Powder Priming of SMC. Part II: Failure Mechanism

Abstract

Current sheet molding compound (SMC) panels, when coated with powder primer, show primer popping in the bake oven due to the degassing of the substrate moisture. In the absence of moisture, however, it was found that some SMCs showed severe popping, while other SMC materials did not. These results suggested that, contrary to general opinion, the moisture content in SMC might not be the only cause for popping. This report covers the results of a systematic study that was carried out to identify the factors that contribute to powder primer popping. Several potential variables that could affect popping, such as volatiles in the substrate, thermal conductivity of the substrate, static charges, and powder bake profile were studied. The experiments showed that the poly(vinyl acetate) in the low profile additive (LPA) is the main cause. More specifically, the micro void formation of this low profile additive that eliminates SMC shrinkage, and enables a smooth surface finish, also causes primer popping. Based on the experimental results, it was concluded that the air permeation into these micro voids is the reason behind the popping of the moisture free SMC substrates. This understanding of the failure mechanism, paves the way for the development of low moisture absorbing SMC materials that can be powder primed in our assembly plants, and could remove the barriers for the usage of SMC on GM vehicles.

Keywords

Sheet molding compound (SMC)powder primer paint popping sheet molding compound porosity coating defects powder coating

Get full access to this article

View all access options for this article.

References

Cleveland, M. , Rao, N. , Migda, F. and Hulway, J. (2001). Low Paint Emissions and Low Vehicle Mass: Conflicting Challenges? , International Coatings for Plastics Symposium, June 4-6, Troy, MI.

Kia, H. G. , Mitchell, H. A. , Wathen, T. J. , Shah, B. and Berger, C. R. (2006). Powder Priming of SMC, Part I: Assessment of the Current Technologies , Journal of Composite Materials, 40(16): 1413-1429 .

Kim, S. , Park, J.-K. , Lee, D. , Merle, G. , Allemand, J. , Camino, G. , Luda, M. P. , Revellino, M. and Blancon, R. (1998). Morphology Analysis of Micro Voids in SMC: Ageing Effects , Composites Part A, 29A: 1535-1543 .

Suspene, L. , Fourquier, D. and Yang, Y. (1991). Application of Phase Diagrams in the Curing of Unsaturated Polyester Resins with Low Profile Additives , Polymer, 32(9): 1593-1604 .

Kia, H. G. and Viscomi, P. V. (1992). High-Pressure/High-Temperature Dilatometer , J. of Reinforced Plastics and Composites, 13(8): 666-680 .

Zang, Z. and Zhu, S. (2000). Microvoids in Unsaturated Polyester Resins Containing Poly(vinyl acetate) and Composites with Calcium Carbonate and Glass Fibers , Polymer, 41(10): 3861-3870 .

Ross, L. R. , Hardbeck, S. P. and Bachmann, M. A. (1988). A Review of Mechanisms of Low Profile Resins , In: 43rd Annual Conference, Composites Institute, The Society of Plastics Industry, Inc., February 1-5.

Kiaee, L. , Yang, Y. S. and Lee, L. J. (1988). Effect of Low Profile Additives on the Curing and Surface Morphology of Sheet Molding Compounds , In: 43rd Annual Conference, Composites Institute, The Society of Plastics Industry, Inc., February 1-5.

Kia, H. G. (1993). In: Hamid Kia (ed.), Sheet Molding Compounds Science and Technology, Hanser Publishers, New York .

10.

Kia, H. G. , Mitchell, H. A. , Wathen, T. J. , Shah, B. and Berger, C. R. Powder Priming of SMC, Part III: Low Moisture Formulations (to be published).