Influence of accelerator/sulphur and co-agent/peroxide ratios in mixed vulcanisation systems on cure characteristics,mechanical properties and heat aging resistance of vulcanised SBR

Abstract

The influence of accelerator/sulphur and co-agent/peroxide ratios on cure characteristic and vulcanisate properties in mixed vulcanisation of styrene butadiene rubber (SBR) was investigated in this work. Accelerator/sulphur ratio was investigated with three alternative sulphur curing systems, namely conventional, semi-efficient and efficient vulcanisation (EV) systems. Zinc dimethacrylate (ZDMA) was used as a co-agent to enhance the performance of peroxide and to provide ionic linkages. Ionic linkages contributed by ZDMA create bridges between two polymer chains. The ZDMA/peroxide ratio was varied from 2 to 10. The concentration of dicumyl peroxide was held fixed while the ZDMA content was varied. Cure characteristics, mechanical properties, dynamic mechanical properties and heat aging resistance were investigated in relation to the crosslink structure. Increasing the ZDMA/peroxide ratio significantly increased density of ionic linkages, especially in combination with the EV system. The combination of EV system with high ZDMA/peroxide ratio provided the highest ionic crosslink density and the lowest polysulphidic crosslink density: this enhanced the mechanical properties, the dynamic mechanical properties and the thermal stability of SBR vulcanisates.

Keywords

Mixed vulcanisation Zinc dimethacrylate Ionic linkage Mechanical properties

Get full access to this article

View all access options for this article.

References

Cowie

J. M. G.

and Arrighi

: ‘Polymers: chemistry and physics of modern materials’, 2007, New York, CRC press.

Akiba

and Hashim

A. S.

: ‘Vulcanization and crosslinking in elastomers’, Prog. Polym. Sci. , 1997, 22, 475–521. doi: 10.1016/S0079-6700(96)00015-9

Alvarez Grima

M. M.

: ‘Novel co-agents for improved properties in peroxide cure of saturated elastomers’, 2007, Twente, University of Twente.

Loan

: ‘Mechanism of peroxide vulcanization of elastomers’, Rubber Chem. Technol. , 1967, 40, 149–176. doi: 10.5254/1.3539040

Dluzneski

P. R.

: ‘Peroxide vulcanization of elastomers’, Rubber Chem. Technol. , 2001, 74, 451–492. doi: 10.5254/1.3547647

Brodsky

G. I.

: ‘Mixed peroxide-sulfur rubber curing system’, Rubber World , 1994, 5, 31–40.

E. Bevervoorde-Meilof: ‘Improving mechanical properties of EPDM rubber by mixed vulcanisation’, PhD, University of Twente, Twente, 1998.

Peng

, Liang

, Zhang

and Zhang

: ‘Reinforcement of EPDM by in situ prepared zinc dimethacrylate’, J. Appl. Polym. Sci. , 2002, 84, 1339–1345. doi: 10.1002/app.10112

Nie

, Huang

, Qu

, Zhang

, Weng

and Wu

: ‘Cure kinetics and morphology of natural rubber reinforced by the in situ polymerization of zinc dimethacrylate’, J. Appl. Polym. Sci. , 2010, 115, 99–106. doi: 10.1002/app.31045

10.

Nie

, Huang

, Liu

, Qu

, Zhang

, Weng

and Wu

: ‘Improved mechanical properties and special reinforcement mechanism of natural rubber reinforced by in situ polymerization of zinc dimethacrylate’, J. Appl. Polym. Sci. , 2010, 116, 920–928.

11.

Wei

, Lu

, Meng

and Zhang

: ‘Improved understanding of in-situ polymerization of zinc dimethacrylate: The solid bulk polymerization’, Polymer , 2012, 53, 1409–1417. doi: 10.1016/j.polymer.2012.01.056

12.

Flory

P. J.

: ‘Statistical mechanics of swelling of network structures’, J. Chem. Phys. , 1950, 18, 108–111. doi: 10.1063/1.1747424

13.

George

S. C.

, Ninan

K. N.

and Thomas

: ‘Effect of degree of crosslinking on swelling and mechanical behaviour of conventionally vulcanised styrene-butadiene rubber membranes’, Polym. Polym. Compos. , 1999, 7, 343–353.

14.

