In the present paper, hot corrosion behaviour of functionally graded material (FGM) and usual ceria-yttria stabilised zirconia (CYSZ) TBCs, prepared by atmospheric plasma spraying method was evaluated. In addition, coating microstructures were investigated using scanning electron microscope; EDS and X-ray diffraction techniques before and after hot corrosion test. The results showed, due to different corrosion mechanisms, the life of FGM TBC was higher than the usual one. The degradation mechanism of usual TBC was formation of TGO at the bond coat/CYSZ layer interface resulted in delamination, while in FGM coating was the stress induced by phase transformation volume increment occurred in the coating and the thermal stress accompanied by thermal expansion mismatch.
LuZ., KimM.-S., MyoungS.-W., LeeJ.-H., JungY.-G., KimI.-S. and JoC.-Y.: ‘Thermal stability and mechanical properties of thick thermal barrier coatings with vertical type cracks’, Trans. Nonferrous Met. Soc. China, 2014, 24, 29–35. doi: 10.1016/S1003-6326(14)63284-2
2.
PadtureN. P., SchlichtingK. W., BhatiaT., OzturkA., CetegenB., JordanE. H., GellM., JiangS., XiaoT. D., StruttP. R., GarcyiaE., MiranzoP. and OsendiM. I.: ‘Towards durable thermal barrier coatings with novel microstructures deposited by solution-precursor plasma spray’, Acta Mater., 2001, 49, 2251–2257. doi: 10.1016/S1359-6454(01)00130-6
3.
ZhouC., ZhangQ. and LiY.: ‘Thermal shock behavior of nanostructured and microstructured thermal barrier coatings on a Fe-based alloy’, Surf. Coat. Tech., 2013, 217, 70–75. doi: 10.1016/j.surfcoat.2012.11.074
4.
MoridiA., Hassani-GangarajS. M., GuaglianoM. and DaoM.: ‘Cold spray coating: review of material systems and future perspectives’, Surf. Eng., 2014, 36, (6), 369–395. doi: 10.1179/1743294414Y.0000000270
5.
PourbafraniM., Shoja RazaviR., BakhshiS. R., Loghman-EstarkiM. R. and JamaliH.: ‘Effect of microstructure and phase of nanostructured YSZ thermal barrier coatings on its thermal shock behaviour’, Surf. Eng., 2015, 31, (1), 64–73. doi: 10.1179/1743294414Y.0000000397
6.
KumarS., KantS., SuriN. M. and VermaR.: ‘Mullite based thermal barrier coatings and coating techniques: a review ’, IJAMAE, 2014, 1, (3), 68–73.
7.
MoskalG.: ‘Thermal barrier coatings. Part 1 – characteristics of microstructure and properties, generation and directions of development of bond ’, Arch. Mater. Sci., 2007, 28, 100–112.
8.
LeviC. G., HutchinsonJ. W., Vidal-SétifM. H. and JohnsonC. A.: ‘Environmental degradation of thermal-barrier coatings by molten deposits’, MRS Bull., 2012, 37, (10), 932–941. doi: 10.1557/mrs.2012.230
9.
XiaoyunX. I. E., HongboG. U. O., ShengkaiG. O. N. G. and HuibinX. U.: ‘Hot corrosion behavior of double-ceramic-layer LaTi2Al9O19/YSZ thermal barrier coatings’, Chinese J. Aeronaut., 2012, 25, (1), 137–142. doi: 10.1016/S1000-9361(11)60372-5
10.
Hassani-GangarajS. M., MoridiA. and GuaglianoM.: ‘Critical review of corrosion protection by cold spray coatings’, Surf. Eng., 2015, 31, (11), 803–815. doi: 10.1179/1743294415Y.0000000018
11.
GaoF., YangQ., LiuR. and HuangX.: ‘Oxidation resistance of novel multilayer coatings for gas turbine components’, Surf. Eng., 2014, 30, (9), 624–635. doi: 10.1179/1743294414Y.0000000283
12.
XuY., MiaoQ., LiangW. P., YangJ. J. and YaoZ. J.: ‘Interdiffusion performance and oxidation behaviours of NiCrAlY/Al coatings on γ-TiAl’, Surf. Eng., 2014, 30, (1), 64–70. doi: 10.1179/1743294413Y.0000000200
13.
