phpro.2011.03.018
PanD, GaoK, YuJ.Cold roll bonding of bimetallic sheets and strips. Met Sci J. 1989;5(9):934–939.
22.
SzekdyJ.Fluid flow phenomena in metal processing. New York: Academic Press; 1979.
23.
KalininGM, IvanovAD, ObushevAN, Ageing effect on the properties of CuCrZr alloy used for the ITER HHF components. J Nucl Mater. 2007;367(part-PB):920–924. doi: 10.1016/j.jnucmat.2007.03.256
24.
AsparB, JalaguierE, MasA, Smart-Cut(R) process using metallic bonding: application to transfer of Si, GaAs, InP thin films. Electron Lett. 1999;35(12):1024–1025. doi: 10.1049/el:19990663
25.
CarterArya, EmilyA.Structure, bonding, and adhesion at the ZrC(100)/Fe(110) interface from first principles. J Chem Phys. 2003;118(19):8982–8996. doi: 10.1063/1.1565323
26.
FisherJC.On the strength of solid solution alloys. Acta Metall. 1954;2(1):9–10. doi: 10.1016/0001-6160(54)90087-5
27.
BahrDF, VasquezG.Effect of solid solution impurities on dislocation nucleation during nanoindentation. J Mater Res. 2005;20(8):1947–1951. doi: 10.1557/JMR.2005.0244
28.
ChenS, HuangJ, XiaJ, Influence of processing parameters on the characteristics of stainless steel/copper laser welding. J Mater Process Technol. 2015;222:43–51. doi: 10.1016/j.jmatprotec.2015.03.003
29.
YangY, WangD, JiaL, Evolution of structure and fabrication of Cu/Fe multilayered composites by a repeated diffusion-rolling procedure. Mater Des. 2015;85:635–639. doi: 10.1016/j.matdes.2015.07.082
30.
ZhangP, LiSX, ZhangZF.General relationship between strength and hardness. Mater Sci Eng A. 2011;529(1):62–73. doi: 10.1016/j.msea.2011.08.061
31.
CalvoFA, UreñaA, SalazarJMGD, Solid-state transformations during diffusion bonding of copper to iron. J Mater Sci. 1988;23(4):1231–1236. doi: 10.1007/BF01154583
32.
RodriguezJA, GoodmanDW.The nature of the metal-metal bond in bimetallic surfaces. Science. 1992;257(5072):897–903. doi: 10.1126/science.257.5072.897