A Simple Fatigue Life Model for Three-dimensional Fiber-Polymer Composites

Abstract

A simple model is proposed for predicting the fatigue life of three-dimensional (3D) fiber-polymer composite materials for certain cyclic load conditions. The fatigue life can be easily calculated using the model with three empirically determined constants: (i) the ultimate strength of the 3D composite, (ii) the ultimate strength of the two-dimensional (2D) laminate, which is identical in every respect to the 3D composite (e.g., same fiber layup pattern, fiber volume content) except for the through-thickness reinforcement, and (iii) the slope parameter (m) of the fatigue-life (S-log N) curve for the 2D laminate. It is shown that the S-log N curves for stitched composites under cyclic tension-tension and compression-compression loading and for z-pinned composites under cyclic bending loading can be accurately predicted using this model. This model can also approximate the tensile fatigue life of composite lap joints reinforced by stitches or z-pins. However, the model is not reliable in predicting the fatigue life of 3D composites in all cases. It is only accurate when the fatigue damage mechanisms and failure mode of the 3D composite are not altered significantly by the through-thickness reinforcement. Consequently, a limitation of the model is that a priori knowledge of the fatigue damage process of the 3D composite is needed before it can be used with confidence to predict fatigue life. This problem is exasperated by the paucity of information available on the fatigue mechanisms of many types of 3D composites. Until this problem is resolved, the model should only be applied to those types of 3D composites in which their fatigue processes have been determined.

Keywords

fatigue modeling 3D composites stitching z-pins

Get full access to this article

View all access options for this article.

References

Tong, L. , Mouritz, A.P. and Bannister, M.K. (2002). 3D Fibre-Reinforced Polymer Composites, Elsevier, London .

Mouritz, A.P. , Bannister, M.K. , Falzon, P.J. and Leong, K.H. (1999). Review of Applications for Advanced Three-dimensional Fibre Textile Composites , Comp., 27A: 1445-1461 .

Mouritz, A.P. and Cox, B.N. (2000). A Mechanistic Approach to the Properties of Stitched Laminates , Comp., 31A: 1-27 .

Guess, T.R. and Reedy, E.D. (1985). Comparison of Interlocked Fabric and Laminated Fibre Kevlar 49/epoxy Composites , J. Comp. Tech. & Res., 7: 136-142 .

Arendts, F.J. , Drechler, K. and Brandt, J. (1993). Advanced Textile Structural Composites - Status and Outlook , In: Chandra, T. and Dhingra, A.K. (eds), Proc. Int. Conf. on Advanced Composite Materials, pp. 409-416 .

Cox, B.N. , Dadkhah, M.S. , Inman, R.V. , Morris, W.L. and Zupon, J. (1992). Mechanisms of Compressive Failure in 3D Composites , Acta Metal. et. Mat., 40: 3285-3298 .

Ding, Y.Q. , Wenger, W. and McIlhagger, R. (1993). Structural Characterization of Mechanical Properties of 3-D Woven Composites , In: Proc. European SAMPE Conf.

Lee, B. , Leong, K.H. and Herszberg, I. (2001). The Effect of Weaving on the Tensile Properties of Carbon Fibre Tows and Woven Composites , J. Rein. Plastics & Comp., 20: 652-670 .

Freitas, G. , Fusco, T. , Campbell, T. , Harris, J. and Rosenberg, S. (1996). Z-fiber Technology and Products for Enhancing Composite Design , In: Proc. 83rd Meeting of the AGARD SMP on ‘Bolted/Bonded Joints in Polymeric Composites’, 2-3 Sept., Paper 17.

10.

Steeves, C. and Fleck, N. (1999). Z-pinned Composite Laminates: Knockdown in Compressive Strength , In: Proc. 5th Conf. on Delamination & Fracture of Comp., 18-19 March, pp. 60-68 .

11.

Stringer, L.G. and Hiley, M.J. (2003). Through-thickness Reinforcement of Composites: z-pinning, Stitching, and 3D Weaving , In: Proc. 14th Int. Conf. Comp. Mats., 14-18 July, Paper 1312.

12.

Chang, P. , Mouritz, A.P. and Cox, B.N. (2004). Tensile Fatigue Properties of z-pinned Carbon/Epoxy Composite , In: Proc. 49th SAMPE 2004 Symp. Exhib., May 16-20, Long Beach, CA.

13.

Rudov-Clark, S. , Mouritz, A.P. and Bannister, M.K. (2003). Tensile Fatigue Properties of 3D Woven Composites , In: Proc. 14th Int. Conf. Comp. Mats., 14-18 July, Paper 0816.

14.

Aymerich, F.P. , Priolo, P. and Sun, C.T. (2003). Static and Fatigue Behaviour of Stitched Carbon/Epoxy Composite Laminates , Comp. Sci. & Tech., 63: 907-917 .

