Asymmetric microcellular composites were prepared by injection molding to study the effects of temperature gradient inside the mold (0 to 60℃) as well as blowing agent (0 to 1%) and natural fibers (0 to 30%) contents. High-density polyethylene, flax fiber, and azodicarbonamide were used as the matrix, reinforcement, and chemical blowing agent, respectively. From the samples produced, a complete morphological characterization was performed. As expected, cell size, cell density, and skin and core thicknesses were affected by blowing agent and natural fiber contents and mold temperatures. It was found that a better microcellular asymmetric structure was obtained with higher fiber and blowing agent contents and higher average mold temperature. From the data obtained, a simple mathematical model was used to fit the relative density of asymmetric foams to include skin, core, and transition zone thicknesses.
Statistics Canada. Estimated areas, yield, production and average farm price of principal field crops, in metric units, http://www.statcan.gc.ca (2013, accessed 28 November 2013).
2.
PattersonJ. New opportunities with wood-flour-foamed PVC. J Vinyl Addit Technol2001; 7: 138–141.
3.
KeenerTJStuartRKBrownTK. Maleated coupling agents for natural fibre composites. Composites Part A2004; 35: 357–362.
4.
MohantyAKMisraMDrzalLT. Sustainable bio-composites from renewable resources: opportunities and challenges in the green materials world. J Polym Environ2002; 10: 19–26.
5.
ShahDU. Developing plant fibre composites for structural applications by optimising composite parameters: a critical review. J Mater Sci2013; 48: 6083–6107.
6.
RiedelUNickelJ. Natural fibre-reinforced biopolymers as construction materials—new discoveries. Angew Makromol Chem1999; 272: 34–40.
7.
NetravaliANChabbaS. Composites get greener. Mater Today2003; 6: 22–29.
8.
BledzkiAKFarukOSperberVE. Cars from bio-fibres. Macromol Mater Eng2006; 291: 449–457.
9.
AshoriA. Wood-plastic composites as promising green-composites for automotive industries!. Bioresour Technol2008; 99: 4661–4667.
MohantyAKMisraMDrzalLT. Surface modifications of natural fibers and performance of the resulting biocomposites: an overview. Compos Interfaces2001; 8: 313–343.
MohantyAKMisraMDrzalLT. Natural fibres, biopolymers, and biocomposites, Boca Raton: CRC Press, Taylor & Francis Group, 2005.
14.
LiXTabilLGOguochaIN. Thermal diffusivity, thermal conductivity, and specific heat of flax fiber-HDPE biocomposites at processing temperatures. Compos Sci Technol2008; 68: 1753–1758.
ZhangYRodrigueDAit-KadiA. High-density polyethylene foams. I. Polymer and foam characterization. J Appl Polym Sci2003; 90: 2111–2119.
17.
BledzkiAKFarukOKirschlingH. Microcellular polymers and composites, Part I: types of foaming agents and technologies of microcellular processing. Polimer2006; 10: 697–703.
18.
Beyer CE and Dahl RB. A method of molding expandable thermoplastic resinous beads. Patent 3,058,161, USA, 1962.
19.
Angell RG Jr. Molding of foamed thermoplastic articles. Patent 3,436,446, USA, 1969.
20.
Martini J, Waldman F and Suh NP. The production and analysis of microcellular thermoplastic foam. In: SPE ANTEC, San Francisco, California, USA, 10–13 May 1982, pp.674–676.
21.
Martini-Vvedensky JE, Suh NP and Waldman FA. Microcellular closed cell foams and their method of manufacture. Patent 4,473,655, USA, 1984.
22.
BarzegariMRRodrigueD. The effect of injection molding conditions on the morphology of polymer structural foams. Polym Eng Sci2009; 49: 949–959.
23.
FarukOBledzkiAKMatuanaLM. Microcellular foamed wood-plastic composites by different processes: a review. Macromol Mater Eng2007; 292: 113–127.
24.
Rodrigue D and Leduc S. The influence of injection molding conditions and polymer composition on skin thickness and flexural properties of HDPE structural foams. In: PPS-19, Melbourne, Australia, 7–10 July 2003, paper no. 41.
25.
Tovar-CisnerosCGonzalez NúñezRRodrigueD. Effect of mold temperature on morphology and mechanical properties of injection molded HDPE structural foams. J Cell Plast2008; 4: 223–237.
26.
Bledzki AK and Faruk O. Microcellular foaming of polypropylene containing wood fibre in an injection moulding process. In: SPE ANTEC, San Francisco, California, USA, 5–9 May 2002, pp.1897–1901.
27.
BledzkiAKFarukO. Microcellular wood fibre reinforced polypropylene composites in an injection moulding process. Cell Polym2002; 21: 417–429.
TissandierCVazquez FletesRCGonzález-NúñezR. Microcellular agave fibre-high density polyethylene composites produced by injection molding. J Mater Sci Eng2012; 11: 677–692.
32.
KumarVWellerJE. A model for the unfoamed skin on microcellular foams. Polym Eng Sci1994; 34: 169–173.
33.
GosselinRRodrigueD. Cell morphology analysis of high density polymer foams. Polym Test2005; 24: 1027–1035.
34.
KumarVSuhNP. A process for making microcellular thermoplastic parts. Polym Eng Sci1990; 30: 1323–1329.
35.
KumarVWellerJ. Production of microcellular polycarbonate using carbon dioxide for bubble nucleation. Trans ASME J Eng Ind1994; 116: 413–420.
36.
Rodrigue D. The effect of density profile on the flexural modulus of polymer foams. In: SPE ANTEC, Cincinnati, Ohio, USA, 6–11 May 2007, pp.3038–3042.
37.
RodrigueD. Using density profiles to predict the flexural modulus of structural polymer foams. J Cell Plast2008; 44: 381–389.
38.
VillamizarCAHanCD. Studies on structural foam processing II. Bubble dynamics in foam injection molding. Polym Eng Sci1978; 18: 699–710.
39.
JohnMJAnandjiwalaRD. Recent developments in chemical modification and characterization of natural fiber-reinforced composites. Polym Compos2008; 29: 187–207.
BalasuriyaPWYeLMaiYW. Mechanical properties of wood flake-polyethylene composites, Part I: effects of processing methods and matrix melt flow behaviour. Composites Part A2001; 32: 619–629.
42.
Leyva-PorrasCEsneider-AlcaláMAToxqui-TeránA. Effect of molding parameters on Young’s modulus of an injection molded low-density polyethylene (LDPE). Ind Eng Chem Res2013; 52: 5666–5671.
43.
BaldwinDFParkCBSuhNP. A microcellular processing study of poly(ethylene terephthalate) in the amorphous and semicrystalline states, Part I: microcell nucleation. Polym Eng Sci1996; 36: 1437–1445.
44.
BaldwinDFParkCBSuhNP. A microcellular processing study of poly(ethylene terephthalate) in the amorphous and semicrystalline states, Part II: cell growth and process design. Polym Eng Sci1996; 36: 1446–1453.
45.
WangCYingSXiaoZ. Preparation of short carbon fiber/polypropylene fine-celled foams in supercritical CO2. J Cell Plast2013; 49: 65–82.
46.
MechraouiABarzegariMRRiedlB. Compression moulding of polypropylene foams and their properties. Cell Polym2008; 27: 217–233.
47.
GosselinRRodrigueDRiedlB. Injection molding of postconsumer wood-plastic composites, Part 1: morphology. J Thermoplast Compos Mater2006; 19: 639–657.