Implementation of an YSZ coating material to prevent clogging of the submerged entry nozzle (SEN) during continuous casting of Ce-treated steels

Abstract

The possibility to reduce clogging in the submerged entry nozzle (SEN) during continuous casting of Ce alloyed stainless steels has been studied. This was done by implementing a new plasma coating material, consisting of yttria-stabilised zirconia (YSZ). The coating was first tested in pilot–plant trials; where the amount of steel teemed through the plasma-coated nozzles was monitored. Thereafter, samples of the coatings from the nozzles were studied using a FEG-SEM equipped with EDS. In addition, the coating material was tested in industrial trials where the performance was judged with respect to the clogging tendency detected as the movement of the stopper rod. The results from both the pilot–plant trials and industrial trials showed that the use of an YSZ coating led to a decreased clogging tendency during the casting in comparison to when using an uncoated SEN. Specifically, the pilot–plant trials showed that the clogging factor was lowered when implementing the YSZ coatings. Furthermore, the industrial trials showed that the clogging tendency, measured by the stopper rod movements, were lower when implementing the YSZ coating.

Get full access to this article

View all access options for this article.

References

Memarpour

Brabie

Jönsson

P. G.

: ‘Studies on the decarburization of commercial submerged entry nozzles', Steel Grips J. Steel Related Mater. Plants Equipment, 2011, 9, 121–127.

Memarpour

Brabie

Jönsson

P. G.

: ‘Studies of effect of glass/silicon powder coatings on clogging behaviour of submerged entry nozzles when using REM alloyed stainless steels', Ironmak. Steelmak., 2011, 38, (3), 229–239. doi: 10.1179/1743281210Y.0000000005

Vermeulen

Coletti

Wollants

Blanpain

Haers

: ‘Clogging in submerged entry nozzles', Steel Res. Process Metall., 2000, 71, (10), 391–395. doi: 10.1002/srin.200001334

Svensson

J. K. S.

Memarpour

Brabie

Jönsson

P. G.

: ‘Studies of the decarburisation phenomena during preheating of submerged entry nozzles (SEN) in continuous casting processes', Ironmak. Steelmak., ISSN: 0301-9233, published online 18th of March 2016.

Memarpour

Brabie

Jönsson

P. G.

: ‘Post-mortem study of the internal coated SENs (submerged entry nozzle) respecting clogging phenomena’, 7th European Continuous Casting Conference Proceedings, Refractory material and tundish lining, Session 14, Düsseldorf, Germany, 27 June – 1 July, 2011, 1–10.

Poirier

Guiban

M. A.

Tassot

Hanse

Thillou

Benson

: ‘Development of new submerged nozzles to reduce alumina build up n in continuous casting’, UNITECR ‘95 Congress Proceedings, Global Development of Refractories, Kyoto, Japan, 19–22 November, The Technical Association of Refractories, 1995, 79–86.

Poirier

Thillou

Guiban

M. A.

Provost

: ‘Mechanisms and countermeasures of alumina clogging in submerged nozzles’, Steelmaking Conference Proceedings, 78th, ISS-AIME, Nashville, TN, 1995, 451–456.

Ohyabu

Kuma

Kato

Arai

Yamazaki

: ‘Development of technology for REM additional austenite stainless steel at Naoetsu Works’, Proceedings, International Congress Stainless Steel ‘99 Science and Market, Innovation in Processes and Products, 3rd European Congress, Sardinia, Italy, 6–9 June, 1999, 2, 147–156.

Kojola

Ekerot

Andersson

Jönsson

P. G.

: ‘Pilot-plant study of nozzle clogging mechanisms during casting of REM treated stainless steels', Ironmak. Steelmak., 2011, 38, (1), 1–11. doi: 10.1179/030192310X12690127076398

10.

Katsumata

Todoroki

: ‘Effect of rare earth metal on inclusion composition in molten stainless steel’, ISS Trans., 2002, 51–57.

11.

Suosheng

Qiyong

Fuyuan

Guanglu

Zhoungyin

: ‘Study on the nozzle blockage mechanism of steel containing rare earth metals during casting’, Scand. J. Metall., 1985, 14, 175–182.

12.

Keming

Ruiming

: ‘Research on determination of the rare-earth content in metal phases of steel’, Metall. Trans. A, 1986, 17A, 315–323. doi: 10.1007/BF02643907

13.

Memarpour

: ‘An experimental study of submerged entry nozzles (SEN) focusing on decarburization and clogging’, Doctoral Thesis in Applied Process Metallurgy, Stockholm Sweden, KTH Industrial Engineering and Management, 2011, Supplement 5.

14.

von Niessen

Gindrat

Refke

: ‘Vapor phase deposition using plasma spray-PVD™’, J. Thermal Spray Technol., 2010, 19, 502–509. doi: 10.1007/s11666-009-9428-9

15.

S. G.

Zhang

H. Y.

Tian

G. L.

Xia

Z. L.

Shao

J. D.

Fan

Z. X.

: ‘Y₂O₃ stabilized ZrO₂ thin films deposited by electron beam evaporation: structural, morphological characterization and laser induced damage threshold’, Appl. Surf. Sci., 2006, 253, 1561–1565. doi: 10.1016/j.apsusc.2006.02.044

16.

Kojola

Ekerot

Jönsson

: ‘Pilot-plant study of clogging rates in low carbon and stainless steel grades', Ironmak. Steelmak., 2011, 38, (2), 81–89. doi: 10.1179/030192310X12706364542704

17.

Bannenberg

: ‘Inclusion modification to prevent nozzle clogging’, Steelmaking Conference Proceedings, Nashville, Tennessee, USA, April 1995, 78, 457–463.

18.

Svensson

J. K. S.

Larsson

Memarpour

Brabie

Jönsson

P. G.

: ‘Post-mortem Studies of Submerged Entry Nozzles (SEN) Coated with Yttria Stabilized Zirconia (YSZ)’, The 6th International Congress on the Science and Technology of Steelmaking, The Chinese Society for Metals, Beijing, China, May 12–14, China Machine Press, ISBN 978–7-111-50125-1, 2015, 469–472.