The influences of microstructure and inclusion on cold cracking were studied in high-strength steel welds of YS 600 MPa grade using the Y-groove test. The weld microstructure showed a mixture of acicular ferrite, bainite and predominantly martensite. Cold crack fractography identified intergranular fracture (IF) and quasi-cleavage fracture (QCF). Bainite and martensite predominated on the surface and subsurface of IF while the QCF showed inclusions that nucleated acicular ferrite. The influence of inclusions on cold cracking can be described as follows: (i) the inclusions acted as nucleation sites of QCF, (ii) the inclusions contributed to the nucleation and growth of micro-cracks and (iii) new cracks were produced from inclusions when a crack impinged on the inclusions. Inclusions smaller than 2 μm increased the cold crack resistance by contributing to the nucleation of acicular ferrite. Inclusions larger than 2 μm increased the cold crack susceptibility by inducing crack nucleation in welds.
KouS.: ‘Welding metallurgy’, 2nd edn, 2002, New York, John Wiley and Sons.
2.
HartP. H. M.: ‘Resistance to hydrogen cracking in steel weld metal’, Weld. J., 1986, 65, 14–22.
3.
YiH. J., LeeY. J., KimJ. Y. and KangS. S.: ‘Effect of microstructure and chemical composition on cold crack susceptibility of high-strength weld metal’, J. Mech. Sci. Technol., 2011, 25, 2185–2193. doi: 10.1007/s12206-011-0529-2
4.
SeoJ. S., KimH. J. and RyooH. S.: ‘Effect of grain boundary ferrite on susceptibility to cold cracking in high-strength weld metal’, Met. Mater. Int., 2008, 14, 515–522. doi: 10.3365/met.mat.2008.08.515
5.
KarlssonL. and BhadeshiaH. K. D. H.: ‘Some European developments in welding consumables’, J. Jpn. Weld. Soc., 2011, 80, 110–119. doi: 10.2207/jjws.80.110
6.
LeeM. J. and KangN. H.: ‘The effects of microstructure on cold crack in high-strength weld metals’, J. KWJS, 2014, 32, 22–27.
7.
JiangQ. L., LiY. J., WangJ. and ZhangL.: ‘Effects of inclusions on formation of acicular ferrite and propagation of crack in high strength low alloy steel weld metal’, Mater. Sci. Technol., 2011, 20, 1565–1569. doi: 10.1179/026708310X12815992418535
8.
GreggJ. M. and BhadeshiaH. K. D. H.: ‘Solid-state nucleation of acicular ferrite on minerals added to molten steel’, Acta Mater., 1997, 45, 739–748. doi: 10.1016/S1359-6454(96)00187-5
9.
LeeT. K., KimH. J., KangB. Y. and HwangS. K.: ‘Effect of inclusion size on the nucleation of acicular ferrite in welds’, ISIJ Int., 2000, 40, 1260–1268. doi: 10.2355/isijinternational.40.1260
10.
BabuS. S.: ‘The mechanism of acicular ferrite in weld deposits’, Curr. Opin. Solid State Mater. Sci., 2004, 8, 267–278. doi: 10.1016/j.cossms.2004.10.001
11.
LiuS. and OlsonD. L.: ‘The role of inclusions in controlling HSLA steel weld microstructure’, Weld. J., 1986, 65, 139–149.
12.
DebRoyT. and DavidS. A.: ‘Physical processes in fusion welding’, Rev. Mod. Phys., 1995, 67, 85–112. doi: 10.1103/RevModPhys.67.85
13.
RicksR. A., HowellP. R. and BarritteG. S.: ‘The nature of acicular ferrite in HSLA steel weld metals’, J. Mater. Sci., 1982, 17, 732–740. doi: 10.1007/BF00540369
14.
BramfittB. L.: ‘The effect of carbide and nitride additions on the heterogeneous nucleation behavior of liquid iron’, Metall. Trans., 1970, 1, 1987–1995. doi: 10.1007/BF02642799
15.
ZhangS., HattoriN., EnomotoM. and TaruiT.: ‘Ferrite nucleation at ceramic/austenite interfaces’, ISIJ Int., 1996, 36, 1301–1309. doi: 10.2355/isijinternational.36.1301
16.
BrooksbankD. and AndrewsK. W.: ‘Stress fields around inclusions and their relation to mechanical properties’, J. Iron Steel Inst., 1972, 210, 246–255.
17.
DevillersL.: Proc. of Int. Conf. on Effect of Residual, Impurity and Microalloying Elements on Weldability and Weld Properties, Welding Inst., London,1983, Paper 1.
18.
KosekiT.: ‘A review on inclusion-assisted microstructure control in C–Mn and low-alloy steel welds’, Weld. World, 2005, 49, 22–28. doi: 10.1007/BF03263406
19.
MabuchiH., UemoriR. and FujiokaM.: ‘The role of Mn depletion in intra-granular ferrite transformation in the heat affected zone of welded joints with large heat input in structural steels’, ISIJ Int., 1996, 36, 1406–1412. doi: 10.2355/isijinternational.36.1406
20.
ChoY. W., ByunJ. S. and ShimJ. H.: ‘Effect of Ti addition on mixed microstructure of allotriomorphic and Bainitic ferrite in wrought C–Mn steels’, Mater. Sci. Forum, 2003, 426–432, 1511–1516. doi: 10.4028/www.scientific.net/MSF.426-432.1511
21.
FarrarR. A.: ‘The role of inclusions in the ductile fracture of weld metals’, Weld. Met. Fabr., 1976, 44, 578–581.
22.
ParkS. C., LeeY. J., YiH. J., YuG. B. and KangS. S.: ‘Effect of nonmetallic inclusions on cold crack susceptibility of armor casting steel weld metal’, Int. J. Precision Eng. Manuf., 2013, 14, 2137–2142. doi: 10.1007/s12541-013-0289-2
23.
