Long-term Fatigue Strength Prediction of CFRP Structure Based on Micromechanics of Failure

Abstract

A prediction method for the fatigue strength of polymer composites under arbitrary frequency, load ratio and temperature was developed with the combined method of the micromechanics of failure (MMF) developed by Ha and the accelerated testing methodology (ATM) developed by Miyano and Nakada. The time— temperature dependent master curves of MMF/ATM critical parameters were constructed by tensile and compressive static and fatigue tests for the longitudinal and transverse directions of unidirectional CFRP under various temperatures based on the three-dimensional micromechanics of fibers and matrix resin and the time— temperature superposition principle which holds for the viscoelastic behavior of matrix resin. These master curves can be used to predict the fatigue strength of composite structures with multi-directional laminations at any time, temperature, and number of cycles to failure. The applicability of MMF/ATM combined method to predict the long term strength of CFRP structures was experimentally confirmed by prediction of the open hole compression fatigue strength of the quasi-isotropic CFRP laminates.

Keywords

accelerated testing methodology fatigue strength failure prediction micromechanics of failure constituent-based strength analysis.

Get full access to this article

View all access options for this article.

References

Aboudi, J. and Cederbaum, G. (1989). Analysis of Viscoelastic Laminated Composite Plates , Composite Structure, 12: 243-256.

Miyano, Y. , Nakada, M. , McMurray, M.K. and Muki, R. (1997). Prediction of Flexural Fatigue Strength of CFRP Composites under Arbitrary Frequency, Stress Ratio and Temperature, Journal of Composite Materials, 31: 619-638.

Miyano, Y. , Nakada, M. and Muki, R. (1999). Applicability of Fatigue Life Prediction Method to Polymer Composites, Mechanics of Time-Dependent Materials , 3: 141-157.

Miyano, Y. , Nakada, M. , Kudoh, H. and Muki, R. (1999). Prediction of Tensile Fatigue Life under Temperature Environment for Unidirectional CFRP, Advanced Composite Materials , 8: 235-246.

Miyano, Y. , Nakada, M. and Sekine, N. (2005). Accelerated Testing for Long-term Durability of FRP Laminates for Marine Use, Journal of Composite Materials , 39: 5-20.

Ha, S.K. (2007). Micro-Mechanical Failure Theory:Continuous Fiber Reinforced Composites, Proceedings of the 12th Composites Durability Workshop (CDW-12), St. Maximin, France, March 27-31 (CD-Rom).

Christensen, R. (2006). A Comparative Evaluation of Three Isotropic, Two Property Failure Theories, Journal of Applied Mechanics, 73: 852-859.

Christensen, R.M. (2004). A Two Property Yield, Failure (Fracture) Criterion for Homogeneous, Isotropic Materials, Journal of Engineering Materials and Technology, 126: 45-52.

Christensen, R. and Miyano, Y. (2006). Stress Intensity Controlled Kinetic Crack Growth and Stress History Dependent Life Prediction with Statistical Variability, International Journal of Fracture , 137: 77-87.