Oxidation behaviour of an austenitic steel HR3C at 620∼650°C for 1000 h in steam with two different levels of dissolved oxygen (DO), 20 ppb and 5 ppm, was investigated by gravimetry, X-ray diffraction and scanning electron microscopy. Results showed that mainly a single-layered (Cr, Mn)2O3 scale was developed. The oxide growth followed near-power kinetics and was accelerated with DO concentration and exposure temperature. At the higher DO concentration, the formation of (Cr, Mn)2O3 with a much smaller size was favoured. Besides, the oxide scale became undulated and interfacial voids formed. Higher exposure temperature resulted in the growth of the (Cr, Mn)2O3 crystals and the change of their morphology from acicular to granular. Fe3O4 nodules and Ni-Cr spinel occurred at 650°C/5 ppm DO. Related oxidation mechanisms were discussed.
KritzerP.Corrosion in high-temperature and supercritical water and aqueous solutions: a review. J Supercrit Fluids. 2004; 29 (1-2): 1–29. doi: 10.1016/S0896-8446(03)00031-7
2.
BursikADooleyRB.Organics: a retrospective look at fossil plant cycle chemistry and the possible requirements for the future. Power Plant Chem. 2005; 7 (10): 593–598.
3.
DooleyRBShieldsKJShulderSJ.Flow-accelerated corrosion (FAC) in conventional fossil units: cycle chemistry influences and management approach. Power Plant Chem. 2009; 11 (6): 352–361.
DooleyRB.Flow-accelerated corrosion in fossil and combined cycle/HRSG plants. Power Plant Chem. 2008; 10 (2): 68–86.
6.
JiangDXuHDengB. Effect of oxygenated treatment on corrosion of the whole steam-water system in supercritical power plant. Appl Therm Eng. 2016; 93: 1248–1253. doi: 10.1016/j.applthermaleng.2015.10.098
7.
DooleyRBBursikA.Oxide growth and exfoliation of materials in steam tubing. Power Plant Chem. 2011; 13 (4): 236–240.
8.
ChenYSridharanKAllenT.Corrosion behavior of ferritic-martensitic steel T91 in supercritical water. Corros Sci. 2006; 48 (9): 2843–2854. doi: 10.1016/j.corsci.2005.08.021
9.
AmpornratPWasGS.Oxidation of ferritic-martensitic alloys T91, HCM12A and HT-9 in supercritical water. J Nucl Mater. 2007; 371 (1-3): 1–17. doi: 10.1016/j.jnucmat.2007.05.023
10.
ZhangNQXuHLiBR. Influence of the dissolved oxygen content on corrosion of the ferritic-martensitic steel P92 in supercritical water. Corros Sci. 2012; 56: 123–128. doi: 10.1016/j.corsci.2011.11.013
11.
ZhangNQZhuZLZhangQ. Corrosion in supercritical water with different dissolved oxygen content. Proc. NACE corrosion Conf. Expo.; FL, March 2013, NACE International, Paper 2318 .
12.
WasGSAllenTR.Time, temperature, and dissolved oxygen dependence of oxidation of austenitic and ferritic-martensitic alloys in supercritical water. Pro. Conf. on Advances in Nuclear power plants; Seoul, Korea, May 2005, American Nuclear Society, Paper 5690 .
13.
ZhuZXuHJiangD. The role of dissolved oxygen in supercritical water in the oxidation of ferritic-martensitic steel. J Supercrit Fluids. 2016; 108 (1): 56–60. doi: 10.1016/j.supflu.2015.10.017
14.
WasGSAmpornratPGuptaG. Corrosion and stress corrosion cracking in supercritical water. J Nucl Mater. 2007; 371 (1-3): 176–201. doi: 10.1016/j.jnucmat.2007.05.017
15.
YangZLuJTZhaoXB. Study on the oxidation behaviour of HR3C in air and pure steam at 750°C. J Chinese Soc Power Eng (China). 2014; 35 (10): 859–864.
16.
FonticellaR.The usefulness of the R2 statistic, Proc. Conf. Casualty Actuarial Society Forum, Maryland, 1998, Paper 55.
17.
HanselMGarciafresnilloLTobingSL. Effect of H 2/H 2O ratio on thermally grown chromia scales formed on Ni25Cr alloy in Ar-H 2-H 2O atmospheres at 1000°C. Mater High Temp. 2012; 29 (3): 187–192. doi: 10.3184/096034012X13322698137785
18.
BambaGWoutersYGalerieA. Inverse growth transport in thermal chromia scales on Fe-15Cr steels in oxygen and in water vapour and its effect on scale adhesion. Scr Mater. 2007; 57 (8): 671–674. doi: 10.1016/j.scriptamat.2007.06.050
19.
YangZLuJTYangZ. Oxidation behavior of a new wrought Ni-30Fe-20Cr based alloy at 750°C in pure steam and the effects of alloyed yttrium. Corros Sci. 2017; 125: 106–113. doi: 10.1016/j.corsci.2017.06.009
20.
ZurekJYoungDJEssumanE. Growth and adherence of chromia based surface scales on Ni-base alloys in high- and low-pO 2 gases. Mater Sci Eng A. 2008; 477 (1-2): 259–270. doi: 10.1016/j.msea.2007.05.035
21.
KofstadP.High temperature corrosion. London and New York: Elsevier Applied Science; 1988.
22.
JiangQZhangSHLiJC.Grain size-dependent diffusion activation energy in nanomaterials. Solid State Commun. 2004; 130 (9): 581–584. doi: 10.1016/j.ssc.2004.03.033
23.
WurschumRHerthSBrossmannU.Diffusion in nanocrystalline metals and alloys – a status report. Adv Eng Mater. 2003; 5 (5): 365–372. doi: 10.1002/adem.200310079
24.
WangZBTaoNRTongWP. Diffusion of chromium in nanocrystalline iron produced by means of surface mechanical attrition treatment. Acta Mater. 2003; 51 (14): 4319–4329. doi: 10.1016/S1359-6454(03)00260-X
25.
OudrissACreusJBouhattateJ. Grain size and grain-boundary effects on diffusion and trapping of hydrogen in pure nickel. Acta Mater. 2012; 60 (19): 6814–6828. doi: 10.1016/j.actamat.2012.09.004
26.
TanLYangYAllenTR.Oxidation behavior of iron-based alloy HCM12A exposed in supercritical water. Corros Sci. 2006; 48 (10): 3123–3138. doi: 10.1016/j.corsci.2005.10.010
27.
WagnerC.Reaktionstypen bei der Oxydation von Legierungen. Zeitschrift für Elektrochemie, Berichte der Bunsengesellschaft für physikalische Chemie. 1959; 63 (7): 772–782.
28.
YoungDJ.High temperature oxidation and corrosion of metals. Amsterdam: Elsevier; 2008.
29.
KuangWWuXHanEH.Influence of dissolved oxygen concentration on the oxide film formed on 304 stainless steel in high temperature water. Corros Sci. 2012; 63: 259–266. doi: 10.1016/j.corsci.2012.06.007
30.
DaviesHDinsdaleA.Theoretical study of steam grown oxides as a function of temperature, pressure and p(O 2). Mater High Temp. 2005; 22 (1-2): 15–25. doi: 10.1179/mht.2005.003
31.
BarinI.Thermochemical data of pure substances. Weinheim: VCH Verlagsgesellschaft mbH; 2003.