Saville

and Watson

A. A.

: ‘Structural characterization of sulfur-vulcanized rubber networks’, Rubber Chem. Technol. , 1967, 40, 100–148. doi: 10.5254/1.3539039

15.

Tawney

, Wenisch

, Van Der Burg

and Relyea

: ‘Vulcanization with maleimides’, J. Appl. Polym. Sci. , 1964, 8, 2281–2298. doi: 10.1002/app.1964.070080524

16.

Grima

M. A.

, Talma

A. G.

, Datta

R. N.

and Noordermeer

J. W. M.

: ‘New concept of co-agents for scorch delay and property improvement in peroxide vulcanization’, Rubber Chem. Technol. , 2006, 79, 694–711. doi: 10.5254/1.3547961

17.

Coran

: ‘7 vulcanization’, Sci. Technol. Rubber , 1994, 339–385. doi: 10.1016/B978-0-08-051667-7.50012-3

18.

Ghosh

, Katare

, Patkar

, Caruthers

J. M.

, Venkatasubramanian

and Walker

K. A.

: ‘Sulfur vulcanization of natural rubber for benzothiazole accelerated formulations: from reaction mechanisms to a rational kinetic model’, Rubber Chem. Technol. , 2003, 76, 592–693. doi: 10.5254/1.3547762

19.

Fujio

, Kitayama

, Kataoka

and Anzai

: ‘Effects of sulfur on the peroxide cure of EPDM and divinylbenzene compounds’, Rubber Chem. Technol. , 1979, 52, 74–83. doi: 10.5254/1.3535209

20.

Das

and Banerjee

: ‘Studies on dicumyl peroxide vulcanization of styrene-butadiene rubber in presence of sulfur and 2-mercaptobenzothiazole’, Rubber Chem. Technol. , 1974, 47, 266–281. doi: 10.5254/1.3540436

21.

Dijkhuis

K. A. J.

, Noordermeer

J. W. M.

and Dierkes

W. K.

: ‘The relationship between crosslink system, network structure and material properties of carbon black reinforced EPDM’, Eur. Polym. J. , 2009, 45, 3302–3312. doi: 10.1016/j.eurpolymj.2009.06.029

22.

Fan

R. L.

, Zhang

, Li

, Zhang

Y. X.

, Sun

and Fan

Y. Z.

: ‘Effect of high-temperature curing on the crosslink structures and dynamic mechanical properties of gum and N330-filled natural rubber vulcanizates’, Polym. Test. , 2001, 20, 925–936. doi: 10.1016/S0142-9418(01)00035-6

23.

Kovacic

and Hein

R. W.

: ‘Cross-linking of unsaturated polymers with dimaleimides’, J. Am. Chem. Soc. , 1959, 81, 1190–1194. doi: 10.1021/ja01514a044

24.

Coran

A. Y.

: ‘Chemistry of the vulcanization and protection of elastomers: a review of the achievements’, J. Appl. Polym. Sci. , 2003, 87, 24–30. doi: 10.1002/app.11659

25.

Cooper

: ‘Copolymers of butadiene and unsaturated acids: crosslinking by metal oxides’, J. Polym. Sci. , 1958, 28, 195–206. doi: 10.1002/pol.1958.1202811618

26.

Hagen

, Salmén

and Stenberg

: ‘Effects of the type of crosslink on viscoelastic properties of natural rubber’, J. Polym. Sci. Part B: Polym. Phys. , 1996, 34, 1997–2006. doi: 10.1002/(SICI)1099-0488(19960915)34:12<1997::AID-POLB5>3.0.CO;2-N

27.

Morrison

and Porter

: ‘Temperature effects on the stability of intermediates and crosslinks in sulfur vulcanization’, Rubber Chem. Technol. , 1984, 57, 63–85. doi: 10.5254/1.3536002

28.

Chen

C. H.

, Koenig

J. L.

, Shelton

J. R.

and Collins

E. A.

: ‘Characterization of the reversion process in accelerated sulfur curing of natural rubber’, Rubber Chem. Technol. , 1981, 54, 734–750. doi: 10.5254/1.3535831

29.

Blackman

E. J.

and McCall

E. B.

: ‘Relationships between the structures of natural rubber vulcanizates and their thermal and oxidative aging’, Rubber Chem. Technol. , 1970, 43, 651–663. doi: 10.5254/1.3547279