Corrosion of reinforcing steel embedded in kaolinite clay was studied for a two year exposure period. Electrochemical impedance spectroscopy (EIS) and potentiodynamic polarisation (POL) revealed a decrease of the corrosion rate (CR) of the steel bars up to average values of 2.5 μm y−1. X-ray photoelectron spectroscopy (XPS), and Scanning electron microscope (SEM) equipped with Energy-dispersive X-ray spectroscopy (EDX) techniques showed the formation of a thick and compacted corrosion layer composed of several iron oxides, namely, Fe2O3, Fe (OH)2, Fe3O4 and FeCO3. The external corrosion product is composed mainly of magnetite (Fe3O4) and siderite (FeCO3). EDX mapping showed a homogeneous distribution of the elements across the cross-sectional of the corrosion layer.
Pacheco-TorgalFJalaliS.Earth construction: lessons from the past for future eco–efficient construction. Constr Build Mater. 2012; 29: 512–519. doi: 10.1016/j.conbuildmat.2011.10.054
2.
AlamINaseerAShahAA.Economical stabilization of clay for earth buildings construction in rainy and flood prone areas. Constr Build Mater. 2015; 77: 154–159. doi: 10.1016/j.conbuildmat.2014.12.046
3.
ZamiMSLeeA.Economic benefits of contemporary earth construction in low-cost urban housing – state-of-the-art review. J Build Appraisal. 2010; 5: 259–2710. doi: 10.1057/jba.2009.32
4.
PerrotARangeardDLevigneurA.Linking rheological and geotechnical properties of kaolinite materials for earthen construction. Mater Struct. 2016; 49: 4647–4655. doi: 10.1617/s11527-016-0813-9
5.
PerrotARangeardDMenasriaF. Strategies for optimizing the mechanical strengths of raw earth-based mortars. Constr Build Mater. 2018; 167: 496–504. doi: 10.1016/j.conbuildmat.2018.02.055
6.
NeffDDillmannPDescostesM. Corrosion of iron archaeological artefacts in soil: estimation of the average corrosion rates involving analytical techniques and thermodynamic calculations. Corros Sci. 2006; 48: 2947–2970. doi: 10.1016/j.corsci.2005.11.013
7.
SahebMNeffDDillmannP. Long-term corrosion behaviour of low-carbon steel in anoxic environment: characterisation of archaeological artefacts. J Nucl Mater. 2008; 379: 118–123. doi: 10.1016/j.jnucmat.2008.06.019
8.
MichelinADrouetEFoyE. Investigation at the nanometre scale on the corrosion mechanisms of archaeological ferrous artefacts by STXM. J Anal At Spectrom. 2013; 28: 59–66. doi: 10.1039/C2JA30250K
9.
NeffDReguerSBellot-GurletL. Structural characterization of corrosion products on archaeological iron: an integrated analytical approach to establish corrosion forms. J Raman Spectrosc. 2004; 35: 739–745. doi: 10.1002/jrs.1130
10.
JeanninMCalonnecDSabotR. Role of a clay sediment deposit on the corrosion of carbon steel in 0.5 mol L-1 NaCl solutions. Corros Sci. 2010; 52: 2026–2034. doi: 10.1016/j.corsci.2010.02.033
11.
El MendiliYAbdelouasABardeauJF.Corrosion of P235GH carbon steel in simulated bure soil solution. J Mater Environ Sci. 2013; 4: 786–791.
12.
ANDRA. 2005. Argiles. Tome 3: Corrosion des matériaux métalliques. Rapport Andra C.RP.ASCM.04.015/A.2005c, 363 pages.
13.
LantenoisSLansonBMullerF. Experimental study of smectite interaction with metal Fe at low temperature: 1. Smectite destabilization. Clays Clay Miner. 2005; 53: 597–612. doi: 10.1346/CCMN.2005.0530606
14.
PerronnetM.Réactivité des matériaux argileux dans un contexte de corrosion métallique, application au stockage des déchets radioactifs en site argileux. PhD Thesis. Institut National Polytechnique de Lorraine, NancyFrance; 2004.
15.
MatthiesenHHilbertLRGregoryDJ.Siderite as a corrosion product on archaeological iron from a Waterlogged environment. Studies in Conserv. 2003; 48: 183–194. doi: 10.1179/sic.2003.48.3.183
16.
