Free radical suspension copolymerization of styrene (St) with methyl methacrylate (MMA) in the presence of n-pentane was investigated. The batch polymerization was performed in a stirred reactor via a two-stage process. First, free radical suspension polymerization of St and MMA in aqueous media was carried out at about 80—90°C with the aid of a monofunctional initiator to the monomer conversions up to about 70%. Second process, called impregnation stage, consisted of a high temperature—high pressure cycle (110—120°C and 10 bars) in which the blowing agent was charged in the reactor and polymerization was carried out with the aid of a high temperature initiator. Fine particles of micron sizes of St/MMA copolymer were synthesized by manipulation of some experimental parameters governing the copolymerization system. Polymerization was carried out at different agitation rates, suspending agent and aqueous phase initiator concentrations as well as emulsifier amounts, while keeping constant the MMA/St ratio. To reach a desired bead size, the above parameters were optimized using the Taguchi method for experimental design and the relative importance of the mentioned parameters was analyzed. Particles with a spherical shape of 250—350 μm were formed. The obtained copolymers were also characterized in terms of molecular weight, polydispersity index, copolymer composition, morphology of the polymer beads, thermal behavior, and particle size and particle size distribution.
Kiparissides, C. (1996). Polymerization Reactor Modeling: A Review of Recent Developments and Future Directions, Chem. Eng. Sci., 51(10): 1637-1659.
2.
Kalfas, G.A. (1992). Experimental Studies and Mathematical Modeling of Aqueous Suspension Polymerization Reactors. Ph.D. Thesis, University of WisconsinMadison, USA, 1992.
3.
Kotoulas, C. and Kiparissides , C. (2006). A Generalized Population Balance Model for the Prediction of Particle Size Distribution in Suspension Polymerization Reactors, Chem. Eng. Sci., 61(2): 332-346.
4.
Sonnenberg, F. and Schwarz, R.A. (2002). Processes for Forming Styrenic Copolymers. United State Patent No. 6,497,269, B2, Dec. 24, 2002 (to StyroChem Delaware, Inc.).
5.
Sonnenberg, F. and Miladinov, V.D. (2003). Processes for Forming Styrene/ Methyl Methacrylate Copolymers. United State Patent No. 6,502,621, B2, Jan. 7, 2003 (to StyroChem Delaware, Inc.).
6.
Sonnenberg, F. and Schwarz, R.A. (2002). Processes for Forming Styrenic Copolymers. United State Patent No. 6,360.807, B2, March 26, 2002 (to StyroChem Delaware, Inc.).
7.
Sonnenberg, F., Taristo, K.M. and Johansson, T.V.J. (2001). Treatment for Reducing Residual Carbon in the Lost Foam Process. United State Patent No. 6,303,664, Oct. 16, 2001 (to StyroChem Delaware, Inc.).
8.
Tang, S., Lu, G., Han, X. and Hong, J. (2004). Foamable Copolymer Resin and a Method for Preparing the Same. United State Patent No. 6,770,681, B2, Aug. 3, 2004 (to Hangzhou Yuhang Yatai Chemical Industries Co., Ltd.).
Horie, K., Mita, I. and Kambe, H. (1968). Calorimetric Investigation of Polymerization Reactions. I. Diffusion-Controlled Polymerization of Methyl Methacrylate and Styrene , J. Polym. Sci. Part A: Polym. Chem., 6(9): 2663-2676.
11.
Villalobos, M.A. , Hamielec, A.E. and Wood, P.E. (1993). Bulk and Suspension Polymerization of Styrene in the Presence of n-Pentane. An Evaluation of Monofunctional and Bifunctional Initiation, J. Appl. Polym. Sci., 50(2): 327-343.
12.
Maggioris, D. , Goulas, A., Alexopoulos , A.H., Chatzi, E.G. and Kiparissides , C. (2000). Prediction of Particle Size Distribution in Suspension Polymerization Reactors: Effect of Turbulence Nonhomogeneity, Chem. Eng. Sci., 55(20): 4611-4627.
13.
Kiparissides, C., Alexopoulos, A., Roussos , A., Dompazis, G. and Kotoulad, C. (2004). Population Balance Modeling of Particulate Polymerization Processes, Ind. Eng. Chem. Res. , 43(23): 7290-7302.
14.
Kiparissides, C. (2006). Challenges in Particulate Polymerization Reactor Modeling and Optimization: A Population Balance Perspective , J. Process Control, 16: 205-224.
15.
ASTM D1921: Standard Test Methods for Particle Size (Sieve Analysis) of Plastic Materials (1993). Annual Book of ASTM Standards, American Society for Testing and Materilas, West Conshohocken, PA. Annual Book of ASTM Standards. 1993 . D1921, Vol. 08.01, p. 612.
16.
Lima, E.V., Wood, P.E. and Hamielec, A.E. (1997). An Updated Review on Suspension Polymerization, Ind. Eng. Chem. Res., 36(4): 939-965.
