Damage Mechanics Approach to Material-Dependency of Fracture Toughness in Aluminum Alloys

Abstract

Mixed-mode elastic-plastic fracture toughness in aluminum alloys,i.e., heat-treatable and non-heat-treatable alloys, depends on the hardening mechanism. Present investigation have been carried out to clarify the material dependency of the fracture toughness in aluminum alloys. Two kinds of alloys were regarded as particle reinforced composites which contain inclusions and dispersoids in different matrices. The matrix in the non-heat-treatable alloy has low yield stress and high strain hardening, while the matrix in the heat-treatable alloy has high yield stress and low strain hardening because it is hardened by shearable precipitates. Elastic-plastic analyses of mode I and mode II cracks were conducted for two alloys using finite element method based on Tohgo–Chou–Weng’s constitutive relation of particle-reinforced composites which describes the plasticity of the matrix and the debonding damage between the particles and matrix. From the numerical results for plastic zone and damage evolution around a crack tip, it is qualitatively explained that the heat-treatable alloy exhibits the crack initiation in brittle manner from mode I crack and in ductile manner from mode II crack, while in the non-heat-treatable alloy the crack initiation occurs in ductile manner from both cracks.

Keywords

fracture toughness aluminum alloy heat-treatable alloy non-heattreatable alloy particle reinforced composites debonding damage plastic zone

Get full access to this article

View all access options for this article.

References

Bao, G. (1992). Damage due to fracture of brittle reinforcements in a ductile matrix. Acta Metall. Mater., 40: 2547–2555.

Brockenbrough, J.R. and Zok, F.W. (1995). On the role of particle cracking in flow and fracture of metal matrix composites. Acta Metall. Mater., 43: 11–20.

Cho, Y.T. , Tohgo, K. and Ishii, H. (1997). Load carrying capacity of a broken ellipsoidal inhomogeneity.Acta Mater., 45: 4787–4795.

Eshelby, J.D. (1957). The determination of the elastic field of an ellipsoidal inclusion, and related problems. In: Proceedings of the Royal Society. London. A241: pp. 376–396.

Kiser, M.T. , Zok, F.W. and Wilkinson, D.S. (1996). Plastic flow and fracture of a particulate metal matrix composite. Acta Mater., 44: 3465–3476.

Llorca, J. , Martin, A. , Ruiz, J. and Elices, M. (1993). Particulate fracture during deformation of a spray formed metal-matrix composite. Metall. Trans. A, 24A: 1575–1588.

Mori, T. and Tanaka, K. (1973). Average stress in matrix and average elastic energy of materials with misfitting inclusions. Acta Metall., 21: 571–574.

Needleman, A. (1987). A continuum model for void nucleation by inclusion debonding. Trans. ASME, J. Appl. Mech., 54: 525–531.

Tohgo, K. and Ishii, H. (1992). Elastic-plastic fracture toughness test under mixed mode I–II loading. Eng. Frac. Mech., 41: 529–540.

10.

Tohgo, K. and Ishii, H. (1995). Material-dependency of mixed mode elastic-plastic fracture toughness in aluminum alloys. JSME Annual Meeting, No. 95-1(II): 298–299.

11.

Tohgo, K. and Chou, T.W. (1996). Incremental theory of particulate-reinforced composites including debonding damage. JSME Int. J., 39: 389–397.

12.

Tohgo, K. and Cho, Y.T. (1999). Theory of reinforcement damage in discontinuously reinforced composites and its application. JSME Int. J., 42: 521–529.

13.

Tohgo, K. and Weng, G.J. (1994). A progressive damage mechanics in particle-reinforced metal-matrix composites under high triaxial tension. Trans. ASME, J. Eng. Mater. Technol., 116: 414–420.

14.

Tohgo, K. , Suzuki, N. and Ishii, H. (1996). Influence of debonding damage on a crack tip field in particulate-reinforced ductile-matrix composite.Int. J. Damage Mechanics, 5: 150–170.

15.

Tohgo, K. , Fukuhara, D. , Hadano, A. and Ishii, H. (1998). Influence of debonding damage on mechanical performance of glass particle reinforced nylon 66 composites. ASME Int., PVP, 374: 331–338.

16.

Whitehouse, A.F. and Clyne, T.W. (1993). Cavity formation during tensile straining of particulate and short fibre metal matrix composites.Acta Metall. Mater., 41: 1701–1711.