RahnavardM., Ostad Ahmad GhorabiM. J., RahneinM. and RafieeH.: ‘Effects of incorporation of micro and nano Al2O3 layers on thermal shock behaviour of YSZ thermal barrier coatings’, Can. Metall. Quart., 2016. doi:10.1080/00084433.2016.1196845.
14.
YildirimB. and ErdoganF.: ‘Edge crack problems in homogenous and functionally graded material thermal barrier coatings under uniform thermal loading ’, J. Therm. Stresses, 2004, 27, (4), 311–329. doi: 10.1080/01495730490427564
15.
LeeY. D. and ErdoganF.: ‘Residual thermal stresses in FGM and laminated thermal barrier coating ’, Int. J. Fract., 1995, 69, 145–165. doi: 10.1007/BF00035027
16.
SaeediB., SabourA. and KhoddamiA. M.: ‘Study of microstructure and thermal shock behavior of two types of thermal barrier coatings’, Mater. Corr., 2009, 60, (9), 695–703. doi: 10.1002/maco.200905111
17.
HilleT., TurteltaubS., SuikerA.: ‘Oxide growth and damage evolution in thermal barrier coatings’, Eng. Fract. Mech., 2011, 78, 2139–2152. doi: 10.1016/j.engfracmech.2011.04.003
18.
Loghman-EstarkiaM. R., NejatibM., EdriscH., RazaviaR. S., JamaliaH. and PaksereshtA. H.: ‘Evaluation of hot corrosion behavior of plasma sprayed scandia and yttriaco-stabilized nanostructured thermal barrier coatings in the presence of molten sulfate and vanadate salt ’, J. Eur. Ceram. Soc., 2015, 35, (2), 693–702. doi: 10.1016/j.jeurceramsoc.2014.08.029
19.
WellmanR. G. and NichollsJ. R.: ‘Erosion, corrosion and erosion–corrosion of EB PVD thermal barrier coatings’, Tribol. Int., 2008, 41, 662–657. doi: 10.1016/j.triboint.2007.10.004
20.
KrämerS., YangJ., LeviC. G. and JohnsonC. A.: ‘Thermochemical interaction of thermal barrier coatings with molten CaO–MgO–Al2O3–SiO2 (CMAS) deposits ’, J. Am. Ceram. Soc., 2006, 89, 3167–3175. doi: 10.1111/j.1551-2916.2006.01209.x
21.
SaremiM., AfrasiabiA. and KobayashiA.: ‘Microstructural analysis of YSZ and YSZ/Al2O3 plasma sprayed thermal barrier coatings after high temperature oxidation’, Surf. Coat. Tech., 2008, 202, 3233–3238. doi: 10.1016/j.surfcoat.2007.11.029
22.
BatistaC., PortinhaA., RibeiroR., TeixeiraV. and OliveiraC.: ‘Evaluation of laser-glazed plasma-sprayed thermal barrier coatings under high temperature exposure to molten salts ’, Surf. Coat. Tech., 2006, 200, 6783–6791. doi: 10.1016/j.surfcoat.2005.10.011
23.
TsipasS.: ‘Effect of dopants on the phase stability of zirconia-based plasma sprayed thermal barrier coatings ’, J. Eur. Ceram. Soc., 2010, 30, 61–72. doi: 10.1016/j.jeurceramsoc.2009.08.008
24.
RafieeH., ArabiH. and RastegariS.: ‘Effects of temperature and Al-concentration on formation mechanism of an aluminide coating applied on superalloy IN738LC through a single step low activity gas diffusion process’, J. Alloys Compd, 2010, 505, 206–212. doi: 10.1016/j.jallcom.2010.06.030
25.
RafieeH., RastegariS., ArabiH. and MojaddamiM.: ‘Effects of temperature and Al-concentration on formation mechanism of an aluminide coating applied on super alloy IN738LC through a single-step high activity gas diffusion process’, Iran. J. Mater. Sci. Eng., 2010, 7, 42–49.
26.
MojaddamiM., RastegariS., ArabiH. and RafieeH.: ‘Effect of heat treatment on coating microstructure applied by high activity diffusion process on IN738LC’, Surf. Eng., 2012, 28, (10), 772–777. doi: 10.1179/1743294412Y.0000000064
27.
RafieeH., RastegariS. and ArabiH.: ‘Formation mechanism of IDZ during coating of IN738 by single step gas phase aluminising’, Can. Metall. Quart., 2011, 50, (1), 85–90. doi: 10.1179/000844311X552359