Mode II Interlaminar Fracture and Damage Evaluation of GFRP Woven Laminates at Cryogenic Temperatures using the 4ENF Specimen

Abstract

This article focuses on understanding the Mode II interlaminar fracture and damage behavior of glass fiber reinforced polymer (GFRP) woven laminates at cryogenic temperatures. A four point bend, end notched flexure (4ENF) test is performed at room temperature (RT), liquid nitrogen temperature (77 K) and liquid helium temperature (4K), and an R-curve characterization is conducted for determining the mode II cryogenic fracture properties of GFRP woven laminates. The test configuration is also analyzed by finite element analysis coupled with damage. The damage distributions within the 4ENF specimens are predicted, and the effect of damage on the Mode II energy release rate is examined. This work is the first application of failure criteria (Hoffman criterion and maximum strain criterion) to the description of the R-curve behavior and interlaminar fracture toughness values of woven laminate ENF specimens at cryogenic temperatures.

Keywords

cryomechanics end notched flexure testing finite element analysis woven glass—epoxy laminates fracture toughness delamination damage superconducting magnets.

Get full access to this article

View all access options for this article.

References

Takeda, T. , Takano, S. , Shindo, Y. and Narita, F. (2005). Deformation and Progressive Failure Behavior of Woven-Fabric-Reinforced Glass/Epoxy Composite Laminates under Tensile Loading at Cryogenic Temperatures, Composites Science and Technology , 65(11/12): 1691-1702.

Shindo, Y. , Horiguchi, K. , Wang, R. and Kudo, H. (2001). Double Cantilever Beam Measurement and Finite Element Analysis of Cryogenic Mode I Interlaminar Fracture Toughness of Glass-Cloth/Epoxy Laminates, ASME Journal of Engineering Materials and Technology , 123: 191-197.

Horiguchi, K. , Shindo, Y. , Kudo, H. and Kumagai, S. (2002). End-Notched Flexure Testing and Analysis Mode II Interlaminar Fracture Behavior of Glass-Cloth/Epoxy Laminates at Cryogenic Temperatures, ASTM Journal of Composites Technology and Research, 24(4): 239-245.

Rizov, V. , Shindo, Y. , Horiguchi, K. and Narita, F. (2006). Mode III Interlaminar Fracture Behavior of Glass Fiber Reinforced Polymer Woven Laminates at 293 to 4 K, Applied Composite Materials, 13(5): 287-304.

Shindo, Y. , Shinohe, D. , Kumagai, S. and Horiguchi, K. (2005). Analysis and Testing of Mixed-Mode Interlaminar Fracture Behavior of Glass-Cloth/Epoxy Laminates at Cryogenic Temperatures , ASME Journal of Engineering Materials and Technology, 127: 468-475.

Martin, R.H. and Davidoson, B.D. (1999). Mode II Fracture Toughness Evaluation Using Four Point Bend, End Notched Flexure Test, Plastics, Rubber and Composites, 28: 401-406.

Davies, P. , Casari, P. and Carlsson, L.A. (2005). Influence of Fiber Volume Fraction on Mode II Interlaminar Fracture Toughness of Glass/Epoxy Using the 4ENF Specimen, Composites Science and Technology, 65(2): 295-300.

Hahn, H.T. and Pandey, R. (1994). A Micromechanics Model for Thermoelastic Properties of Plain Weave Fabric Composites, ASME Journal of Engineering Materials and Technology, 116: 517-522.

Takeda, T. , Shindo, Y. and Narita, F. (2004). Three-Dimensional Thermoelastic Analysis of Cracked Plain Weave Glass/Epoxy Composites at Cryogenic Temperatures, Composites Science and Technology, 64(15): 2353-2362.

10.

Hoffman, O. (1967). The Brittle Strength of Orthotropic Materials, Journal of Composite Materials, 1: 200-207.