Investigation on the Reduction of In-Plane Compressive Strength in Thick Preconditioned Composite Panels

Abstract

This paper investigates the effects of damage characteristics and local curvature change on the residual compressive strength (RCS) of flat 4-mm thick carbon/epoxy panels through the examination of their buckling behavior. The damage was induced by impact, quasi-static loading and embedment of artificial delamination for a variety of damage areas, intensities and different local curvature changes. The embedment technique of artificial delaminations allowed the separation of the damage from the local curvature change. Panels with no or less significant damage in conjunction with no or little local curvature change failed in end crushing because of large membrane reaction, in-plane shear resistance and flexural rigidity. Prebuckling and Poisson's effect dictated their compressive behavior. Panels with significant damage followed the sequential behavior of prebuckling, local buckling, global buckling and ultimate failure in the mid-section region. Their RCSs were dictated by a combination of delamination size, intensity and local curvature change. Propagation of the damage with certain size and intensity associated with reduced flexural rigidity in the damaged area led to the local-to-global buckling transition and the panels failed at the global buckling-to-postbuckling transition at a nodal line. The effect of increasing the panel thickness on the ratio of RCS to a baseline value was not straightforward due to the end crushing failure of the thicker intact panels.

Keywords

composite panels in-plane compression buckling postbuckling delamination compression-after-impact damage tolerance thickness effect.

Get full access to this article

View all access options for this article.

References

Zhou, G. and Rivera, L.A. (2004). Investigation for the Reduction of In-plane Compressive Strength in Preconditioned Thin Panels, J. Composite Materials, 39(5): 391—422.

Starnes, J.H. and Rouse, M. (1981). Postbuckling and Failure Characteristics of Selected Flat Rectangular Graphite—epoxy Plates Loaded in Compression, Proc. 22nd AIAA/ASME/ASCE/ AHS Structures, Structural Dynamics and Materials Conf: 422—423.

Starnes, J.H. and Williams, J.G. (1982). Failure Characteristics of Graphite—epoxy Structural Components Loaded in Compression. In Z. Hashin and C.T. Herakovich (eds.), Mechanics of Composite Materials-Recent Advances, pp. 283—306, Pergamon, New York.

Avva, V.S. (1983). Effect of Specimen Size on the Buckling Behavior of Laminated Composites Subjected to Low-velocity Impact, Compression Testing of Homogeneous Materials and Composites, ASTM STP 808: 140—154.

Guynn, E.G. and O'Brien, T.K. (1985). The Influence of Lay-up and Thickness on Composite Impact Damage and Compression Strength, Proc. 26th AIAA/ASME/ASCE/AHS Structures, Structural Dynamics and Materials Conf., AIAA-85-0646: 187—196.

Vedula, M. , Lee, W.M. , Benedetto, E.E. and Groleau, M.R. (1992). Screening Test for Compression after Impact Strength Evaluation of Composites, Proc. 7th Conf. American Society for Composites: 804—814.

Zhou, G. (1996). Effect of Impact Damage on Residual Compressive Strength of Glass-fibre Reinforced Polyester Laminates, Composite Structures, 35: 171—181.

Davies, G.A.O. , Hitchings, D. and Zhou, G. (1996). Impact Damage and Residual Strengths of Woven Fabric Glass/Polyester Laminates, Composites Part A, 27(7): 1147—1156.

Zhou, G. (1997). Compressive Behaviour of Large Undamaged and Damaged Thick Laminated Panels, Composite Structures, 38(1—4): 589—597.

10.

Wang, J. (1999). Prediction of Post-impact Compressive Strength of Composite Laminates Using an Inhomogeneity Model, J. Composite Materials, 33(24): 2226—2247.

11.

Ilcewicz, L.B. , Dost, E.F. and Coggeshall , R.L. (1989). A Model for Compression after Impact Strength Evaluation, Proc. 21st Int. SAMPE Technical Conf: 130—140.

12.

Kröber, I. (1992). Effect of Impacts on CFRP Structures, Results of a Comprehensive Test Program for Practical Use, Proc. AGARD Conf. 530 Debonding/Delamination of Composites: 29.1—29.6.

13.

Jegley, D.C. (1992). Effect of Low-speed Impact Damage and Damage Location on Behavior of Composite Panels, NASA Technical Paper 3196.

14.

Dost, E.F. , Ilcewicz, L.B. , Avery, W.B. and Coxon, B.R. (1991). Effects of Stacking Sequence on Impact Damage Resistance and Residual Strength for Quasi-isotropic Laminates, Composite Materials: Fatigue and Fracture, ASTM STP 1110: 476—500.

15.

Demuts, E.D. , Sandhu, R.S. and Daniels, J.A. (1992). Post Impact Compressive Strength in Composites, Proc. 9th DoD/NASA/FAA Conf. Fibrous Composites, 2: 1097—1104.

16.

Zhou, G. , Green, E.R. and Morrison, C. (1995). In-plane and Interlaminar Shear Properties of Carbon/Epoxy Laminates, Composites Science and Technology , 55(2): 187—193.

17.

Englestad, S.P. , Reddy, J.N. and Knight, N.F. (1992). Postbuckling Response and Failure Prediction of Graphite—epoxy Plates Loaded in Compression , AIAA J., 30: 2106—2113.

18.

Aston, J.E. and Love, T.S. (1969). Experimental Study of the Stability of Composite Plates, J. Composite Materials, 3: 230—242.

19.

Nemeth, M.P. (1986). Importance of Anisotropy on Buckling of Compression-loaded Symmetric Composite Plates, AIAA J., 24: 1831—1835.

20.

Whitney, J.M. (1987). The Effect of Shear Deformation on the Bending and Buckling of Anisotropic Laminated Plates, Proc. of 4th Int. Conf. on Composite Structures, pp. 1.109—121.

21.

Jensen, D.W. and Lagace, P.A. (1988). Influence of Mechanical Couplings on the Buckling and Postbuckling of Anisotropic Plates, AIAA J., 26: 1269—1277.

22.

Rohwer, K. (1988). Bending-twisting Coupling Effects on the Buckling Load of Symmetrically Stacked Plates, Proc. Int. Conf. Composite Materials and Structures: 313—323.

23.

Grenestedt, J.L. (1989). A Study on the Effect of Bending-Twisting Coupling on Buckling Strengths, Composite Structures, 12: 271—290.

24.

Leissa, A. (1987). A Review of Laminated Composite Plate Buckling , Applied Mechanics Review, 40(5): 575—591.

25.

Whitney, J.M. (1987). Structural Analysis of Laminated Anisotropic Plates , Technomic Publishing Company Inc., PA, USA.

26.

Whitney, J.M. and Browning, C.E. (1985). On Short-beam Shear Tests for Composite Materials, Experimental Mechanics, 25: 294—300.

27.

Cui, W. , Wisnom, M.R. and Jones, M. (1994). Effect of Specimen Size on Interlaminar Shear Strength of Unidirectional Carbon Fibre-epoxy, Composites Engineering, 4(3): 299—307.

28.

Manders, P.W. and Harris, W.C. (1986). A Parametric Study of Composite Performance in Compression-after-impact Testing, SAMPE J., Nov/Dec: 47—51.