Abstract
Herein, CoF2 nanoparticles (NPs) are prepared by simple coprecipitation method and are characterized by various techniques, i.e., XRD, SEM/EDX, FTIR, and UV/Vis, for their structure identification. As-prepared nanostructures were used as photocatalyst, as antioxidant, and as antimicrobial agent. The degradation studies of the prepared samples were carried out for specific time for the degradation of methylene blue (MLB) dye under a UV/visible spectrophotometer to determine decolorization and change in concentration of MLB with respect to time. The antibacterial activity against Escherichia coli (E. coli) and Bacillus subtilis (B. subtilis) was measured by well diffusion and serial dilution method to determine their efficiency against these two bacteria, through a dose-dependent method. The antibacterial activity was further confirmed against the experimental bacteria through calculation of minimum inhibition concentration (MIC). The antioxidant activity (radical scavenging activity) of the prepared CoF2 NPs was also assessed.
1. Introduction
The utilization of matter at the nanoscale (1-100 nm), i.e., atomic, molecular, or supramolecular, for commercial and industrial applications is related to nanotechnology. Quantum confinement and size are the important aspects of the nanomaterials for the development of devices and commercial products [1, 2]. Nanotechnology includes a variety of fields, and on the basis of size, nanomaterials have diverse applications including energy storage, surface chemistry, semiconductor, catalysis, organic chemistry, engineering, biology, thin layer, and self-assemblies [3–5]. Various types of semiconductor oxide and sulphide like TiO2, SnO2, Fe2O3, ZnO, WO3, CdS, WS2, ZnS, and MoS2 have been used widely for the degradation of organic pollutants; however, they have poor activity without the addition of cocatalyst due to the rapid recombination of electron and hole pair before they migrate to the surface for reaction [6–8]. Metal fluorides (like zirconium, aluminum, rare-earth metals, and hafnium) have commercial application in isotopic separation and metallurgy and in the preparation of optical and ceramic materials; however, recently, their used has been increased in the field of biosensing, catalysis, as cathode materials for LIBs, super capacitors, and photonics [9–12]. In the past, researchers have used CoF2 as promising anode material for LIBs. Fu et al. for the first time use CoF2 as anode material for LIBs [13]. MnF2 and CaF2 were used as antimicrobial agents for gram-positive and gram-negative bacteria to find their efficiency [14, 15]. Similarly, Zapała et al. used niflumic acid synthesized with different transition metal complexes for determination of their catalytic and antibacterial activity [16]. Xi et al. used fluorides as disinfectant for the treatment of bacteria [17]. Gajendiran et al. synthesized cobalt ferrite and treat as antimicrobial agent which shows good results against gram-positive bacteria [18]. Arun and Li et al. prepared cobalt and cobalt ferrite NPs and used them as photocatalyst for the degradation of organic dyes like MLB dye and showed efficient results against these dyes as catalyst [19, 20]. Yan et al. used bimetallic fluorides as efficient oxygen reduction catalyst in the defect-enriched carbon nanofibers [21]. Li et al. used cobalt- and fluoride-based photocatalyst for the high-performance evolution of oxygen [22–24]. However, no literature data on CoF2 is available as catalyst for the degradation of MLB and as antimicrobial agent and used as photocatalyst for the first time with high efficiency by decolorizing and degraded MLB. The novelty of the prepared CoF2 nanostructures lies in their application, i.e., catalytic and antimicrobial results which were carried out for the first time and not reported in the literature yet.
2. Experimental
2.1. Materials
Cobalt nitrate tetrahydrate, deionized (DI) water, ammonium fluoride, ethanol, etc. were purchased from Sigma-Aldrich and used for the preparation of CoF2 NPs.
2.2. Synthesis of CoF2 NPs by Coprecipitation Method
CoF2 NPs were prepared by dissolving 0.582 g of cobalt nitrate tetrahydrate and 0.182 g of ammonium fluoride in two separate beakers in 4 mL of DI water. The two solutions were then mixed in 30 mL of ethanol in a beaker and stirred for 20 min; immediately, pink color precipitate will appear for CoF2 NPs; centrifuge and filter the precipitate and dry in an oven for two hours and characterize on various techniques for their structure confirmation and identification. The prepared CoF2 NPs were then used as catalyst for the degradation of MLB dye as antioxidant and as microbial agent for the treatment of gram-positive and gram-negative bacteria.
