Mechanical and electrical properties of MoSi 2 –RSiC composites via a combination of phenolic resin infiltration–pyrolysis and MoSi 2 –Si–Ti alloy-activated melting infiltration composite processes
Restricted accessResearch articleFirst published online July, 2016
Mechanical and electrical properties of MoSi 2 –RSiC composites via a combination of phenolic resin infiltration–pyrolysis and MoSi 2 –Si–Ti alloy-activated melting infiltration composite processes
A three-dimensional interpenetrated network structure composite was designed and prepared via a combination of phenolic resin infiltration-pyrolysis and MoSi2–Si–Ti alloy-activated melting infiltration processes to effectively merge the desirable properties of MoSi2 and RSiC. Influence of infiltration temperature on the microstructure, mechanical and electrical properties of the composites was examined. Almost dense MoSi2–RSiC composites with the designed structure were obtained at 1900°C. Formation of the gradient interface modified the interface combination and enhanced the mechanical and electrical properties of the composite. Flexural strength of the composites reached approximately 114.262 MPa (room temperature) and 128.392 MPa (1400°C), respectively, indicating corresponding increases of 37.08 and 35.69% compared with the RSiC matrix. Volume resistivity decreased to 57.63 mΩ cm, nearly five orders of magnitude lower than that of RSiC. Influence of the interpenetrated network structure and interface combination on the electrical conductivity behaviour of the composites was discussed via a modified mixture rule.
SharifA. A.: ‘High-temperature oxidation of MoSi2’, J. Mater. Sci., 2010, 45, 865–870. doi: 10.1007/s10853-009-4012-8
2.
GaoP.-Z., ZhangX.-L., HuangS.-T., LiuJ.-X., WangW.-X. and XiaoH.-N.: ‘Influence of MoSi2 content on the microstructure and properties of MoSi2–RSiC composites’, Mater. Res. Bull., 2014, 54, 13–19. doi: 10.1016/j.materresbull.2014.03.009
3.
DasguptaT. and UmarjiA. M.: ‘Improved ductility and oxidation resistance in Nb and Al co-substituted MoSi2’, Intermetallics, 2008, 16, 739–744. doi: 10.1016/j.intermet.2008.01.006
4.
PengK., YiM., RanL. and GeY.: ‘Effect of the W addition content on valence electron structure and properties of MoSi2-based solid solution alloys’, Mater. Chem. Phys., 2011, 129, (3), 990–994. doi: 10.1016/j.matchemphys.2011.05.049
5.
ZhangH., WuH. and GuS.: ‘Preparation and properties of MoSi2 based composites reinforced by carbon nanotubes’, Ceram. Int., 2013, 39, 7401–7405. doi: 10.1016/j.ceramint.2013.02.083
6.
YanJ., ZhangH., TangS. and XuJ.: ‘Room temperature mechanical properties and high temperature oxidation behavior of MoSi2 matrix composite reinforced by adding La2O3 and Mo5Si3’, Mater. Charact., 2009, 60, 447–450. doi: 10.1016/j.matchar.2008.11.017
7.
MeierS. and HeinrichJ. G.: ‘Processing–microstructure–properties relationships of MoSi2–SiC composites’, J. Eur. Ceram. Soc., 2002, 22, 2357–2363. doi: 10.1016/S0955-2219(02)00035-3
8.
WangZ., LiS., WangM., WuG., SunX. and LiuM.: ‘Effect of SiC whiskers on microstructure and mechanical properties of the MoSi2–SiCw composites’, Int. J. Refract. Met. Hard Mater., 2013, 41, 489–494. doi: 10.1016/j.ijrmhm.2013.06.007
9.
XuJ., ChenF. and TanF.: ‘In-situ preparation of SiC–MoSi2 composite by microwave reaction sintering’, Ceram. Int., 2012, 38, 6895–6898. doi: 10.1016/j.ceramint.2012.04.072
10.
SchollR., BöhmA. and KiebackB.: ‘Fabrication of silicide materials and their composites by reaction sintering’, Mater. Sci. Eng. A, 1999, 261, 204–211. doi: 10.1016/S0921-5093(98)01067-3
11.
XuJ., ZhangB., JiangG., LiW. and ZhuangH.: ‘Fabrication and characterization of SiCw/MoSi2 composite from COSHSed powder’, J. Mater. Sci., 2007, 42, 5795–5798. doi: 10.1007/s10853-006-0703-6
12.
YamadaK. and KamiyaN.: ‘High temperature mechanical properties of Si3N4–MoSi2 and Si3N4–SiC composites with network structures of second phases’, Mater. Sci. Eng. A, 1999, 261, 270–277. doi: 10.1016/S0921-5093(98)01075-2
CarterC. H.Jr, DavisR. F. and BentleyJ.: ‘Kinetics and mechanisms of high-temperature creep in silicon carbide: II, chemically vapor deposited’, J. Am. Ceram. Soc., 1984, 67, 732–740. doi: 10.1111/j.1151-2916.1984.tb19510.x
15.
GaoP.-Z., WangL., HuangS.-T., GuoW.-M., XieW. and XiaoH.-N.: ‘Microstructure and mechanical properties of 3-D interpenetrated network structure MoSi2–RSiC composite’, Ceram. Int., 2012, 38, 5799–5805. doi: 10.1016/j.ceramint.2012.04.027
16.
SonntagA.: ‘New R-SiC extends service life in kiln furniture’, Am. Ceram. Soc. Bull., 1997, 76, 51–54.
17.
WenmingG.: ‘Sintering mechanism and performance improvements of recrystallized silicon carbide’, Dissertation, Hunan University, China, 2012.
18.
