It is imperative to reduce the pollution and energy consumption in the blast furnace ironmaking process. High pellets operation is a developing direction in the future. The function of blast furnace slag system cannot be ignored. In order to balance the MgO content in blast furnace slag and improve the metallurgical properties of pellets in the high pellets ratio operation, the research on MgO-bearing pellets is necessary. In this paper, the metallurgical properties of MgO-bearing pellets and the properties of blast furnace slag effect by MgO in different raw material conditions, especially for Vanadium Titanomagnetite, were analysed and summarized. This review provided a reference for the development of MgO-bearing pellets and the performance of blast furnace slag effect by MgO. It is hoped to reduce pollution and promote the technical progress of blast furnace ironmaking.
Get full access to this article
View all access options for this article.
References
1.
ScarlettNVYPowncebyMIMadsenICet al.Reaction sequences in the formation of silico-ferrites of calcium and aluminum in iron ore sinter. Metall Mater Trans B-Proc Metall Mater Proc Sci. 2004;35:929–936. doi:10.1007/s11663-004-0087-4.
2.
KouMLiHWuSet al.Study on the sintering melting characteristics of Meishan concentrate and its influencing factors. Ironmak Steelmak. 2018;46:199–205. doi:10.1080/03019233.2018.1507069.
3.
WuSLiHZhangWet al.Effect of thermodynamic melt formation characteristics on liquid phase fluidity of iron ore in the sintering process. Metals. 2019;9. doi:10.3390/met9040404.
4.
WuSLiuXZhouQet al.Low temperature reduction degradation characteristics of sinter, pellet and lump ore. J Iron Steel Res Int. 2011;18:20–24. doi:10.1016/s1006-706x(11)60098-8.
5.
GuoZCFuZX.Current situation of energy consumption and measures taken for energy saving in the iron and steel industry in China. Energy. 2010;35:4356–4360. doi:10.1016/j.energy.2009.04.008.
6.
DongLZhangHFujitaTet al.Environmental and economic gains of industrial symbiosis for Chinese iron/steel industry: Kawasaki’s experience and practice in Liuzhou and Jinan. J Clean Prod. 2013;59:226–238. doi:10.1016/j.jclepro.2013.06.048.
7.
XuWWanBZhuTet al.CO2 emissions from China’s iron and steel industry. J Clean Prod. 2016;139:1504–1511. doi:10.1016/j.jclepro.2016.08.107.
8.
GuptaPKRaoASSekharVRet al.Burden distribution control and its optimisation under high pellet operation. Ironmak Steelmak. 2013;37:235–239. doi:10.1179/174328109x422566.
9.
EklundNLindblomBWikströmJ-O.Operation at high pellet ratio and without external slag formers-trials in an experimental blast furnace. Steel Res. 2008;80:379–384. doi:10.2374/SRI09SP025.
10.
WangBChenWZhangYZet al.Design and optimisation of charging ingredients and structure in an ironmaking system (Part II). Ironmak Steelmak. 2016;44:59–65. doi:10.1080/03019233.2016.1156222.
11.
WuSSuBLiuXLet al.Optimisation of the blast furnace burden based on its primary slag formation behaviour. Ironmak Steelmak. 2016;45:50–57. doi:10.1080/03019233.2016.1237073.
12.
ChenMZhangDKouMet al.Viscosities of iron blast furnace slags. ISIJ Int. 2014;54:2025–2030. doi:10.2355/isijinternational.54.2025.
13.
OlivierKDarquennesABenboudjemaFet al.Early-age self-healing of cementitious materials containing ground granulated blast-furnace slag under water curing. J Adv Concr Technol. 2016;14:717–727. doi:10.3151/jact.14.717.
14.
ShankarAGörnerupMLahiriAKet al.Estimation of viscosity for blast furnace type slags. Ironmak Steelmak. 2013;34:477–481. doi:10.1179/174328107x17467.
15.
KravchenkoVPBaglyukGATrotsanAI.Effectiveness of jet milling for producing superfine powders from blast-furnace slag. Powder Metall Met Ceram. 2017;55:745–750. doi:10.1007/s11106-017-9863-y.
16.
