In most countries, fibreboards are not recovered after utilization but burned for energy production. This study aims at recovering fibres from industrial fibreboards and reusing them as reinforcement elements in wood polymer composites (WPC). Recovered fibre (RF) material was generated by the thermo-hydrolytic disintegration of medium and high density fibreboards bonded with urea-formaldehyde resin. Various formulations of RF and polypropylene were used with or without the addition of the coupling agent to manufacture WPC using a co-rotating extruder. Test specimens were produced via injection moulding whereby those containing ‘virgin’ fibres served as a reference with respect to mechanical and physical properties. WPC formulations containing RF and ‘virgin’ fibres exhibited similar results, but composites containing RF exhibited improved mechanical and water-related properties, especially without coupling agent. The study indicates that recovered fibres are suitable to produce WPC with very similar physico-mechanical properties as those from ‘virgin’ fibres.
AdhikaryKB, PangS, StaigerMP.2008. Dimensional stability and mechanical behaviour of wood-plastic composites based on recycled and virgin high-density polyethylene (HDPE). Compos Part B: Eng. 39:807–815. doi: 10.1016/j.compositesb.2007.10.005
2.
BAV. 2015. Waste wood recycling in Germany. Berlin: German Association of Waste Wood Recyclers.
BledzkiAK, ReihmaneS, GassanJ.1998. Thermoplastics reinforced with wood fillers: a literature review. Polym-Plast Technol. 37(4):451–468. doi: 10.1080/03602559808001373
5.
ButylinaS, MartikkaO, KärkiT.2011. Properties of wood fibre-polypropylene composites: effect of wood fibre source. Appl Compos Mater. 18:101–111. doi: 10.1007/s10443-010-9134-2
6.
CantwellWJ, MortonJ.1991. The impact resistance of composite materials – a review. Composites. 22:347–362. doi: 10.1016/0010-4361(91)90549-V
7.
CaulfieldDF, ClemonsC, JacobsonRE, RowellRM.2005. Wood thermoplastic composites. Chap. 13. In: RowellRoger M., editors. Handbook of wood chemistry and wood composites. Boca Raton (FL): CRC Press LLC; p. 365–378.
8.
ClemonsC.2002. Wood-plastic composites in United States: the interfacing of two industries. Forest Products J. 52(6):10.
9.
DányádiL, MóczóJ, PukánskyB.2010. Effect of various surface modifications of wood flour on the properties of PP/wood composites. Compos Part A: Appl Sci. 41:199–206. doi: 10.1016/j.compositesa.2009.10.008
10.
FAO. 2016. 2015 global forest products facts and figures. Rome: FAO – Food and Agriculture Organization of the United Nations.
11.
GozdeckiC, WilcynskiA, KociszewskiM, ZajchowskiS.2015. Properties of wood-plastic composites made of milled particleboard and polypropylene. Eur J Wood Wood Prod. 73:87–95. doi: 10.1007/s00107-014-0852-2
12.
GozdeckiC, ZajchowskiS, KociszewskiM, WilczynskiA, MirowskiJ.2011. Effect of wood particle size on mechanical properties of industrial wood particle-polyethylene composites. Polimery. 56(5):375–380.
13.
GwonJA, LeeSY, ChunSJ, DohGH, KimJH.2010. Effects of chemical treatments of hybrid fillers on the physical and thermal properties of wood plastic composites. Compos Part A: Appl Sci. 41:1491–1497. doi: 10.1016/j.compositesa.2010.06.011
14.
Indufor. 2013. Study on the wood raw material supply and demand for the EU wood-processing industries. Helsinki: Indufor Oy.
15.
IrleM, PrivalF, CouretL, BelloncleC, DéroubaixG, BonninE, CathalaB.2018. Advanced recycling of post-consumer solid wood and MDF. Wood Material Sci Eng. doi:10.1080/17480272.2018.1427144.
16.
LercheH, BenthienJT, SchwarzKU, OhlmeyerM.2014. Effects of defibration conditions on mechanical and physical properties of wood fiber/high-density polyethylene composites. J Wood Chem Technol. 34(2):98–110. doi: 10.1080/02773813.2013.838269
17.
LiB, HeJ.2004. Investigation of mechanical property, flame retardancy and thermal degradation of LLDPE–wood-fibre composites. Polym Degrad Stabil. 83:241–246. doi: 10.1016/S0141-3910(03)00268-4
18.
LuJZ, WuQ, McNabbHS.JR2000. Chemical coupling in wood fibre and polymer composites: a review of coupling agents and treatments. J Wood Fibre Sci. 32(1):88–104.
19.
MantauU.2012. Wood flows in Europe (EU27). Project report, Celle: CEPI-Confederation of European Paper Industries and CEI-Bois European Confederation of Woodworking Industries.
20.
MatuanaLM, StarkNM.2014. The use of wood fibers as reinforcements in composites. Chap. 20. In: O. Sain, M. Faruk, editors. Biofiber reinforcement in composite materials. Cambridge: Elsevier Inc. ISBN: 978-1-78242-122-1; p. 648–688.
