The effects of magnesia (MgO) addition on the ionic conductivity and thermal stability of CaO-stabilised zirconia (CSZ) was investigated by structural and morphological analysis. MgO was added to CSZ using a solid-state reaction, and a secondary phase was not observed via XRD of all specimens sintered at 1600°C. However, Mg2SiO4 and Mg-rich phases were detected in the microstructure of CSZ doped with 5 and 10 mol-% MgO, respectively. Ionic conductivity increased with an increase in MgO content, and CSZ doped with 5 mol-% MgO exhibited a maximum value of 0.819 S cm−1 measured at 1500°C due to the scavenging of Si impurities. The thermal diffusivity increased from 0.517 (CSZ) to 0.649 mm2 s−1 (5 mol-% doped CSZ), and the thermal expansion coefficient of 0.5 mol-% doped CSZ was maximal at 9.855 μm/m°C. The value of mol-% doped CSZ decreased to 8.937 μm/m°C as it was affected by the Mg–Si phase formation.
ChoiS. R. and BansalN. P.: ‘Mechanical behavior of zirconia/alumina composites‘, Ceram. Int., 2005, 31, 39–46. doi: 10.1016/j.ceramint.2004.03.032
2.
HuangW., ShukP., GreenblattM., GroftM., ChenF. and LiuM.: ‘Structural and electrical characterization of a novel mixed conductor: CeO2-Sm2O3-ZrO2 solid solution’, J. Electrochem. Soc., 2000, 147, 4196–4202. doi: 10.1149/1.1394040
3.
RadfordK. C. and BrattonR.J.: ‘Zirconia electrolyte cells‘, J. Mater. Sci., 1979, 14, 59–65. doi: 10.1007/BF01028328
4.
KooH. W., ParkH. J., ChoiG. M. and LeeH. G.: ‘Electrochemical deoxidation of molten steel with application of an oxygen permeable membrane’, ISIJ Int., 2007, 47, 689–698. doi: 10.2355/isijinternational.47.689
5.
ChenX. J., KhorK. Z., ChanS. H. and YuL. G.: ‘Influence of microstructure on the ionic conductivity of yttria-stabilized zirconia electrolyte’, Mater. Sci. Eng., 2002, 335, 246–252. doi: 10.1016/S0921-5093(01)01935-9
6.
TojoT., KawajiH. and AtakeT.: ‘Molecular dynamics study on lattice vibration and heat capacity of yttria-stabilized zirconia’, Solid State Ionics, 1999, 118, 349–353. doi: 10.1016/S0167-2738(98)00424-X
7.
WorrellW. and LiuQ.: ‘Development of an extended-life oxygen sensor for iron and steel melts‘, Solid State Ionics, 1990, 40, 761–763. doi: 10.1016/0167-2738(90)90115-8
8.
ZhouM. and AhmadA.: ‘Synthesis, processing and characterization of calcia-stabilized zirconia solid electrolytes for oxygen sensing applications‘, Mater. Res. Bulletin, 2006, 41, 690–696. doi: 10.1016/j.materresbull.2005.10.018
9.
OotaT. and YamaiI.: ‘Thermal expansion behavior of NaZr4 (PO4)3 type compounds‘, J. Am. Ceram. Soc., 1986, 69, 1–6. doi: 10.1111/j.1151-2916.1986.tb04682.x
10.
BadwalS. P. S.: ‘Zirconia-based solid electrolytes: microstructure, stability and ionic conductivity’, Solid State Ionics, 1992, 52, 23–32. doi: 10.1016/0167-2738(92)90088-7
11.
LeeJ. H., MoriT., LiJ. G., IkegamiT. and TakenouchiS.: ‘The influence of alumina addition and its distribution upon grain-boundary conduction in 15 mol.% calcia-stabilized zirconia’, Ceram. Int., 2001, 27, 269–276. doi: 10.1016/S0272-8842(00)00075-4
12.
GuoX., TangC. Q. and YuanR. Z.: ‘Grain boundary ionic conduction in zirconia-based solid electrolyte with alumina addition’, J. Eur. Ceram. Soc., 1995, 15, 25–32. doi: 10.1016/0955-2219(95)91296-Z
13.
CarvalhoT., AntunesE., CaladoJ., FigueredoF. M. and FradeJ. R.: ‘Lanthanum oxide as a scavenging agent for zirconia electrolytes‘, Solid State Ionics, 2012, 225, 484–487. doi: 10.1016/j.ssi.2012.02.037
14.
ChoY. H., ChoP. S., AuchterlonieG., KimD. K., LeeJ. H., KimD. Y., ParkH. M. and DrennanJ.: ‘Enhancement of grain-boundary conduction in gadolinia-doped ceria by the scavenging of highly resistive siliceous phase’, Acta Mater., 2007, 55, 4807–4815. doi: 10.1016/j.actamat.2007.05.001
15.
LeeK. Y., LeeJ. H., KimH. I., HanK. W. and ParkJ. M.: ‘The influence of sintering additives on the lifetime of the heater for sensor application with Al2O3 substrate’, Mater. Lett., 1998, 37, 90–97. doi: 10.1016/S0167-577X(98)00071-8
16.
PorterD. L. and HeuerA. H.: ‘Microstructural development in MgO-partially stabilized zirconia (Mg-PSZ)’, J. Am. Ceram. Soc., 1979, 62, 298–305. doi: 10.1111/j.1151-2916.1979.tb09484.x
17.
LeachC. A.: ‘Sintering of magnesium partially stabilized zirconia-behavior of an impurity silicate phase’, Mater. Sci. Tech. Ser., 1987, 3, 321–324. doi: 10.1179/mst.1987.3.5.321
18.
GarvieR. C.: ‘The thermal conductivity of stabilized zirconia’, J. Mater. Sci., 1976, 11, 1365–1367. doi: 10.1007/BF00545160
19.
SlackG. A.: ‘Thermal conductivity of MgO, Al2O3, MgAl2O4, and Fe3O4 crystals from 3 to 300°K’, Phys. Rev., 1962, 126, 427. doi: 10.1103/PhysRev.126.427
20.
SuzukiI., OhtaniE. and KumazawaM.: ‘Thermal expansion of modified spinel, BETA-Mg2SiO4’, J. Phys. Earth, 1980, 28, 273–280. doi: 10.4294/jpe1952.28.273