SongKParkSKimWet al.Effects of experimental parameters on the extraction of silica and carbonation of blast furnace slag at atmospheric pressure in low-concentration acetic acid. Metals. 2017;7. doi:10.3390/met7060199.
17.
ChunTJMuGTMengQMet al.Preparation of MgO added iron ore pellets and effects on a pilot scale blast furnace operation. J Min Metall Sect B. 2019;55:167–175. doi:10.2298/jmmb181129015c.
18.
HildingTGuptaSSahajwallaVet al.Degradation behaviour of a high CSR coke in an experimental blast furnace: effect of carbon structure and alkali reactions. ISIJ Int. 2005;45:1041–1050. doi:10.2355/isijinternational.45.1041.
19.
HaapakangasJUusitaloJMattilaOet al.A method for evaluating coke hot strength. Steel Res Int. 2013;84:65–71. doi:10.1002/srin.201200078.
20.
GuoWXueQLiuYet al.Investigation on burden particle softening and melting process under high reduction potential condition. High Temp Mater Process. 2016;35:805–812. doi:10.1515/htmp-2015-0031.
21.
SivrikayaOArolAİ. The bonding/strengthening mechanism of colemanite added organic binders in iron ore pelletization. Int J Miner Process. 2012;110-111:90–100. doi:10.1016/j.minpro.2012.04.010.
22.
WangSGuoYZhengFet al.Improvement of roasting and metallurgical properties of fluorine-bearing iron concentrate pellets. Powder Technol. 2020;376:126–135. doi:10.1016/j.powtec.2020.08.004.
23.
ForsmoSPEApelqvistAJBjörkmanBMTet al.Binding mechanisms in wet iron ore green pellets with a bentonite binder. Powder Technol. 2006;169:147–158. doi:10.1016/j.powtec.2006.08.008.
24.
ForsmoSPESamskogPOBjörkmanBMT.A study on plasticity and compression strength in wet iron ore green pellets related to real process variations in raw material fineness. Powder Technol. 2008;181:321–330. doi:10.1016/j.powtec.2007.05.023.
25.
DevasahayamS.A novel iron ore pelletization for increased strength under ambient conditions. Sust Mater Technol. 2018;17. doi:10.1016/j.susmat.2018.e00069.
26.
ZhuDYangCPanJet al.Comparison of the oxidation behaviors of high FeO chromite and magnetite concentrates relevant to the induration of ferrous pellets. Metall Mater Trans B. 2016;47:2919–2930. doi:10.1007/s11663-016-0770-2.
27.
XuCZhangJLiuZet al.A comprehensive study of pore characteristics, formation mechanism and reliability analysis with advanced characterization methods within pellets. Trans Indian Inst Met. 2020;73:2503–2510. doi:10.1007/s12666-020-02059-8.
28.
Sandeep KumarTKViswanathanNNAhmedHet al.Investigation of magnetite oxidation kinetics at the particle scale. Metall Mater Trans B. 2018;50:150–161. doi:10.1007/s11663-018-1459-5.
29.
ParkHSohnITsalapatisJet al.Reduction behavior of dolomite-fluxed magnetite: coke composite pellets at 1573 K (1300°C). Metall Mater Trans B. 2018;49:1109–1118. doi:10.1007/s11663-018-1208-9.
30.
JuJ-tMaKXingX-det al.Investigate the oxidation induration mechanism of manganese-bearing magnetite concentrate pellets. Ironmak Steelmak. 2022: 1–8. doi:10.1080/03019233.2022.2032976.
31.
HanG-hJiangTZhangY-bet al.High-temperature oxidation behavior of vanadium, titanium-bearing magnetite pellet. J Iron Steel Res Int. 2011;18:14–19. doi:10.1016/s1006-706x(11)60097-6.
32.
FerreiraSCoresARoblaJIet al.The influence of gangue and additives on the divalent iron content of magnetite pellets. Steel Res Int. 2014;85:261–272. doi:10.1002/srin.201300370.
33.
ShenFGaoQWeiGet al.Densification process of MgO bearing pellets. Steel Res Int. 2015;86:644–650. doi:10.1002/srin.201400372.
34.
ShenFGaoQJiangXet al.Effect of magnesia on the compressive strength of pellets. Int J Min Met Mater. 2014;21:431–437. doi:10.1007/s12613-014-0926-5.