JeanninMCalonnecDSabotR. Role of a clay sediment deposit on the passivity of carbon steel in 0,1 mol.dm-3 NaHCO3 solutions. Electrochim Acta. 2011; 56: 1466–1475. doi: 10.1016/j.electacta.2010.10.063
17.
MartinFBataillonCSchlegelM.Corrosion of iron and low-alloyed steel within a water saturated brick of clay under anaerobic deep geological disposal conditions: an integrated experiment. J Nucl Mater. 2008; 379: 80–90. doi: 10.1016/j.jnucmat.2008.06.021
18.
GallianoFGerwinWMenzelK.In Metal 98 conference on metals conservation, Draguignan- Figaniéres, Mourey W, Robbiola (eds). James and James. France. 1998, pp. 87-91.
19.
FoctFCabreraJDridiW. Corrosion behaviour of carbon steel in the Tournemire clay. Eurocorr 2004, proceedings of the 2nd International workshop: Prediction of long term corrosion behaviour in nuclear waste systems, September, Nice, France, 2004. 10 pages.
Aciers pour béton armé soudables en barre a verrous, edition. 2014; 10:1-6.
22.
BroomfieldJP.Corrosion of steel in concrete: understanding, investigation and repair. London. UK: E&FN Spon. 1997: 5–45.
23.
CostaDMarcusPYangWP.Resistance to pitting and chemical composition of passive films of a Fe-17%Cr alloy in chloride-containing acid solution. J Electrochem Soc. 1994; 141: 2669–2676. doi: 10.1149/1.2059166
24.
MontemorMFSimoesAMPFerreiraMGS.Chloride-induced corrosion on reinforcing steel: from the fundamentals to the monitoring techniques. Cement Concrete Comp. 2003; 25: 491–502. doi: 10.1016/S0958-9465(02)00089-6
25.
AgarwalPOrazemMEGarcia-RubioLH.Measurement models for electrochemical impedance spectroscopy I. Demonstration of applicability. J Electrochem Soc. 1992; 139: 1917–1927. doi: 10.1149/1.2069522
26.
FrateurIDeslouisCOrazemME. Modeling of the cast iron/drinking water system by electrochemical impedance spectroscopy. Electrochim Acta. 1999; 44: 4345–4356. doi: 10.1016/S0013-4686(99)00150-4
27.
DiazBJoiretSKeddamM. Passivity of iron in red mud's water solutions. Electrochim Acta. 2004; 49: 30–39. doi: 10.1016/j.electacta.2004.01.063
28.
DouWLiuJCaiW. Electrochemical investigation of increased carbon steel corrosion via extracellular electron transfer by a sulfate reducing bacterium under carbon source starvation. Corros Sci. 2019; 150: 258–267. doi: 10.1016/j.corsci.2019.02.005
29.
SerdarMZuljLVBjegovićD.Long-term corrosion behaviour of stainless reinforcing steel in mortar exposed to chloride environment. Corros Sci. 2013; 69: 149–157. doi: 10.1016/j.corsci.2012.11.035
30.
LiZWanHSongD. Corrosion behavior of x80 pipelinesteel in the presence of Brevibacterium halotolerans in Beijing soil. Bioelectrochemistry. 2018; 121: 18–26. doi: 10.1016/j.bioelechem.2018.01.011
31.
DeoRNBirbilisNCullJP.Measurement of corrosion in soil using the galvanostatic pulse technique. Corros Sci. 2014; 80: 339–349. doi: 10.1016/j.corsci.2013.11.058
32.
AndradeCKeddamMNovoaX. Electrochemical behaviour of steel rebars in concrete: influence of environmental factors and cement chemistry. Electrochim Acta. 2001; 46: 3905–3912. doi: 10.1016/S0013-4686(01)00678-8
33.
MorozovYCastelaADiasA. Chloride-induced corrosion behavior of reinforcing steel in spent fluid cracking catalyst modified mortars. Cem Concr Res. 2013; 47: 1–7. doi: 10.1016/j.cemconres.2013.01.011
34.
PanCGuoMHanW. Study of corrosion evolution of carbon steel exposed to an industrial atmosphere. Corros Eng Sci Technol. 2019; 54: 241–248. doi: 10.1080/1478422X.2019.1574955
35.
