Porous Poly(DL-lactic- co -glycolic acid)/Calcium Phosphate Cement Composite for Reconstruction of Bone Defects

Calcium phosphate (Ca-P) cements are injectable, self-setting ceramic pastes generally known for their favorable bone response. Ingrowth of bone and subsequent degradation rates can be enhanced by the inclusion of macropores. Initial porosity can be induced by CO₂ foaming during setting of the cement, whereas secondary porosity can develop after hydrolysis of incorporated poly(DL-lactic- co-glycolic acid) (PLGA) microparticles. In this study, we focused on the biological response to porous PLGA/Ca-P cement composites. Pre-set composite discs of four formulations (4 wt% or 15 wt% PLGA microparticles and low or high CO₂ induced porosity) were implanted subcutaneously and in cranial defects in rats for 12 weeks. Histological analysis of the explanted composites revealed that bone and fibrous tissue ingrowth was facilitated by addition of PLGA microparticles (number average diameter of 66 ± 25 µm). No adverse tissue reaction was observed in any of the composites. Significant increases in composite density due to bone ingrowth in cranial implants were found in all formulations. The results suggest that the PLGA pores are suitable for bone ingrowth and may be sufficient to enable complete tissue ingrowth without initial CO₂ induced porosity. Finally, bone-like mineralization in subcutaneous implants suggests that, under appropriate conditions and architecture, porous PLGA/Ca-P cement composites can exhibit osteoinductive properties. These PLGA/Ca-P composites are a promising scaffolding material for bone regeneration and bone tissue engineering.