35.
GaoQJiangXGuoWet al.Effects of MgO on densification and consolidation of oxidized pellets. J Cent South Univ. 2014;21:877–883. doi:10.1007/s11771-014-2013-5.
36.
FanXGanMJiangTet al.Influence of flux additives on iron ore oxidized pellets. J Cent South Univ: Sci Technol. 2010;17:732–737. doi:10.1007/s11771−010−0548−7.
37.
WangRZhangJLiuZet al.Effect of CaO and MgO additives on the compressive strength of pellets: exploration on the decisive stage during induration. Powder Technol. 2021;390:496–503. doi:10.1016/j.powtec.2021.06.001.
38.
GuoYGuoX.Formation of [Mg1-x, Fex]O·Fe2O3 in solid-state reactions between MgO and Fe2O3 in the Fe2O3 -rich system. ISIJ Int2017;57:228–236. doi:10.2355/isijinternational.ISIJINT-2016-451.
39.
WangRZhangJLiuZet al.Effect of lime addition on the mineral structure and compressive strength of magnesium containing pellets. Powder Technol. 2020;376:222–228. doi:10.1016/j.powtec.2020.08.038.
40.
LiJAnH-fLiuW-xet al.Effect of basicity on metallurgical properties of magnesium fluxed pellets. J Iron Steel Res Int. 2019;27:239–247. doi:10.1007/s42243-019-00307-w.
41.
HeikkiläAIljanaMBartuschHet al.Reduction of iron ore pellets, sinter, and lump ore under simulated blast furnace conditions. Steel Res Int. 2020;91:2000047. doi:10.1002/srin.202000047.
42.
FanYZhangYLiZet al.Mechanism on reduction swelling of pellets prepared from Bayan Obo iron ore concentrate. Ironmak Steelmak. 2021: 1–11. doi:10.1080/03019233.2021.1939943.
43.
HanG-hZhangDHuangY-fet al.Swelling behavior of hot preheated pellets in reduction roasting process. J Cent South Univ. 2016;23:2792–2799. doi:10.1007/s11771-016-3342-3.
44.
IljanaMKemppainenAPaananenTet al.Effect of adding limestone on the metallurgical properties of iron ore pellets. Int J Miner Process. 2015;141:34–43. doi:10.1016/j.minpro.2015.06.004.
45.
LiGHTangZKZhangYBet al.Reduction swelling behaviour of haematite/magnetite agglomerates with addition of MgO and CaO. Ironmak Steelmak. 2013;37:393–397. doi:10.1179/030192310x12690127076352.
46.
XuBHouTChenX-let al.Effect of dolomite on reduction swelling property of iron ore pellets. J Cent South Univ. 2013;20:2806–2810. doi:10.1007/s11771-013-1800-8.
47.
DwarapudiSBanerjeePKChaudharyPet al.Effect of fluxing agents on the swelling behavior of hematite pellets. Int J Miner Process. 2014;126:76–89. doi:10.1016/j.minpro.2013.11.012.
48.
GaoQShenFWeiGet al.Effects of MgO containing additive on low-temperature metallurgical properties of oxidized pellet. J Iron Steel Res Int. 2013;20:25–28. doi:10.1016/S1006-706X(13)60121-1.
49.
ZhuDChunTPanJet al.Influence of basicity and MgO content on metallurgical performances of Brazilian specularite pellets. Int J Miner Process. 2013;125:51–60. doi:10.1016/j.minpro.2013.09.008.
50.
WangPDaiMChunTet al.Influence of the gangue compositions on the reduction swelling index of hematite briquettes. Metall Mater Trans B. 2021;52B:2021–2139. doi:10.1007/s11663-021-02177-8.
51.
QingGWuKTianYet al.Effect of the firing temperature and the added MgO on the reduction swelling index of the pellet with low SiO2 content. Ironmak Steelmak. 2016;45:83–89. doi:10.1080/03019233.2016.1242248.
52.
ZhangY-bChenX-jSuZ-jLiuSChenFWuN-yJiangT, Improving properties of fluxed iron ore pellets with high-silica by regulating liquid phase, J Iron Steel Res Int. 29(2021)1381–1392. doi:10.1007/s42243-021-00665-4.