15.

Shah Khan, M.Z. and Mouritz, A.P. (1996). Fatigue Behaviour of Stitched GRP Laminates , Comp. Sci. & Tech., 56: 695-701 .

16.

Mouritz, A.P. (2004). Fracture and Tensile Fatigue Properties of Stitched Fibreglass Composites , J. Inst. Mech. Eng., Part L: Mats: Design & Apps., 218: 87-93 .

17.

Dadkhah, M.S. , Morris, W.L. and Cox, B.N. (1995). Compression-Compression Fatigue in 3D Woven Composites , Acta Metal. et Mat., 43: 4235-4245 .

18.

Dow, M.B. and Smith, D.L. (1989). Damage-tolerant Composite Materials Produced by Stitching Carbon Fabrics , In: Proc. 21st Int. SAMPE Tech. Conf., 25-28 Sept., pp. 595-605 .

19.

Furrow, K.W. , Loos, A.C. and Cano, R.J. (1996). Environmental Effects of Stitched RTM Textile Composites , J. Rein. Plast. Comp., 15: 378-419 .

20.

Lubowinski, S.J. and Poe, C.C. (1987). Fatigue Characterization of Stitched Graphite/Epoxy Composites , In: Proc. Fiber-Tex 1897 Conf., NASA Conf. Pub., pp. 253-271 .

21.

Portanova, M.A. , Poe, C.C. and Whitcomb, J.D. (1992). Open Hole and Postimpact Compressive Fatigue of Stitched and Unstitched Carbon-Epoxy Composites, In: Glenn, G.C. (ed.), Composite Materials: Testing and Design, Vol. 10, ASTM STP 1120, pp. 37-53, American Society for Testing and Materials, Philadelphia .

22.

Vandermey, N.E. , Morris, D.H. and Masters, J.E. (1991). Damage Development under Compression-Compression Fatigue Loading in a Stitched Uniwoven Graphite/Epoxy Composite Material, NASA Report PB91-236026.

23.

Sawyer, J.W. (1985). Effect of Stitching on the Strength of Bonded Composite Single Lap Joints , J. AIAA, 23: 1744-1748 .

24.

Tada, Y. and Ishikawa, T. (1989). Experimental Evaluation of the Effects of Stitching on CFRP Laminate Specimens with Various Shapes and Loadings , Key Eng. Mat., 37: 305-316 .

25.

Lee, C. and Liu, D. (1990). Tensile Strength of Stitching Joint in Woven Glass Fabrics , J. Eng. Mat. & Tech., 112: 125-130 .

26.

Tong, L. , Jain, L.K. , Leong, D. , Kelly, D. and Herszberg, I. (1998). Failure of Transversely Stitched RTM Lap Joints , Comp. Sci. & Tech., 58: 221-227 .

27.

Tong, L. and Jain, L.K. (1995). Analysis of Adhesive Bonded Composite Lap Joints with Transverse Stitching , App. Comp. Mats., 2: 343-395 .

28.

Rugg, K.L. , Cox, B.N. , Ward, K.E. and Serrick, G.O. (1998). Damage Mechanisms for Angled Through-thickness Rod Reinforcement in Carbon-Epoxy Laminates , Comp., 29A: 1603-1613 .

29.

Owsley, G.S. (2000). The Effect of Z-FiberTM Reinforcement on Fatigue Properties of Stiffened Composite Panels , In: Proc. 15th Tech. Conf. American Soc. Comp., 25-27 September.

30.

Chang, P. , Mouritz, A.P. and Cox, B.N. (2004). Tensile Strength and Fatigue Properties of z-pinned Composite Lap Joints , In: Proc. 4th Asian-Australian Conf. Comp. Mats., 6-9 July, Paper No. L650.

31.

Reifsnider, K. and Case, S. (2003). Micromechanical Models, In: Harris, B. (ed.), Fatigue in Composites, Woodhead Publishing Ltd, Cambridge .

32.

Talreja, R. (1987). Fatigue of Composite Materials, Technomic, Pennsylvania .

33.

Harris, B. , Gathercole, N. , Lee, J.A. , Reiter, H. and Adam, T. (1997). Life Prediction of Constant-stress Fatigue in Carbon-fibre Composites , Phil. Trans. Roy. Soc. (London), A355: 1259-1294 .

34.

Ding, X. and Jin, H. (2002). Flexural Fatigue Performance of 3D Woven Composites , In: Proc. 3rd Asian-Australasian Conf. on Comp. Mats., 15-17 July, pp. 761-766 .

35.

Chang, C. , Mouritz, A.P. and Cox, B.N. Flexural Fatigue Properties of z-pinned Carbon/Epoxy Composites (unpublished data).