GabrielliCTakenoutiH.Méthodes électrochimiques appliquées à la corrosion-technique stationnaire. Technique de L'ingénieur. 2010; 33: 1–17.
36.
AkkoucheRRémazeillesCJeanninM. Influence of soil moisture on the corrosion processes of carbon steel in artificial soil: active area and differential aeration cells. Electrochim Acta. 2016; 213: 698–708. doi: 10.1016/j.electacta.2016.07.163
37.
SternMGearyAL.A theoretical analysis of the shape of polarization curves. J Electrochem Soc. 1957; 104: 33–63. doi: 10.1149/1.2428653
38.
BardAJFaulknerLR.Electrochemical methods: fundamentals and applications. 2nd ed. New York: 3.3 Butler-Volmer Model of Electrode Kinetics, John Wiley & Sons; 2001. p. 92–98.
39.
ASTM. Standard Practice for calculation of corrosion rates and related information from electrochemical measurements, G102-89, ASTM International. West Conshohocken, USA, 2004.
40.
BarbalatMLanardeLCaronD. Electrochemical study of the corrosion rate of carbon steel in soil: evolution with time and determination of residual corrosion rates under cathodic protection. Corros Sci. 2012; 55: 246–253. doi: 10.1016/j.corsci.2011.10.031
41.
El-ShamyAMShehataMFIsmailAIM.Effect of moisture contents of bentonitic clay on the corrosion behavior of steel pipelines. Appl Clay Sci. 2015; 114: 461–466. doi: 10.1016/j.clay.2015.06.041
42.
AndradeCAlonsoCGulikersJ. Test methods for on-site corrosion rate measurement of steel reinforcement in concrete by means of the polarization resistance method. Mater Struct. 2004; 37: 623–643. doi: 10.1007/BF02483292
43.
TakasakiSYamadaY.Effects of temperature and aggressive anions on corrosion of carbon steel in portable water. Corros Sci. 2007; 49: 240–247. doi: 10.1016/j.corsci.2006.05.035
44.
LiuTMWuYHLuoSX. Effect of soil compositions on the electrochemical corrosion behavior of carbon steel in simulated soil solution. Materwiss Werksttech. 2010; 41: 228–233. doi: 10.1002/mawe.201000578
45.
El MendiliYAbdelouasAAit ChaouA. Carbon steel corrosion in clay-rich environment. Corros Sci. 2014; 88: 56–65. doi: 10.1016/j.corsci.2014.07.020
46.
MoulderJFStickleWFSobolPE. Handbook of X-ray photoelectron spectroscopy. Eden Prairie (MN): Perkin-Elmer Corp; 1992.
47.
BiesingerMCLauLWMGersonAR. Resolving surface chemical states in XPS analysis of first row transition metals, oxides and hydroxides: Sc, Ti, V, Cu and Zn. Appl Surf Sci. 2010; 257: 887–898. doi: 10.1016/j.apsusc.2010.07.086
48.
HeuerJKStubbinsJF.An XPS characterization of FeCO3 films from CO2 corrosion. Corros Sci. 1999; 41: 1231–1243. doi: 10.1016/S0010-938X(98)00180-2
49.
KozakiTImamuraYTakadaJ. Corrosion of iron and migration of corrosion products in compacted bentonite. Mat Res Soc Symp Proc. 1995; 353: 329–336. doi: 10.1557/PROC-353-329
50.
JinSAtrensA.ESCA-Studies of the structure and composition of the passive film formed on stainless steels by various immersion times in 0,1M NaCl solution. Appl Phys A. 1987; 42: 149–165. doi: 10.1007/BF00616726
51.
SmartNRReddyBRanceAP. The anaerobic corrosion of carbon steel in saturated compacted bentonite in the Swiss repository concept. Corros Eng Sci Technol. 2017; 52: 113–126. doi: 10.1080/1478422X.2017.1316088
52.
MelchersREPetersenRBWellsT.Empirical models for long-term localized corrosion of cast iron pipes buried in soils. Corros Eng Sci Technol. 2019; 54: 587–600. doi: 10.1080/1478422X.2019.1638564
53.
PetersenRBMelchersRE.Effect of moisture content and compaction on the corrosion of mild steel buried in clay soils. Corros Eng Sci Technol. 27 June 2019. doi:10.1080/1478422X.2019.1638564. accepted for publication.