The combined effect of resistance spot welding and precipitation hardening on the localised corrosion of A286 superalloy is studied. The specimens tested by double loop electrochemical potentiokinetic reactivation were welded in the solution treated condition, and then subjected to different precipitation hardening treatments. For both base metal and weld nugget, the maximum localised corrosion is reached when η phase is clearly observable. The fact that the localised corrosion resistance of weld nugget is different from that shown by base metal may be explained by the segregation of Ni and Ti towards the interdendritic region of weld nugget (studied by using scanning electron microscope/energy dispersive X-ray analysis).
MustafaAHHashmiMSYilbasBSInvestigation into thermal stresses in gas turbine transition-piece: influence of material properties on stress levels. J Mater Process Technol. 2008; 201: 369–373.
2.
MouritzAP.Introduction to aerospace materials. Cambridge: Woodhead; 2012.
3.
Narayana RaoM.High performance stainless steels for critical engineering applications. Trans Indian Inst Met. 2010; 63: 321–330.
4.
SavoieMEsnoufCFournierLInfluence of ageing heat treatment on alloy A-286 microstructure and stress corrosion cracking behaviour in PWR primary water. J Nucl Mater. 2007; 360: 222–230.
5.
FournierLSavoieMDelafosseD.Influence of localized deformation on A-286 austenitic stainless steel stress corrosion cracking in PWR primary water. J Nucl Mater. 2007; 366: 187–197.
6.
KrishnaSCGangwarNKJhaAKOn the direct aging of iron based superalloy hot rolled plates. Mater Sci Eng A. 2015; 648: 274–279.
7.
SinghalLKMartinJW.The mechanism of tensile yield in an age-hardened steel containing γ′ (ordered Ni3Ti) precipitates. Acta Metall. 1968; 16: 947–953.
8.
ThompsonAWBrooksJA.The mechanism of precipitation strengthening in an iron-base superalloy. Acta Metall. 1982; 30: 2197–2203.
9.
ZhangPZhuQHuCCyclic deformation behavior of a nickel-base superalloy under fatigue loading. Mater Des. 2015; 69: 12–21.
10.
ZhaoMJGuoZFLiangHEffect of boron on the microstructure, mechanical properties and hydrogen performance in a modified A286. Mater Sci Eng A. 2010; 527: 5844–5851. doi:10.1016/j.msea.2010.05.070.
11.
SeifollahiMRazaviSHKheirandishSThe mechanism of η phase precipitation in A286 superalloy during heat treatment. J Mater Eng Perform. 2013; 22: 3063–3069.
12.
LiXZhangJRongLCellular η phase precipitation and its effect on the tensile properties in an Fe-Ni-Cr alloy. Mater Sci Eng A. 2008; 488: 547–553.
13.
BarlowCYRalphB.Observations of cellular transformation products in nickel-base superalloys. J Mater Sci. 1979; 14: 2500–2508.
14.
De CiccoHLuppoMIGribaudoLMMicrostructural development and creep behavior in A286 superalloy. Mater Charact. 2004; 52: 85–92.
15.
BrooksJAThompsonAW.Microstructure and hydrogen effects on fracture in the alloy A-286. Metall Trans A. 1993; 24: 1983–1991.
16.
GuoZLiangHZhaoMEffect of boron addition on hydrogen embrittlement sensitivity in Fe-Ni based alloys. Mater Sci Eng A. 2010; 527: 6620–6625.
17.
RhoBSNamSWXieX.The effect of test temperature on the intergranular cracking of Nb-A286 alloy in low cycle fatigue. J Mater Sci. 2002; 37: 203–209.
18.
ChenSZhaoMRongL.Effect of Ti content on the microstructure and mechanical properties of electron beam welds in Fe-Ni based alloys. Mater Sci Eng A. 2013; 571: 33–37.
19.
MartínÓDe TiedraPSan-JuanM.Combined effect of resistance spot welding and precipitation hardening on tensile shear load bearing capacity of A286 superalloy. Mater Sci Eng A. 2017; 688: 309–314.
20.
ASM International Handbook Committee. Welding. In: DaviesJr, editor. ASM spec. handbook. stainl. steels. Materials Park, OH: ASM International; 1994. p. 340–401.
21.
BrooksJAKrenzerRW.Progress toward a more weldable A-286. Weld J1974; 53: 242S–245S.
22.
ShinozakiK.Welding and joining Fe and Ni-base superalloys. Weld Int. 2001; 15: 593–610.
23.
MartínOLópezMMartínF.Redes neuronales artificiales para la predicción de la calidad en soldadura por resistencia por puntos. Rev Metal. 2006; 42: 345–353.
24.
EftekharimilaniPvan der AaEMHermansMJMMicrostructural characterisation of double pulse resistance spot welded advanced high strength steel. Sci Technol Weld Join. 2017; 22: 545–554.
25.