17.
Hamielec, A.E. and Tobita, H. (1992). Polymerization Processes: Ullmann's Encyclopedia of Industrial Chemistry. VCH Publishers, Inc., New York, Vol. A21, p. 305.
18.
Wenning, W. (1956). Über den Mechanismus der dreiphasigen Emulgierung bei der Perlpolymerisation, Makromol. Chem., 20(1): 196-213.
19.
Tanaka, M. and O'Shima, E. (1988). Dispersing Behaviour of Droplets in Suspension Polymerization of Styrene in a Loop Reactor, Canad. J. Chem. Eng., 66(1): 29-35.
20.
Wolters, D. , Zaika, W.M. and Bandermann , F. (2001). Suspension Polymerization of Styrene with Pickering Emulsifiers, Macromol . Mater. Eng., 286(2): 94-106.
21.
Scheirs, J. and Priddy, D.B. (2003). Modern Styrenic Polymers: Polystyrenes and Styrenic Copolymers. Wiley & Sons, Ltd., The Atrium, Southern Gate, Chichester, West Sussex, p. 165.
22.
Tanaka, M. and Hosogai, K. (1990). Suspension Polymerization of Styrene with Circular Loop Reactor, J. Appl. Polym. Sci., 39(4): 955-966.
23.
Chatzi, E.G. and Kiparissides, C. (1994). Drop Size Distributions in High Holdup Fraction Suspension Polymerization Reactors: Effect of the Degree of Hydrolysis of PVA Stabilizer, Chem. Eng. Sci., 49(24B): 5039-5052.
24.
Zhou, G. and Kresta, S. (1998). Evolution of Drop Size Distribution in Liquid-Liquid Dispersions for Various Impellers, Chem. Eng. Sci., 53(11): 2099-2113.
25.
Kiatkamjornwong, S., Chientachakul, P., Prasassarakich , P. and Damronglerd, S. (2001). Kinetic Studies on Styrene-Divinylbenzene Copolymerization by Suspension Technique , J. Appl. Polym. Sci., 82(6): 1521-1540.
26.
Ahmed, S.M. (1984). Effects of Agitation and the Nature of Protective Colloid on Particle Size during Suspension Polymerization, J. Dispersion Sci. Technol., 5(3,4): 421-432.
27.
Kongkaew, A. and Wootthikanokkhan , J. (2000). Effects of Reaction Conditions on Poly(methyl methacrylate) Polymerized by Living Radical Polymerization with Iniferter, J. Appl. Polym. Sci., 75(7): 938-944.
28.
Kongkaew, A. and Wootthikanokkhan , J. (1999). Polymerization of Isoprene by Using Benzyl Diethyldithiocarbamate as an Iniferter , J. Sci. Asia., 25(1): 35-41.
29.
Randall, J.C. (1977). Polymer Sequence Determination . Academic Press, New York, p. 109.
30.
Opresnik, M. and Sebenik, A. (1995). Free Radical Two Step Synthesis of Styrene and Acrylate Block Copolymers with Disulphide Initiators, Polym. Int., 36(1): 13-22.
31.
Songkhla, P.N. and Wootthikanokkhan , J. (2002). Composition on the K and A Constants of the Mark-Houwink Equation: Styrene-Methyl Methacrylate Random Copolymers, J. Polym. Sci. Part B: Polym. Phys., 40(6): 562-571.
32.
Ghasemi, M. (2003). Characterizing the Lost Foam Copolymer Properties and Comparing with Expandable Polystyrene. MSc. Thesis, Sahand University of Technology, Iran.
33.
Pan, Z.R. (1986). Polymer Chemistry. Chemical Industry Press, Beijing, p. 93.
34.
Zhang, L., Liu, G., Ji, R., Yao, Y., Qu, X., Yang, L. and Gao, J. (2003). Thermal Analysis, Glass Transition Temperature and Rheological Behaviour of Emulsion Copolymers of Methyl Methacrylate with Styrene, Polym. Int., 52(1): 74-80.
35.
Penzel, E., Rieger, J. and Schneider, H.A. (1997). The Glass Transition Temperature of Random Copolymers: 1. Experimental Data and the Gordon-Taylor Equation, Polymer , 38(2): 325-337.
36.
Miura, Y., Nakamura, N., Taniguchi, I. and Ichikawa, A. (2003). Copolymerization of Styrene and Butyl Acrylate and Styrene and Methyl Methacrylate Mediated by Monospiro- and Dispiropiperidinyl-N-oxyl Radicals, Polymer, 44(12): 3461-3467.
37.
Nising, P. (2006). High Temperature Radical Polymerization of Methyl Methacrylate in a Continuous Pilot Scale Process. Ph.D. Thesis, École Polytechnique Fédérale de Lausanne, Switzerland.