53.
RajshekarYPalJVenugopalanT.Sintering characteristics and kinetics of acidic haematite ore pellets with and without mill scale addition. Ironmak Steelmak. 2016;45:325–334. doi:10.1080/03019233.2016.1264153.
54.
HaghiSMAZabettAMirjaliliM.Mechanism of reduction of hematite-magnetite hollow cylindrical pellet by graphite-calcium carbonate mixture. Metall Mater Trans B. 2020: 1460–1468. doi:10.1007/s11663-020-01852-6.
55.
ZhangYBLiGHJiangTet al.Reduction behavior of tin-bearing iron concentrate pellets using diverse coals as reducers. Int J Miner Process. 2012;110-111:109–116. doi:10.1016/j.minpro.2012.04.003.
56.
ChenYZhaoHWangC.Two-stage reduction for the preparation of ferronickel alloy from nickel laterite ore with low Co and high MgO contents. Int J Min Met Mater. 2017;24:512–522. doi:10.1007/s12613-017-1432-3.
57.
CheYMaiGLiSet al.Kinetic mechanism of magnesium production by silicothermic reduction of CaO·MgO in vacuum. Trans Nonferrous Met Soc China. 2020;30:2812–2822. doi:10.1016/s1003-6326(20)65423-1.
58.
DwarapudiSSekharCPaulIet al.Effect of fluxing agents on reduction degradation behaviour of hematite pellets. Ironmak Steelmak. 2016;43:180–191. doi:10.1179/1743281215Y.0000000030.
59.
DwarapudiSGhoshTKTathavadkarVet al.Effect of MgO in the form of magnesite on the quality and microstructure of hematite pellets. Int J Miner Process. 2012;112-113:55–62. doi:10.1016/j.minpro.2012.06.006.
60.
BahgatMHalimKSAI.NasrMet al.Reduction behaviour of wiistite doped with MgO. Process Metall – Ironmak. 2007;70:443–450. doi:10.1002/srin.200706228.
61.
SembergPAnderssonCBjörkmanB.Interaction between iron oxides and olivine in magnetite pellets during reduction to femet at temperatures of 1000–1300°C. ISIJ Int. 2013;53:1341–1349. doi:10.2355/isijinternational.53.1341.
62.
NogueiraPFFruehanRJ.Blast furnace burden softening and melting phenomena: part I. pellet bulk interaction observation. Metall Mater Trans B. 2004;35B:829–838. doi:10.1007/s11663-004-0077-6.
63.
NogueiraPFFruehanRJ.Blast furnace burden softening and melting phenomena: part II. evolution of the structure of the pellets. Metall Mater Trans B. 2005;36B:583–590. doi:10.1007/s11663-005-0049-5.
64.
NogueiraPFFruehanRJ.Blast furnace burden softening and melting phenomena: part III. melt onset and initial microstructural transformations in pellets. Metall Mater Trans B. 2006;37B:551–558. doi:10.1007/s11663-006-0038-3.
65.
ChewSJZulliPMaldonadoDet al.Melt down behaviour of a fused layer in the blast furnace cohesive zone. ISIJ Int. 2003;43:304–313. doi:10.2355/isijinternational.43.304.
66.
KaushikPFruehanRJ.Mixed burden softening and melting phenomena in blast furnace operation part 1 – X-ray observation of ferrous burden. Ironmak Steelmak. 2006;33:507–519. doi:10.1179/174328106x118107.
67.
KaushikPFruehanRJ.Mixed burden softening and melting phenomena in blast furnace operation part 2 – mechanism of softening and melting and impact on cohesive zone. Ironmak Steelmak. 2013;33:520–528. doi:10.1179/174328106x118125.
68.
KaushikPFruehanRJ.Mixed burden softening and melting phenomena in blast furnace operation part 3 – mechanism of burden interaction and melt exudation phenomenon. Ironmak Steelmak. 2013;34:10–22. doi:10.1179/174328106x118161.
69.
PanY-zZuoH-bWangJ-set al.Review on improving gas permeability of blast furnace. J Iron Steel Res Int. 2019;27:121–131. doi:10.1007/s42243-019-00321-y.
70.