2.3. Preparation and Extraction Procedure of MLB Dye for Degradation Studies
Take 3 mg of CoF2 catalyst powder in three separate I-Chem glass vials and add 10 μL of MLB (10 ppm solution) to each vial; seal the vial, vertex, and shake for 1 minute to promote contact between the sample powder and MLB solution. The substrate will be adsorbed on the surface of catalyst, and after 0 min, 30 min, 60 min, 90 min, and 120 min extracted with 2 mL of isopropyl alcohol (IPA), filter through a 0.45 μm PTFE syringe filter and analyze on a UV/visible spectrophotometer for their degradation studies. The same reaction and extraction procedure was used for the rest of sample preparation and degradation studies. To find the efficiency of synthesized CoF2 NPs, the amount of catalyst and methylene was kept fixed for all the samples and only varying the time duration.
2.4. Antimicrobial Activity of Cobalt Fluoride NPs
The prepared CoF2 NPs were examined for their antibacterial activity against Escherichia coli (E. coli) and Bacillus subtilis (B. subtilis), by well diffusion and serial dilution method [25, 26] to determine their efficiency against these two bacteria, through a dose-dependent method. In this method, in 1 mL of deionized water, 2 mg of cobalt fluoride was dissolved and sonicate this solution for 30 min. The bacteria under test were purchased from CGMCC (China General Microbial Culture Collection Center). Incubate the bacterial culture containing LB media in a 4 mL tube. Keep the tube at 37°C to achieve the 0.5 standard of McFarland (
2.5. Minimum Inhibition Concentration (MIC)
The minimum concentration at which no visible growth of the tested bacteria occurs is used as indicator to confirm and verify the inhibition of bacteria. CoF2 NPs and needles of different concentrations (i.e., 7.5, 15, 30, and 60 μg/mL) were added to 4.0 mL LB media broth in four different tubes, and also, 60 μL of culture bacteria to each tube was added. Place these tubes at 37°C for 48 h for incubation and then observe and note the growth of bacteria in each tube.
2.6. Antioxidant Activity
The antioxidant activity (radical scavenging activity) of the prepared CoF2 NPs and needles was performed as reported in literature [27, 28]. Dissolve different concentrations (0.031, 0.062, 0.125, 0.25, 0.5, and 1.0 mg/mL) of CoF2 NPs and needles in methanol and add 0.5 mL of 1 mM of DPPH to each tube containing different concentrations and incubate in the dark for 30 min at room temperature. After that, measure the absorbance of both control and sample by UV-Visible Cary 50 at wavelength 517 nm by taking methanol as blank and vitamin C as control blank and calculate their scavenging ability through the following equation.
3. Results and Discussion
3.1. Physicochemical Characterization
To find the crystal structure and composition of synthesized CoF2 NPs, XRD techniques were used. The X-ray diffraction studies of the synthesized CoF2 NPs matched with JCPDS card number 01-072-1179, which shows purity and tetragonal structure for CoF2 NPs. After drying in oven at 110°C, the crystallinity of the synthesized material improved as evident from the XRD spectrum (Figure 1). The particle size of the prepared cobalt fluoride NPs was calculated by the Scherrer equation which is 36.45 nm after drying.
XRD patterns for CoF2 NPs synthesized by the precipitation method.
To find the morphology and shape of the synthesized CoF2 NPs, SEM was employed. SEM studies of the prepared NPs show flake-type morphology, and the particles agglomerate instead of dispersion as shown in Figure 2. EDX was performed to determine the elemental composition of CoF2 NPs. EDX studies of NPs are shown in Figure 3, and it exhibits that the synthesized material contains only Co, F, and oxygen with no impurities.
(a, b) SEM micrographs of CoF2 NPs prepared by simple precipitation method with different magnifications.
EDX spectrum of the prepared CoF2 NPs.
FTIR studies were used to further confirm the prepared CoF2 NPs. FTIR spectrum of the synthesized material shows its frequency range between 400 cm-1 and 4000 cm-1. FTIR spectrum of the prepared material shows that the broad peak of the hydroxyl group for water disappears after drying as shown in Figure 4 which indicate that the material is pure. Other stretching frequencies for CoF2 NPs appear at 538 cm-1, 1212 cm-1, 1363 cm-1, and 1747 cm-1, which are due to C-H, C-O, and C-F stretching.
FTIR spectra of prepared CoF2 NPs.
UV/visible spectroscopic analysis was performed between 200 and 800 nm to find the wavelength absorption and optical band gap of the synthesized CoF2 NPs through Kubelka-Munk function. The band gap for CoF2 NPs was calculated to be 2.79 eV as shown in Figures 5 and 6, before and after drying. Catalytic properties of the prepared CoF2 NPs depend mainly upon their microstructure, particle size, and surface morphology. XRD studies of the prepared CoF2 NPs show that after drying the crystallinity of the material improved; also, particles size decreases which increase the surface area, and thus, the catalytic behavior of the CoF2 NPs increases. Moreover, band gap calculation of the CoF2 NPs also shows that after drying the crystallite size decreases which decrease the band gap, and thus, their catalytic effect increases as shown in Figure 6 from their band gap calculation through the Kubelka-Munk function.
