The Effects of Through-thickness Compression on the Interlaminar Shear Response of Laminated Fiber Composites

Abstract

The effects of through-thickness compression on the interlaminar shear response of laminated fiber composites were studied. The combined stresses were generated using a hollow cylindrical specimen that was subjected to axial compression and torsion. For both glass- and carbon-fiber composites, through-thickness compression resulted in a significant enhancement in the interlaminar shear stress and strain at failure. Under moderate compression levels, the failure mode changed from elastic to plastic. An attempt was made to predict the observed increase in shear strength for carbon fiber epoxy laminates using three-dimensional lamina failure criteria. Although all the failure theories correctly predicted the trend of increasing shear strength with compression, none were able to predict the full extent of the observed strength increase. These results indicate that improved models are needed for determining failure under a combined state of interlaminar stress. The experimental results demonstrate that there are significant gains to be made in improving interlaminar strengths of composite structures by applying through-thickness compression. This effect could be exploited for improved strength and possibly improved fatigue life of composite joints and other regions in structures where interlaminar stress states are critical.

Keywords

interlaminar shear failure combined stresses through-thickness compression

Get full access to this article

View all access options for this article.

References

1. Berg, C.A. , Tirosh, J. and Israeli, M. (1972). Analysis of Short Beam Bending of Fiber Reinforced Composites, In: Composite Materials: Testing and Design (Second Conference), ASTM STP 497, American Society for Testing and Materials, pp. 206–218.

2. Whitney, J.M. (1985). Elasticity Analysis of Orthotropic Beams under Concentrated Loads, Compos. Sci. Tech., 22: 167–184.

3. Hart-Smith, L.J. (1987). Joints, In: Engineered Materials Handbook, Composites Vol. 1, p. 490. ASM International, Metals Park, OH.

4. Peters, S.T. , Humphrey, W.D. and Foral, R.F. (1991). Filament Winding Composite Structure Fabrication, pp. 7–12, SAMPE, Covina, CA.

5. Simon, N.J. , Drexler, E.S. and Reed, R.P. (1994). Shear/Compression Tests for ITER Magnet Insulation, In: Reed, R.P. , et al. (eds), Advances in Cryogenic Engineering, Vol. 40, Part B, pp. 977–983. Plenum Press, NY.

6. McManamy, T.J. , Kanemoto, G. and Snook, P. (1991). Insulation Irradiation Test Programme for the Compact Ignition Tokamak, Cryogenics, 31: 277–281.

7. McKenna, G.B. , Mandell, J.F. and McGarry, F.J. (1974). Interlaminar Strength and Toughness of Fiberglass Laminates, In: 29th Annual Tech. Conf., Reinforced Plastics/Composites Institute, Section 13-C, pp. 1–8, The Society of the Plastics Industry, Washington D.C.

8. Sun, C.T. and Li, S. (1988). Three-dimensional Effective Elastic Constants for Thick Laminates, J. Comp. Mater., 22: 629–639.

9. Jiang, Z. and Tennyson, R.C. (1989). Closure of the Cubic Tensor Polynomial Failure Surface, J. Comp. Mater. 23: 208–231.

10.

10. Candido, G.M. , Rezende, M.C. and Muller de Almeida, S.F. (2000). Hygrothermal Effects on the Tensile Strength of Carbon/Epoxy Laminates with Molded Edges, Mater. Res. 3(2): 11–17.

11.

11. Christensen, R.M. (1998). The Numbers of Elastic Properties and Failure Parameters for Fiber Composites, J. Eng. Mater. Tech., 120: 110–113.

12.

12. Tsai, S.W. and Wu, E.M. (1971). A General Theory of Strength for Anisotropic Materials, J. Comp. Mater., 5: 58–80.

13.

13. Hashin, Z. (1980). Failure Criteria for Unidirectional Fiber Composites, J. Appl. Mech., 47: 329–334.

14.

14. Kallas, M.N. and Hahn, H.T. (1990). A Failure Criterion for Composites under 3-dimensional State of Stress, In: 35th International SAMPE Symposium, pp. 674–686.

15.

15. Tsai, S.W. and Hahn, H.T. (1980). Introduction to Composite Materials, p. 286. Technomic Pub. Co., Westport, CT.

16.

16. Hahn, H.T. and Kallas, M.N. (1992). Failure Criteria for Thick Composites, BRL-CR-691, U.S. Army Ballistic Research Laboratory, Aberdeen Proving Ground, MD.

17.

17. DeTeresa, S.J. and Larsen, G.J. (2003). Reduction in the Number of Independent Parameters for the Tsai Wu Tensor Polynomial Theory of Strength for Composite Materials, J. Comp. Mater., 37: 1769–1785.