LiTLSunCYLiuXYet al.The effects of MgO and Al2O3 behaviours on softening-melting properties of high basicity sinter. Ironmak Steelmak. 2018;45:755–763. doi:10.1080/03019233.2017.1337263.
71.
DwarapudiSGhoshTKShankarAet al.Effect of pellet basicity and MgO content on the quality and microstructure of hematite pellets. Int J Miner Process. 2011;99:43–53. doi:10.1016/j.minpro.2011.03.004.
72.
DwarapudiSGhoshTKShankarAet al.Effect of pyroxenite flux on the quality and microstructure of hematite pellets. Int J Miner Process. 2010;96:45–53. doi:10.1016/j.minpro.2010.06.002.
73.
KemppainenAOhnoK-iIljanaMet al.Softening behaviors of acid and olivine fluxed iron Ore pellets in the cohesive zone of a blast furnace. ISIJ Int. 2015;55:2039–2046. doi:10.2355/isijinternational.ISIJINT-2015-023.
74.
IljanaMHeikkinenE-PFabritiusT.Estimation of iron ore pellet softening in a blast furnace with computational thermodynamics. Metals. 2021;11:1515. doi:10.3390/met11101515.
75.
ZhouMJiangTYangS-tet al.Sintering behaviors and consolidation mechanism of high-chromium vanadium and titanium magnetite fines. Int J Min Met Mater. 2015;22:917–925. doi:10.1007/s12613-015-1150-7.
76.
YangSZhouMXueXet al.Isothermal reduction kinetics of chromium-bearing vanadium–titanium sinter reduced with CO gas at 1173 K. Jom. 2019;71:2812–2820. doi:10.1007/s11837-019-03533-5.
77.
ZhaoWChuMLiuZet al.High-Temperature interactions between vanadium-titanium magnetite carbon composite hot briquettes and pellets under simulated blast furnace conditions. Metall Mater Trans B. 2019;50:1878–1895. doi:10.1007/s11663-019-01616-x.
78.
FuGLiWChuMet al.Influence mechanism of SiO2 on the oxidation behavior and induration process of hongge vanadium titanomagnetite pellets. Metall Mater Trans B. 2019;51:114–123. doi:10.1007/s11663-019-01734-6.
79.
ZhouMYangSJiangTet al.Influence of coke content on sintering process of chromium-containing vanadium-titanium magnetite. J Wuhan Univ Technol-Mater Sci Ed. 2018;33:68–72. doi:10.1007/s11595-018-1787-y.
80.
LiWWangNFuGet al.Effect of V2O5 addition on the oxidation induration process of Hongge vanadium titanomagnetite pellet. Ironmak Steelmak. 2017;45:913–918. doi:10.1080/03019233.2017.1412383.
81.
LiWFuGChuMet al.Influence of MgO on the oxidation and induration of Hongge vanadium titanomagnetite pellets. Ironmak Steelmak. 2019;47:837–843. doi:10.1080/03019233.2019.1615815.
82.
GaoZChengGXueXet al.Property investigations of low-grade vanadium-titanium magnetite pellets with different MgO contents. Steel Res Int. 2018;89:1700543. doi:10.1002/srin.201700543.
83.
LiuHPengSZhangKet al.Effect of finely ground limestone and dolomite on compression strength and reduction swelling of vanadium-titanium pellets. Materials (Basel). 2021;14. doi:10.3390/ma14164433.
84.
ZhaoWChuMFengCet al.Effect of MgO addition on the metallurgical properties of the vanadium-titanium pellet with simulating blast furnace conditions. Ironmak Steelmak. 2018;47:388–397. doi:10.1080/03019233.2018.1527538.
85.
WangSGuoYZhengFet al.Behavior of vanadium during reduction and smelting of vanadium titanomagnetite metallized pellets. Trans Nonferrous Met Soc China. 2020;30:1687–1696. doi:10.1016/s1003-6326(20)65330-4.
86.
SongWLuoG-PSunC-Cet al.Effect of K and Na on reduction swelling performance of oxidized roasted briquettes. High Temp Mater Processes. 2021;40:241–252. doi:10.1515/htmp-2020-0091.
87.