MartínÓLópezMDe TiedraPPrediction of magnetic interference from resistance spot welding processes on implantable cardioverter-defibrillators. J Mater Process Technol. 2008; 206: 256–262.
26.
MartínÓPeredaMSantosJIAssessment of resistance spot welding quality based on ultrasonic testing and tree-based techniques. J Mater Process Technol. 2014; 214: 2478–2487.
27.
KianersiDMostafaeiAMohammadiJ.Effect of welding current and time on the microstructure, mechanical characterizations, and fracture studies of resistance spot welding joints of AISI 316L austenitic stainless steel. Metall Mater Trans A Phys Metall Mater Sci. 2014; 45: 4423–4442.
28.
PouranvariMAlizadeh-ShMMarashiSPH.Welding metallurgy of stainless steels during resistance spot welding part I: fusion zone. Sci Technol Weld Join. 2015; 20: 502–511.
De TiedraPMartínÓSan-JuanM.Potentiodynamic study of the influence of gamma prime and eta phases on pitting corrosion of A286 superalloy. J Alloys Compd. 2016; 673: 231–236.
31.
MartínÓDe TiedraPSan-JuanM.Study of influence of gamma prime and eta phases on corrosion behaviour of A286 superalloy by using electrochemical potentiokinetic techniques. Mater Des. 2015; 87: 266–271.
32.
AhedoVMartínÓSantosJI. Independence of EPR and PAP tests performed on resistance spot welding joints. Corros Eng Sci Technol. 2017; 52: 418–424.
ProhaskaMKanduthHMoriGOn the substitution of conventional corrosion tests by an electrochemical potentiokinetic reactivation test. Corros Sci. 2010; 52: 1582–1592.
35.
De TiedraPMartínÓLópezM.Combined effect of resistance spot welding and post-welding sensitization on the degree of sensitization of AISI 304 stainless steel. Corros Sci. 2011; 53: 2670–2675.
36.
GarciaCde TiedraMPBlancoYIntergranular corrosion of welded joints of austenitic stainless steels studied by using an electrochemical minicell. Corros Sci. 2008; 50: 2390–2397.
37.
KumarSShahiAS.Studies on metallurgical and impact toughness behavior of variably sensitized weld metal and heat affected zone of AISI 304L welds. Mater Des. 2016; 89: 399–412.
38.
GarcíaCMartínFBlancoYCorrosion behaviour of duplex stainless steels sintered in nitrogen. Corros Sci. 2009; 51: 76–86.
39.
GarcíaCMartínFde TiedraPElectrochemical reactivation methods applied to PM austenitic stainless steels sintered in nitrogen–hydrogen atmosphere. Corros Sci. 2008; 50: 687–697.
40.
ASTM E407-07e1. Standard Practice for Microetching Metals and Alloys. West Conshohocken, PA: ASTM International; 2007. doi:10.1520/E0407-07E01.
41.
McCauleyRBBennettMPBodaryWD. Resistance spot welding. In: LymanT, editor. Welding and Brazing (Metals Handbook). 8th ed. Vol. 6. Metals Park (OH): American Society for Metals; 1971. p. 401–424.
42.
AslanlarS.The effect of nucleus size on mechanical properties in electrical resistance spot welding of sheets used in automotive industry. Mater Des. 2006; 27: 125–131.
43.
BoseADePK.An EPR study on the influence of prior cold work on the degree of sensitization of AISI 304 stainless steel. CORROSION. 1987; 43: 624–631.
44.
ReclaruLLerfREschlerPYCorrosion behavior of a welded stainless-steel orthopedic implant. Biomaterials. 2001; 22: 269–279.
45.
Alizadeh-ShMPouranvariMMarashiSPH.Welding metallurgy of stainless steels during resistance spot welding part II – heat affected zone and mechanical performance. Sci Technol Weld Join. 2015; 20: 512–521.
46.
Čı´halVŠtefecR.On the development of the electrochemical potentiokinetic method. Electrochim Acta. 2001; 46: 3867–3877.
47.
ShingledeckerJPEvansNDPharrGM.Influences of composition and grain size on creep-rupture behavior of inconel® alloy 740. Mater Sci Eng A. 2013; 578: 277–286.
48.
ZhongZGuYYuanY.Microstructural stability and mechanical properties of a newly developed Ni-Fe-base superalloy. Mater Sci Eng A. 2015; 622: 101–107.
49.
ZhaoJ-CRavikumarVBeltranAM.Phase precipitation and phase stability in nimonic 263. Metall Mater Trans A. 2001; 32A: 1271–1282.
50.
ZhaoSXieXSmithGDResearch and improvement on structure stability and corrosion resistance of nickel-base superalloy INCONEL alloy 740. Mater Des. 2006; 27: 1120–1127.
51.
YanYYanYHeYThe mechanism of precipitation strengthening in Fe–Ni austenitic alloy electron beam weldment. Mater Sci Eng A. 2015; 630: 85–89.