21.
MertensO, GurrJ, KrauseA.2017. The utilization of thermomechanical pulp fibers in WPC: a review. J Appl Polym Sci. 134:45161. doi: 10.1002/app.45161
22.
MertensO, KrauseKC, KrauseA.2017. Evaluation of wood fiber composites based on a novel simultaneous defibration and compounding process. J Appl Polym Sci. 135(7):45859. doi: 10.1002/app.45859
23.
MichanicklA, BoehmeC.1998 Sep 8. Process for recovering chips and fibers from residues of timber-derived materials, old pieces of furniture, production residues, waste and other timber containing materials. United States Patent 5804035.
24.
MigneaultS, KoubaaA, ErchiquiF, ChaalaA, EnglundK, WolcottMP.2009. Effects of processing method and fiber size on the structure and properties of wood–plastic composites. Compos Part A: Appl Sci. 40:80–85. doi: 10.1016/j.compositesa.2008.10.004
25.
MigneaultS, KoubaaA, PerreP.2014. Effect of fibre origin, proportion, and chemical composition on the mechanical and physical properties of wood-plastic composites. J Wood Chem Technol. 34(4):241–261. doi: 10.1080/02773813.2013.869604
26.
MonetteL, AndersonMP, GrestGS.1993. The meaning of the critical length concept in composites: Study of matrix viscosity and strain rate on the average fiber fragmentation length in short-fiber polymer composites. Polym Composite. 14(2):101–115. doi: 10.1002/pc.750140204
27.
NourbakhshA, KaregarfardA, AshoriA, NourbakhshA.2010. Effects of particle size and coupling agent concentration on mechanical properties of particulate-filled polymer composites. J Thermoplast Compos. 23(2):169–174. doi: 10.1177/0892705709340962
28.
OksmanK, ClemonsC.1998. Mechanical properties and morphology of impact modified polypropylene-wood flour composites. J Appl Polym Sci. 67:1503–1513. doi: 10.1002/(SICI)1097-4628(19980228)67:9<1503::AID-APP1>3.0.CO;2-H
29.
RoffaelE, DixB.1996. Ablauge aus chemisch-thermische Aufschluß von bereits verarbeiteten bindemittelhaltigen Spen- und Faserplatten, Verfahren zu ihrer Herstellung und ihre Verwendung als Streckmittel für Holzwerkstoff-Bindemittel. Germany Patent 4334422. 1996.
SokkaL, KoponenK, KeränenJ.2015. Cascading use of wood in Finland – with comparison to selected EU countries. Espoo: VTT Technical Research Centre of Finland.
32.
StammAJ.1929. Density of wood substance, adsorption by wood, and permeability of wood. J Phys Chem. 23:398–414.
33.
StarkNM, BergerMJ.1997. Effect of particle size on properties of wood flour reinforced polypropylene composites. In: The fourth international conference on wood fiber-plastic composites. Madison (WI): Forest Products Society; p. 134–143.
34.
StarkNM, RowlandsRE.2003. Effects of wood fibre characteristics on mechanical properties of wood/polypropylene composites. Wood Fibre Sci. 35(2):167–174.
35.
TeuberL.2016. Dissertation: Evaluation of particle and fibre degradation during processing of wood plastic composites (WPC) using dynamic image analysis. Göttingen: Georg-August-University.
36.
TeuberL, MilitzH, KrauseA.2016a. Dynamic particle analysis for the evaluation of particle degradation during compounding of wood plastic composites. Compos Part A: Appl Sci. 84:464–471. doi: 10.1016/j.compositesa.2016.02.028
37.
TeuberL, MilitzH, KrauseA.2016b. Processing of wood plastic composites: the influence of feeding method and polymer melt flow rate on particle degradation. J Appl Polym Sci. 133(13):43231. doi: 10.1002/app.43231
WolcottMP, EnglundK.1999. A technology review of wood-plastic composites. In: 33rd international particleboard/composite materials symposium. Washington (DC): Washington State University; p. 103–111.
41.
YamKL, GogoiBK, LaiCC, SelkeSE.1990. Composites from compounding wood fibers with recycled high density polyethylene. Polym Eng Sci. 30(11):693–699. doi: 10.1002/pen.760301109
42.
ZainiMJ, FuadYA, IsmailZ, MansorMS, MustafahJ.1996. The effect of filler content and size on the mechanical properties of olypropylene/oil palm wood flour composites. Polym Int. 40:51–55. doi: 10.1002/(SICI)1097-0126(199605)40:1<51::AID-PI514>3.0.CO;2-I
43.
ZimmermannMVG, ZatteraAJ.2013. Recycling and reuse of waste electricity distribution networks as reinforcement agents in polymeric composites. Waste Manage. 33:1667–1674. doi: 10.1016/j.wasman.2013.04.002