BahgatMAbdel HalimKSEl-KeleshHAet al.Metallic iron whisker formation and growth during iron oxide reduction: K2O effect. Ironmak Steelmak. 2013;36:379–387. doi:10.1179/174328109x445660.
88.
IljanaMMattilaOAlatarvasTet al.Effect of circulating elements on the dynamic reduction swelling behaviour of olivine and acid iron ore pellets under simulated blast furnace shaft conditions. ISIJ Int. 2013;53:419–426. doi:10.2355/isijinternational.53.419.
89.
ChaiYFanYLiZet al.Kinetics of reduction in stages of pellets prepared from the Bayan Obo iron ore concentrate. ACS Omega. 2022;7:7759–7768. doi:10.1021/acsomega.1c06563.
90.
NurjamanFAstutiWBahfieFet al.Study of selective reduction in lateritic nickel ore: saprolite versus limonite. Mater Today Proc. 2021;44:1488–1494. doi:10.1016/j.matpr.2020.11.687.
91.
RaoMLiGJiangTet al.Carbothermic reduction of nickeliferous laterite ores for nickel pig iron production in China: a review. Jom. 2013;65:1573–1583. doi:10.1007/s11837-013-0760-7.
92.
NurjamanFHandokoASBahfieFet al.Effect of modified basicity in selective reduction process of limonitic nickel ore. J Mater Res Technol. 2021;15:6476–6490. doi:10.1016/j.jmrt.2021.11.052.
93.
YangMLvXWeiRet al.Wetting behavior of TiO2 by calcium ferrite slag at 1523 K. Metall Mater Trans B. 2018;49:2667–2680. doi:10.1007/s11663-018-1360-2.
94.
FengCTangJGaoLet al.Effects of CaO/SiO2 on viscous behaviors and structure of CaO-SiO2-11.00wt%MgO-11.00wt%Al2O3-43.00wt%TiO2 slag systems. ISIJ Int. 2019;59:31–38. doi:10.2355/isijinternational.ISIJINT-2018-444.
95.
ChuangHCHwangWSLiuSH.Effects of basicity and FeO content on the softening and melting temperatures of the CaO-SiO2-MgO-Al2O3 slag system. Mater Trans. 2009;50:1448–1456. doi:10.2320/matertrans.MRA2008372.
96.
DuanWJYuQBLiuJXet al.Research on characteristics and modelling estimation of molten BF slag viscosity in the process of slag waste heat recovery. Ironmak Steelmak. 2016: 1–9. doi:10.1080/03019233.2016.1234733.
97.
JiaoKZhangJLiuZet al.Effect of MgO/Al2O3 ratio on viscosity of blast furnace primary slag. High Temp Mater Proc. 2019;38:354–361. doi:10.1515/htmp-2018-0019.
98.
FengCGaoL-hTangJet al.Effects of MgO/Al2O3 ratio on viscous behaviors and structures of MgO–Al2O3–TiO2–CaO–SiO2 slag systems with high TiO2 content and low CaO/SiO2 ratio. Trans Nonferrous Met Soc China. 2020;30:800–811. doi:10.1016/s1003-6326(20)65255-4.
99.
YaoLRenSLiuGet al.Study of the effect of the MgO/Al2O3 ratio on viscosity of blast furnace slag. Metall Res Technol. 2015;112. doi:10.1051/metal/2015036.
100.
KouMWuSMaXet al.Phase equilibrium studies of CaO-SiO2-MgO-Al2O3 system with binary basicity of 1.5 related to blast furnace slag. Metall Mater Trans B. 2016;47:1093–1102. doi:10.1007/s11663-016-0584-2.
101.
JiangCLiKZhangJet al.Molecular dynamics simulation on the effect of MgO/Al2O3 ratio on structure and properties of blast furnace slag under different basicity conditions. Metall Mater Trans B. 2018;50:367–375. doi:10.1007/s11663-018-1450-1.
102.
ViS-HViS.Bosh slag chemistry control for high PCR and Low slag volume blast furnace operation. Process Metall. 2003;74:413–417. doi:10.1002/srin.200300207.
YaoLRenSWangXet al.Effect of Al2O3, MgO, and CaO/SiO2 on viscosity of high alumina blast furnace slag. Steel Res Int. 2016;87:241–249. doi:10.1002/srin.201500021.
105.
