Hot workability analysis and processing parameters optimisation for 20CrMnTiH steel by combining processing map with microstructure

The processing map of 20CrMnTiH steel is developed by using the dynamic material model according to the hot compression experiments, performed on a Gleeble-3500 thermal simulator at the temperature range of 850–1150°C and the strain rate of 0.01–1 s⁻¹. Hot workability characteristics of 20CrMnTiH steel are analysed based on the developed processing map. The safe deformation regions with higher power dissipation efficiency η exhibit the dynamic recrystallisation (DRX) mechanism and show fine and homogeneous microstructure. The unstable regions with negative instability coefficient ξ occur at both lower temperature with all strain rates and at high temperature with high strain rate at the strain of 0.2. The area of instability gradually decreases with the increasing strain and only appears at lower temperature and higher strain rate when the strain is above 0.2. The unstable regions indicate the flow localisation by microstructure analysis. Combining with the developed processing map with DRX behaviour, the optimal values of hot processing parameters for 20CrMnTiH steel are obtained to achieve good hot workability and small grains sizes at the process parameters ranged at 1036–1070°C/0.1–1 s⁻¹ and 918–985°C/0.01–0.014 s⁻¹.