Hard coatings are required to have a long lifetime without performance degradation when used in tough working environments. In this study, quaternary Ti–Si–B–C coatings with various Si contents were synthesised at a relatively low temperature of 600°C by a plasma-enhanced chemical vapour deposition. Effect of the Si/(Si+B) ratio on the microstructure and mechanical properties of the Ti–Si–B–C coatings was systematically investigated. Instrumental analyses, such as EPMA, XRD, XPS and HR-TEM, revealed that the microstructure was changed from a huge crystalline structure with an hexagonal close-packed (HCP) (Ti,C)B2 phase into a nanocomposite structure that consists of nano-sized HCP (Ti,C)B2 crystallites and amorphous SiC/TiC phases by a percolation effect with the Si addition. As the Si content increased, hardness of the Ti–Si–B–C coatings varied from 18.8 to 35.6 GPa. In addition, the tribology and anti-oxidation properties of the Ti–Si–B–C coatings with the characteristic microstructural evolution were fairy improved compared with Ti–B–C coatings. The Ti–Si–B–C coatings had excellent multifunctional properties, including high hardness, low friction coefficient and high temperature oxidation resistance.
TkadletzM., SchalkN., DanielR., KeckesJ., CzettC. and MittererC.: ‘Advanced characterization methods for wear resistant hard coatings: a review on recent progress’, Surf. Coat. Technol., 2016, 285, 31–46.
2.
KimK. H.: ‘Hybrid functional multi-component composite films for hard coating applications’, J. Ceram. Process. Res., 2009, 10, 1–9.
3.
MollartT. P., BakerM., HauptJ., SteinerA., HammerP. and GisslerW.: ‘Nanostructured titanium boron nitride coatings of very high hardness’, Surf. Coat. Technol., 1995, 74–75, 491–496.
4.
Sánchez-LópezJ. C., AbadM. D., JustoA., GagoR., EndrinoJ. L., García-LuisA. and BrizuelaM.: ‘Phase composition and tribomechanical properties of Ti-B-C nanocomposite coatings prepared by magnetron sputtering’, J. Phys. D: Appl. Phys., 2012, 45, 375–401.
5.
OkJ.-T., ParkI.-W., MooreJ. J., KangM. C. and KimK. H.: ‘Syntheses and mechanical properties of Ti-B-C coatings by a plasma-enhanced chemical vapor deposition’, Surf. Coat. Technol., 2005, 200, 1418–1423.
6.
M. D. Abad, D. Cáceres, Daniel, Y. S. Pogozhev, D. V. Shtansky and J. C. Sánchez López: ‘Bonding structure and mechanical properties of Ti-B-C coatings’, Plasma Process. Polym., 2009, 6, S107–S112.
7.
PangJ., BaiY., QinF., PanL., ZhaoY. and KangR.: ‘Deposition of Ti-Si-N films on Al substrates by magnetron sputtering’, Surf. Eng., 2013, 29, 749–754.
8.
ZhangR. F. and VeprekS.: ‘On the spinodal nature of the phase segregation and formation of stable nanostructure in the Ti-Si-N system’, Mater. Sci. Eng. A, 2006, 424, 128–137.
9.
HanD.-S., SongP. K., ChoK. M., ParkY. H. and KimK. H.: ‘Synthesis and mechanical properties of Ti-Si-C films by a plasma-enhanced chemical vapor deposition’, Surf. Coat. Technol., 2004, 188–189, 446–451.
10.
LimW. J., ShinD.-W., ShinJ. H., KwonS. H., WangQ. and KimK. H.: ‘Synthesis and mechanical properties of Ti-Si-B-N coatings by a PECVD technique’, J. Ceram. Process. Res., 2012, 13, 26–30.
11.
LiuP., ZhangY. B. and LuoH.: ‘Surface modification of pure Ti with TiB2/Si3N4 reinforced coating’, Surf. Eng., 2012, 28, 532–535.