GuoYShenFZhengHet al.A sulphide-capacity perdiction model of blast-furnace slag. Mater Tehnolo / Mater Technol. 2021;55:725–732. doi:10.17222/mit.2021.157.
106.
GuoYShenFZhengHet al.Activity of MgO in CaO–SiO2 –MgO–Al2O3 melts for blast furnace slag at 1 873 K. ISIJ Int. 2021;61:2724–2730. doi:10.2355/isijinternational.ISIJINT-2021-224.
107.
JiangCLiKZhangJet al.Effect of MgO/Al2O3 ratio on the structure and properties of blast furnace slags: A molecular dynamics simulation. J Non-Cryst Solids. 2018;502:76–82. doi:10.1016/j.jnoncrysol.2018.06.043.
108.
YoshikawaTHosokawaMTanakaT.Mgo effect on hydrothermal solidification of blast furnace slag. ISIJ Int. 2008;48:557–562.
109.
RenQZhangYYueLet al.Investigation on the effect of MgO content on the crystallization behavior of synthetic BF slag. Mater Manuf Process. 2018: 1–7. doi:10.1080/10426914.2018.1424903.
110.
MarkandeyaAShanahanNGunatilakeDMet al.Influence of slag composition on cracking potential of slag-portland cement concrete. Constr Build Mater. 2018;164:820–829. doi:10.1016/j.conbuildmat.2017.12.216.
111.
LiPYuQQinQet al.The effects of slag compositions on the coal gasification reaction in molten blast furnace slag. Energy Sources Part A. 2013;36:73–79. doi:10.1080/15567036.2011.606870.
112.
JiangTLiaoD-mZhouMet al.Rheological behavior and constitutive equations of heterogeneous titanium-bearing molten slag. Int J Min Met Mater. 2015;22:804–810. doi:10.1007/s12613-015-1137-4.
113.
LiangHChuMFengCet al.Optimisation study and affecting mechanism of CaO/SiO2 and MgO on viscous behaviours of titanium-bearing blast furnace slag. Ironmak Steelmak. 2018: 1–12. doi:10.1080/03019233.2018.1482819.
114.
QiuGZhanDJiangZet al.Optimisation of the MgO/Al2O3 ratio of high-alumina BF slag based on MOPSO algorithm. Ironmak Steelmak. 2017: 1–9. doi:10.1080/03019233.2017.1405176.
115.
ZhangXJiangTXueXet al.Influence of MgO/Al2O3 ratio on viscosity of blast furnace slag with high Al2O3 content. Steel Res Int. 2016;87:87–94. doi:10.1002/srin.201400523.
116.
PangZLvXJiangYet al.Blast furnace ironmaking process with super-high TiO2 in the slag: viscosity and melting properties of the slag. Metall Mater Trans B. 2019;51:722–731. doi:10.1007/s11663-019-01756-0.
117.
JiaoKZhangJLiuZet al.Analysis of blast furnace hearth sidewall erosion and protective layer formation. ISIJ Int. 2016;56:1956–1963. doi:10.2355/isijinternational.ISIJINT-2016-168.
118.
DastidarMGBhattacharyyaASarkarBKet al.The effect of alkali on the reaction kinetics and strength of blast furnace coke. Fuel. 2020;268:117388. doi:10.1016/j.fuel.2020.117388.
119.
JiaoKXZhangJLLiuZJet al.Circulation and accumulation of harmful elements in blast furnace and their impact on the fuel consumption. Ironmak Steelmak. 2016;44:344–350. doi:10.1080/03019233.2016.1210913.
120.
ChenSWangWXuRet al.Influence of multiple factors on the alkali metal enrichment in blast furnaces by a thermodynamic model. Ironmak Steelmak. 2020;47:219–227. doi:10.1080/03019233.2019.1709700.
121.
ChenYDengYLiuRet al.Optimization of alkali metals discharge performance of blast furnace slag and its extreme value model. High Temp Mater Process. 2022;41:306–314. doi:10.1515/htmp-2022-0013.
122.
WangGWangJ-sXueQ-g.Properties of boron-rich slag separated from boron-bearing iron concentrate. J Cent South Univ. 2018;25:783–794. doi:10.1007/s11771-018-3783-y.