Electric-Current Induced Crack Growth in Thin Films: Experimental Observations and Continuum Description

Abstract

Electric-current (EC) induced failure of pre-cracked, wide unpassivated interconnections is studied on a 0.2 mmthick, pure aluminum film. The film is deposited by high vacuum evaporation coating (HVEC) and patterned into test structures of varying widths. The specimens were electrically loaded to failure under EC via step, and slow or fast ramp loading. The EC induced failure was observed as localized crack growth or spread of a damage zone, depending on the rate of EC loading and the uncracked ligament width. Both crack and damage zone grew or spread towards the positive electrode. The experimental measurements of EC to failure showed a square root dependence on the uncracked ligament width, irrespective of the details of the failure mechanics. Based on this observation, the macroscopic critical current intensity factor is proposed to be used as the material property of the failure criterion, similar to the fracture toughness KIC for brittle fracture.

Get full access to this article

View all access options for this article.

References

Adkins, C. J. 1983. Equilibrium Thermodynamics, Cambridge University Press, New York.

Attardo, M. J. and Rosenberg, R. 1970. “Electromigration Damage in Aluminum Film Conductors,” Journal of Applied Physics, 41(6):2381–2386.

Bastawros, A.-F. and Kim, K.-S. , 1998. “Experimental Study on Electric-Current Induced Damage Evolution at the Crack Tip in Thin Film Conductors,” Journal of Electronic Packaging,120:345–359.

Born, M. and Wolf, E. 1980. Principles of Optics,Pergamon Press, New York.

Bower, A. F. and Freund, L. B. 1995. “Finite Element Analysis of Electromigration and Stress Induced Diffusion in Deformable Solids,” in Materials Reliability in Microelectronics “V”,edited by Oates, A. S. , Gadepally, K. , Rosenberg, R. and Filter, W. F. , Proceedings, MRS Meeting.

Chaug, Y.-S. and Huang, H. L. 1976. “Temperature Distribution on Thin-Film Metallizations,” Journal of Applied Physics,47(5):1775–1779.

Christou, A. 1994. Electromigration and Electronic Device Degradation,John Wiley & Sons Inc., New York.

Gardner, D. S. , Meindl, J. D. and Saraswat, K. C. 1987. “Interconnection and Electromigration Scaling Theory,” IEEE Transactions on Electron Devices,ED-34, pp. 633–643.

Ho, P. S. , 1970. “Motion of Inclusion Induced by a Direct Current and a Temperature Gradient,” Journal of Applied Physics,41:64–68.

10.

Kaneko, H. , Kawanoue, T. , Hasunuma, M. and Miyauchi, M. 1994. “Reliability of Single-Crystal Aluminum Lines and Its Limitation,” in Stress Induced Phenomena in Metalization, edited by Ho, P. S. , Li, C. Y. and Totta, P. , Proceedings,A.I.P. Conference, 305:179–194.

11.

Marieb, T. 1994. Observation of Void Nucleation and Growth in Passivated Metal Lines,Ph.D. Thesis, Stanford University.

12.

Maroudas, D. and Pantelides, S. 1995. “Theory and Computer Simulation of Grain-Boundary and Void Dynamics in Polycrystalline Conductors,” in Materials Reliability in Microelectronics “V,” edited by Oates, A. S. , Gadepally, K. , Rosenberg, R. and Filter, W. F. , Proceedings, MRS Meeting.

13.

Penney, R. V. 1964. “Current-Induced Mass Transport in Aluminum,” Journal of Physics and Chemistry of Solids,25:335–345.

14.

Saka, M. , Sasagawa, K. and Abe, H. 1994. “Theoretical Analysis of Electrothermal Crack Problem Considering Thomson Effect,” Proceedings, ASME Meeting,AMD-193, pp. 53–59.

15.

Sigsbee, R. A. 1973. “Electromigration and Metalization Lifetimes,” Journal of Applied Physics, 44(6):2533–2540.