DaiJ., ChenD. and LiQ.: ‘First-principle study on the X (X=N, P, As, Sb) doped (9.0) single-walled SiC nanotubes’, Phys. B: Condens. Matter, 2014, 447, 56–61. doi: 10.1016/j.physb.2014.04.065
19.
WinzerJ., WeilerL. and PouquetJ.: ‘Wear behavior of interpenetrating alumina–copper composites’, Wear, 2011, 271, 2845–2851. doi: 10.1016/j.wear.2011.05.042
20.
HeC. N. and TianF.: ‘A carbon nanotube-alumina network structure for fabricating epoxy composites’, Scr. Mater., 2009, 61, 285–288. doi: 10.1016/j.scriptamat.2009.04.003
21.
GuoZ., BluganG., GrauleT., ReecebM. and KueblerJ.: ‘The effect of different sintering additives on the electrical and oxidation properties of Si3N4–MoSi2 composites’, J. Eur. Ceram. Soc., 2007, 27, 2153–2161. doi: 10.1016/j.jeurceramsoc.2006.07.009
22.
GuoW., XiaoH., GaoP., XieW., LiQ. and HuJ.: ‘Investigation of MoSi2 melt infiltrated RSiC and its oxidation behavior’, Ceram. Int., 2012, 38, (1), 111–117. doi: 10.1016/j.ceramint.2011.04.138
23.
ShitingH.: ‘Preparation of MoSi2–RSiC composites by PIP–AAMI process and its properties study’, Dissertation, Hunan University, China, 2013.
24.
EsfehanianM., GünsterJ., MoztarzadehF. and HeinrichJ.: ‘Development of a high temperature Cf/XSi2–SiC (X=Mo, Ti) composite via reactive melt infiltration’, J. Eur. Ceram. Soc., 2007, 27, (2), 1229–1235. doi: 10.1016/j.jeurceramsoc.2006.05.058
25.
GaoP.-Z., XiaoH.-N., GuoW.-M. and ZhangX.-L.: ‘One method to prepare the MoSi2–RSiC composites’, 201310715292.2.
26.
BSEN 843-1: ‘Advanced technical ceramics – Monolithic ceramics – Mechanical properties at room temperature – part 1: Determination of flexural strength’, 1995.
ZhangM. X., HuQ. D., HuangB., LiJ. Z. and LiJ. G.: ‘Study of formation behavior of TiC in the Fe-Ti-C system during combustion synthesis’, Int. J. Refract. Met. Hard Mater., 2011, 29, (3), 356–360. doi: 10.1016/j.ijrmhm.2011.01.001
29.
LiuJ., BaiY., ChenP., CuiN. and YinH.: ‘Reaction synthesis of TiSi2 and Ti5Si3 by ball-milling and shock loading and their photocatalytic activities’, J. Alloys Compd., 2013, 555, 375–380. doi: 10.1016/j.jallcom.2012.12.100
30.
YangY., ChangY. A., TanL. and DuY.: ‘Experimental investigation and thermodynamic descriptions of the Mo–Si–Ti system’, Mater. Sci. Eng. A, 2003, 361, 281–293. doi: 10.1016/S0921-5093(03)00560-4
31.
GaoP.-Z., ZhangX.-L., LiuJ.-X., HuangS.-T., XieW. and XiaoH.-N.: ‘Microstructure and properties of MoSi2–RSiC composites prepared by PIP and MoSi2–Si–Al Alloy melting infiltration composite process’, Key Eng. Mater., 2014, 602–603, 494–498. doi: 10.4028/www.scientific.net/KEM.602-603.494
32.
XiaoH.-N. and GaoP.-Z.: ‘High performance structural ceramics and their application’, 04; 2006, Beijing, China, Chemical Industry Press.
33.
HuangQ.-W. and ZhuL.-H.: ‘High-temperature strength and toughness behaviors for reaction-bonded SiC ceramics below 1400°C’, Mater. Lett., 2005, 59, 1732–1735. doi: 10.1016/j.matlet.2005.01.049
34.
GaoP.-Z., ZhangX.-L., HuangS.-T., LiuJ.-X. and XiaoH.-N.: ‘Influence of infiltrated temperatures on the microstructure and properties of MoSi2(Cr5Si3)–Re-crystallized SiC composites’, J. Chin. Ceram. Soc., 2014, 42, (9), 1105–1110.
35.
KimK. J., LimK.-Y. and KimY.-W.: ‘Influence of Y2O3 addition on electrical properties of β-SiC ceramics sintered in nitrogen atmosphere’, J. Eur. Ceram. Soc., 2012, 32, (16), 4401–4406. doi: 10.1016/j.jeurceramsoc.2012.07.001
36.
ChangC.-M., ChangY.-C. and LeeC.-Y.: ‘Ti5Si4nanobats with excellent field emission properties’, J. Phys. Chem. C, 2009, 113, (21), 9153–9156. doi: 10.1021/jp902082x
37.
GoyalaR. K., KambaleaK. R. and NeneaS. S.: ‘Fabrication, thermal and electrical properties of polyphenylene sulphide/copper composites’, Mater. Chem. Phys., 2011, 128, 114–120. doi: 10.1016/j.matchemphys.2011.02.065
38.
BeckmanS., CookB. A. and AkincM.: ‘An analysis of electrical resistivity of compositions within the Mo–Si–B ternary system part II: Multi-phase composites’, Mater. Sci. Eng. A, 2001, 299, 94–104. doi: 10.1016/S0921-5093(00)01410-6
39.
CallisterW. D.: ‘Fundamentals of materials science and engineering’, 5th edn, 12; 2002, Beijing, China, Chemical Industry Press.