SavageW. F., NippesE. F. and SzekeresE. S.: Weld. J., 1976, 55, 276–284.
24.
LeeH. W., KangS. W. and UmD. S.: ‘A study on transverse weld cracks in thick steel plate with the FCAW process’, Weld. J., 1998, 77, 503–510.
25.
‘Standard specification for structural steel for ships’, ASTM A131/A131M-14, 2014, Philadelphia, ASTM.
26.
‘Standard methods for determination of the diffusible hydrogen content of martensitic, Bainitic, and ferritic steel weld metal produced by arc welding’, AWS A 4.3-93, 1993, Miami, American Welding Society.
27.
‘Destructive tests on welds in metallic materials—cold cracking tests for weldments—arc welding processes’, part 2. ‘Self-restraint tests’, ISO 17642-2:2005.
28.
LeeM. J., ChoK. M. and KangN. H.: ‘Effect of martensite on cold cracking in 600-MPa grade flux-cored arc weld metals using the Y-groove test’, Weld. World, 2015, 59, 647–654. doi: 10.1007/s40194-015-0240-5
29.
KangJ. Y., KimD. H., BaikS. I., AhnT. H., KimY. W., HanH. H., OhK. H., LeeH. C. and HanS. H.: ‘Phase analysis of steels by grain-averaged EBSD functions’, ISIJ Int., 2011, 51, 130–136. doi: 10.2355/isijinternational.51.130
30.
‘Standard test method for Vickers hardness of metallic materials’, E92, 2003, Philadelphia, ASTM.
31.
Messler,W. Robert,Jr.: ‘Principles of welding; processes, physics, chemistry and metallurgy’, 2008, New York, John Wiley & Sons.
32.
KraussG.: ‘Principles of heat treatment of steel’, 1st edn, 1980, Ohio City, OH, ASM.
33.
ParkY. D., MaroefI. S., LandauA. and OlsonD. L.: ‘Retained austenite as a hydrogen trap in steel welds’, Weld. J., 2002, 81, 27–35.
34.
Bose-FilhoW. W., CarvalhoA. L. M. and StrangwoodM.: ‘Effects of alloying elements on the microstructure and inclusion formation in HSLA multipass welds’, Mater. Charac., 2007, 58, 29–39. doi: 10.1016/j.matchar.2006.03.004
35.
GrongO., KolbeinsenL., van der EijkC. and TranellG.: ‘Microstructure control of steels through dispersoid metallurgy using novel grain refining alloys’, ISIJ Int., 2006, 46, 824–831. doi: 10.2355/isijinternational.46.824
36.
BarbaroF. J., KrauklisP. and EasterlingK. E.: ‘Formation of acicular ferrite at oxide particles in steels’, Mater. Sci. Technol., 1989, 5, 1057–1068. doi: 10.1179/mst.1989.5.11.1057
37.
N. Alam, H. Li, L. Chen, and D. Dunne: ‘Effect of hydrogen on fracture morphology of hydrogen assisted cracking in steel weldments in Advances in Fracture Research’, Proceedings of the Ninth International Conference on Fracture ICF-9,1-5 April1997, Sydney, Australia, 325–334.
38.
GedeonS. A. and EagarT. W.: ‘Assessing hydrogen-assisted cracking fracture modes in high-strength steel weldments’, Weld. J., 1990, 69, 213–220.
39.
KumarP. G. and Yu-ichiK.: ‘Review-Diffusible hydrogen in steel weldment’, Trans. JWRI, 2013, 42, 39–62.
40.
PitrunM.: Ph.D. thesis, The University of Wollongong, 2004.
41.
XianG., LeeM., LeeJ. and KangN.: ‘Effect of shield gas composition on cold cracking susceptibility of YS 600 MPa flux cored arc weld metal’, Korean J. Met. Mater., 2015, 53, 480–487. doi: 10.3365/KJMM.2015.53.7.480
42.
S. Mackenzie: ‘Overview of the mechanisms of failure in heat treated steel components’ in ‘Failure analysis of heat treated steel components’, (ed. L. C. F. Canale, R. A. Mesquita and G. E. Totten), 43–86; 2008,
ASM Int., Materials Park.
43.
McRobieD. E. and KnottJ. F.: ‘Effects of strain and strain aging on fracture toughness of C–Mn weld metal’, Mater. Sci. Technol., 1985, 1–5, 357–365. doi: 10.1179/mst.1985.1.5.357
44.
TweedJ. H. and KnottJ. F.: ‘Micromechanisms of failure in C Mn weld metals’, Acta Metallur., 1987, 35, 1401–1414. doi: 10.1016/0001-6160(87)90087-3
45.
DavidsonJ. L., LynchS. P. and MajumdarA.: Proceedings of the joint seminar: hydrogen management in steel weldments, Melbourne, Australia, 23rd October, 1996, 21–34.
46.
Bose FilhoW. W., CarvalhoA. L. M. and BowenP.: ‘Micromechanisms of cleavage fracture initiation from inclusions in ferritic welds’, Mater. Sci. Eng. A, 2007, 460–461, 436–452. doi: 10.1016/j.msea.2007.01.115
47.
GotoH., MiyazawaK. I., YamaguchiK. I., OgibayashiS. and TanakaK.: ‘Effect of cooling rate on oxide precipitation during solidification of low carbon steels’, ISIJ Int., 1994, 34, 414–419. doi: 10.2355/isijinternational.34.414
48.
LiuS. and OlsonD. L.: ‘The influence of inclusion chemical composition on weld metal microstructure’, J. Meter. Eng., 1987, 9, 237–251. doi: 10.1007/BF02834144