UV-Vis spectra of prepared CoF2 NPs.
Band gap calculation of CoF2 NPs (a) before and (b) after drying.
3.2. Degradation Studies of MLB Dye
Degradation studies of MLB solution (10 ppm) were carried out with the help of UV/visible spectrophotometer (Cary 50) to determine the efficiency of CoF2 photocatalyst with respect to time and their decolorization rate. Initially, 3.0 mg of CoF2 catalyst powder is in three separate I-Chem glass vials, and add 10 μL of MLB (10 ppm solution) to each vial, seal the vial, vertex, and shake for 1 minute to promote contact between the sample powder and MLB solution. The substrate will be adsorbed on the surface of catalyst, and after 0 min, 30 min, 90 min, and 120 min extracted with 2 mL of isopropyl alcohol (IPA), filter through a 0.45 μm PTFE syringe filter and analyze on a UV/visible spectrophotometer for their degradation studies. The same reaction and extraction procedure was used for the rest of sample preparation and degradation studies. To find the efficiency of synthesized CoF2 NPs, the amount of catalyst and methylene was kept fixed for all the samples and only varying the time duration. UV/visible data of the CoF2 NPs shows that after 0 min no degradation and decolorization occur; after 30 min, 40%; after 60 min, 50% degradation; after 90 min, 70% degradation and decolorization appear in all the samples; and after 120 mint, 90-94% of the samples were degraded with the decrease in concentration with respect to time as indicated from their UV/visible graph (Figure 7).
UV/visible spectrum shows the degradation studies of MLB dye.
3.3. Antioxidant Activity
The scavenging activity of CoF2 NPs is shown in Figure 8. By getting electron or hydrogen from the donor atom, 1-diphenyl-2-picrylhydrazyl (DPPH) radical is reduced [29, 30]. It shows high efficiency at concentration of 1 ppm (1 mg/mL). For CoF2 NPs, the IC50 was higher than 1 μg/mL. The mechanisms of antioxidant activity of CoF2 NPs were unknown; however, it depends upon the transfer of electron from oxygen to nitrogen atom of DPPH and the electronic transition occurs at 517 nm for
Percentage DPPH scavenging of CoF2 NPs and vitamin C.
3.4. Antibacterial Activity
The antibacterial activity of CoF2 NPs was tested against gram-positive B. subtilis and gram-negative E. coli bacteria (Figure 9). The results showed the inhibition of both bacteria at different concentrations of 2, 1, and 0.5 and 0.25, 0.5, 1.0, and 2.0 mg/mL of CoF2 NPs. These NPs show higher inhibition against B. subtilis as compared to E. coli at different concentrations. The zone of inhibition (ZOI) for B. subtilis was 17 mm at concentration of 1 mg/mL. However, E. coli were less susceptible to NPs. The exact mechanism of action of CoF2 NPs on these bacteria is unknown; however, through oxidative stress, it ruptures the cell membrane by damaging the bacterial lipid layer, DNA, and inhibits bacterial growth. Fluoride act as anticaries, by increasing acidification, reducing bacterial growth, and enhancing permeability of proton through membrane by ATPases [31–33].
Antibacterial activity of (a) Bacillus subtilis and (b) E. coli control over CoF2 NPs.
4. Conclusion
CoF2 NPs were prepared through the coprecipitation method and characterized by various techniques, i.e., XRD, SEM/EDX, FTIR, and UV/Vis, to conform their structure. Further catalytic efficiency of CoF2 NPs was checked against MLB dye for the first time. The UV/visible studies of the synthesized catalyst show that MLB degraded after some time by decolorizing the IPA solution, and also, the concentration of dye decreases with passage of time. Thus, it is concluded that CoF2 can be used as an efficient catalyst for the degradation of organic dyes (MLB). The prepared CoF2 NPs show effective antibacterial and antioxidant results against gram-positive and gram-negative bacteria, i.e., Escherichia coli (E. coli) and Bacillus subtilis (B. subtilis), for the first time by rupturing their lipid membrane through oxidative stress and acidification.
Footnotes
Data Availability
All the available data are incorporated in the MS.
Conflicts of Interest
The authors declared that they have no conflict of interest.
Acknowledgments
The authors wish to thank Princess Nourah Bint Abdulrahman University Researchers Supporting Project (number PNURSP2022R33), Princess Nourah Bint Abdulrahman University, Riyadh, Saudi Arabia, for financial support.