12.
ShinJ. H., ChoiK. S., WangT.-G., KimK. H. and NowakR.: ‘Microstructure evolution and mechanical properties of Ti-B-N coatings deposited by plasma-enhanced chemical vapor deposition’, Trans. Nonferrous Met. Soc. China, 2012, 22, s722–s728.
13.
BirkholzM.: ‘Thin film analysis by X-ray scattering’, 252; 2006, Weinheim, Wiley-VCH Verlag GmbH & Co. KGaA.
DiserensM., PatscheiderJ. and LevyF.: ‘Mechanical properties and oxidation resistance of nanocomposite TiN-SiNx physical-vapor-deposited thin films’, Surf. Coat. Technol., 1999, 120–121, 158–165.
16.
MoulderJ. F., StickleW. F., SobolP. E. and BombenK. D.: ‘Handbook of X-ray phothoelectron spectroscopy’, 1995, Minnesota, Physical Electronics, Inc.
17.
NaumkinA. V., Kraut-VassA., GaarenstroomS. W. and PowellC. J.: ‘NIST X-ray photoelectron spectroscopy database’, 2012, National Institute of Standards and Technology
, ver. 4.1, Gaithersburg, National Institute of Standards and Technology.
18.
BenkoE., BarrT. L., HardcastleS., HoppeE., BernasikA. and MorgielJ.: ‘XPS study of the cBN-TiC system’, Ceram. Int., 2001, 27, 637–643.
19.
LuY. H., ShenY. G. and LiK. Y.: ‘Relationship between composition, bonding constitution and microstructure in unbalanced magnetron sputtered Ti-B-N thin films’, Surf. Eng., 2007, 23, 307–312.
20.
ParkI.-W., KimK. H., KunrathA. O., ZhongD., MooreJ. J., VoevodinA. and LevashovE. A.: ‘Microstructure and mechanical properties of superhard Ti-B-C-N films deposited by dc unbalanced magnetron sputtering’, J. Vac. Sci. Technol. B, 2005, 23, 588–593.
21.
LacknerJ. M., WaldhauserW. and EbnerR.: ‘Large-area high-rate pulsed laser deposition of smooth TiCxN1−x coatings at room temperature—mechanical and tribological properties’, Surf. Coat. Technol., 2004, 188–189, 519–524.
22.
KimS. H., KimJ. K. and KimK. H.: ‘Influence of deposition conditions on the microstructure and mechanical properties of Ti-Si-N films by DC reactive magnetron sputtering’, Thin Solid Films, 2002, 420–421, 360–365.
23.
VeprˇekS., NesládekP., NiederhoferA., GlatzF., JílekM. and ŠímaM.: ‘Recent progress in the superhard nanocrystalline composites: towards their industrialization and understanding of the origin of the superhardness’, Surf. Coat. Technol., 1998, 108–109, 138–147.
24.
PodgornikB., KosecT., KocijanA. and DonikČ.: ‘Tribological behaviour and lubrication performance of hexagonal boron nitride (h-BN) as a replacement for graphite in aluminium forming’, Tribol. Int., 2015, 81, 267–275.
25.
WuG. Z. and MaS. L.: ‘Microstructure and mechanical properties of Ti-Si-C-N coatings deposited by hybrid arc enhanced magnetron sputtering’, Surf. Eng., 2010, 26, 50–54.
26.
ParkI.-W., ChoiS. R., SuhJ. H., ParkC.-G. and KimK. H.: ‘Deposition and mechanical evaluation of superhard Ti-Al-Si-N nanocomposite films by a hybrid coating system’, Thin Solid Films, 2004, 447–448, 443–448.
27.
KimK. H. and ParkB. H.: ‘Mechanical properties and oxidation behavior of Ti-Si-N films prepared by plasma-assisted CVD’, Chem. Vapor Depos., 1999, 5, 275–279.