The corrosion of steels in clay soils is of interest for buried steel infrastructure. To obtain better information about the early corrosion effects, mild steel coupons were exposed for 3, 6 and 13 months in finely graded clay soil at different moisture contents and with different degrees of compression to simulate compaction. It was found that the maximum corrosion mass loss and pit depths occurred at a soil moisture content of 17-18 wt-% for all exposures and levels of compaction, corresponding to around 0.65 degree of saturation. These values are broadly consistent with earlier findings for non-clay soils. For exposures of 3 months corrosion was predominantly localised but subsequently became more uniform. This was shown to be consistent with good compaction of the soil against the steel surface. Poorly compacted lumpy clays, however, showed larger areas of localised corrosion and relatively greater corrosion mass loss and deeper pitting.
MelchersRE.The effect of corrosion on the structural reliability of steel offshore structures. Corros Sci. 2005; 47 (10): 2391–2410. doi: 10.1016/j.corsci.2005.04.004
2.
NicholasDMooreG.Corrosion of ferrous watermains: past performance and future prediction – a review. Corros Mater. 2009; 34 (2): 33–40.
3.
RomanoffM.Underground Corrosion, National Bureau of Standards Circular 579, US Government Printing Office (Publishers), Washington, DC; 1957.
4.
TomashovND.Theory of corrosion and protection of metals: the science of corrosion. New York: Macmillan (Publishers); 1966.
5.
RobergePR.Corrosion engineering principles and practice. New York: Mc-Graw-Hill (Publishers); 2008.
6.
JackTRWilmottMJ.Corrosion by soils. In: RevieRW, editor. Uhlig's corrosion handbook. 3rd ed.New York: John Wiley; 2011. p. 333–349.
7.
SchwerdtfegerWJ.Soil resistivity as related to underground corrosion and cathodic protection. J. Res National Bureau Standards C Eng Construct. 1965; 69C (1): 71–77. doi: 10.6028/jres.069C.012
8.
ColeISMarneyD.The science of pipe corrosion: a review of the literature on the corrosion of ferrous metals in soils. Corros Sci. 2012; 56: 5–16. doi: 10.1016/j.corsci.2011.12.001
9.
MelchersREWellsT.Correlation between soil electrical resistivity, polarization resistance and corrosion of steel. Corros Eng Sci Technol.2018; 53 (7): 524–530. doi:10.1080/1478422X.2018.1511325.
10.
MelchersREPetersenRB.A reinterpretation of the Romanoff NBS data for corrosion of steels in soils. Corros Eng Sci Technol. 2018; 53 (2): 131–140. doi:10.1080/1478422X.2017.1417072.
11.
GuptaSKGuptaBK.The critical soil moisture content in the underground corrosion of mild steel. Corros Sci. 1979; 19: 171–178. doi: 10.1016/0010-938X(79)90015-5
12.
NoorEAAl-MoubarakiAH.Influence of soil moisture content on the corrosion behavior of X60 steel in different soils. Arab J Sci Eng. 2014; 39: 5421–5435. doi: 10.1007/s13369-014-1135-2
13.
AkkoucheRRémazeillesCJeanninMInfluence of soil moisture on the corrosion processes of carbon steel in artificial soil: active area and differential aeration cells. Electrochim Acta. 2016; 213: 698–708. doi: 10.1016/j.electacta.2016.07.163
14.
MelchersREPetersenRBWellsT.The effect of atmospheric precipitation on the corrosion of ferrous metals buried in soils. Corros Eng Sci Technol. 2019; 54 (1): 28–36. doi:10.1080/1478422X.2018.1523291.
15.
NorinMVinkaT-G.Corrosion of carbon steel in filling material in an urban environment. Mater Corros. 2003; 54 (9): 641–651. doi: 10.1002/maco.200303680
16.
Al-JudaibiAAl-MoubarakiA.Microbial analysis and surface characterization of SABIC carbon steel corrosion in soils of different moisture levels. Adv Biol Chem. 2013; 3 (3): 264–273. doi: 10.4236/abc.2013.32030
17.
PoursaeeAHanssonCM.Potential pitfalls in assessing chloride-induced corrosion of steel in concrete. Cem Concr Res. 2009; 39: 391–400. doi: 10.1016/j.cemconres.2009.01.015
18.
StockertLHaasMJeffreyRJElectrochemical measurements and short-term-in-situ exposure testing). Proc. ACA conference, corrosion & prevention 2012; 11-14 November ; Melbourne ; 2012. CD ROM, Paper No. 100.
19.
ASTM International. Standard practice for preparing, cleaning and evaluating corrosion test specimens). ASTM G1-03, ASTM International; West Conshohocken, PA ; 2011.
20.
ASTM International. Standard practice for conducting and evaluating laboratory corrosion tests in soils). ASTM G162-99, ASTM International; West Conshohocken, PA ; 2010.
21.
Standards Australia. Soil moisture content tests – Determination of the moisture content of a soil – Oven drying method (standard method), AS 1289.2.1.1-2005. Standards Australia, NSW; 2005.
22.
Standards Australia. Methods of testing soils for engineering purposes – Soil classification tests – Determination of the particle size distribution of a soil – Standard method of fine analysis using a hydrometer, AS 1289.3.6.3-2003. Standards Australia, NSW; 2003.
23.
Standards Australia. Methods of testing soils for engineering purposes. Method 5.1.1: Soil compaction and density tests – Determination of the dry density/moisture content relation of a soil using standard compactive effort.
24.
PetersenRBMelchersRE.Bi-modal trending for corrosion loss of steels buried in soils. Corros Sci. 2018; 137: 194–203. doi: 10.1016/j.corsci.2018.03.048
25.
MelchersRE.Pitting corrosion of mild steel in Marine immersion Environment—part 1: maximum pit depth. Corrosion. 2004; 60 (9): 824–836. doi: 10.5006/1.3287863
26.
BurnsMSalleyDJ.Particle size as a factor in the corrosion of lead by soils. Ind Eng Chem. 1930; 22: 293–297. doi: 10.1021/ie50243a022
27.
KodikaraJRajeevPChanDSoil moisture monitoring at the field scale using neutron probe. Can Geotech J. 2014; 51: 332–345. doi: 10.1139/cgj-2012-0113