Mechanical Self-adaptability of a SiC/PyC/SiC Composite During Oxidation in Air

Abstract

An oxidation test for three-dimensional (3D) SiC/PyC/SiC composite with CVD SiC coating was performed by thermogravimetric analysis (TGA) in simulated air at temperatures ranging from 600 to 1100°C. After oxidation, the mechanical properties were evaluated by a three-point flexural test. Effects of oxidation on mechanical properties of the composite were investigated by comparing the strength and failure behaviors as well as the morphologies examination. The results showed that the failure of the as-received composite was rather brittle while that of the oxidized composite showed a non-brittle pattern. Combining the oxidation analysis with a mechanical test, the result indicated that a certain extended oxidation of the PyC interphase led to an increased toughness without strength degradation due to improved interphase bonding in the SiC/PyC/SiC, namely, the composite showed mechanical self-adaptability with improved strength and toughness. The amount and length of fiber pull-out in the as-received composites were much smaller in comparison with those of oxidized composites.

Keywords

SiC/PyC/SiC oxidation mechanical property.

Get full access to this article

View all access options for this article.

References

Naslain, R. (2004). Design, Preparation and Properties of Non-oxide CMCs for Application in Engines and Nuclear Reactors: An Overview, Composite Science and Technology, 64(2): 155-170.

Schmidt, S. , Beyer, S. , Knabe, H. et al. (2004). Advanced Ceramic Matrix Composite Materials for Current and Future Propulsion Technology Applications, Acta Astronautica, 55(3-9): 409-420.

Kimmel, J. , Miriyala, N. , Price, J. , More, K. et al. (2002). Evaluation of CFCC Liners with EBC after Field Testing in a Gas Turbine, Journal of the European Ceramic Society, 22(14-15): 2769-2775.

Naslain, R. (1998). The Design of the Fibre-matrix Interfacial Zone in Ceramic Matrix Composites, Composites: Part A, 29(A): 1145-1155.

Kerans, R.J. , Hay, R.S. and Parthasarathy, T.A. (1999). Structural Ceramic Composites , Current Opinion in Solid State and Materials Science, 4: 445-451.

Takeda, M. , Sakamoto, J. , Imai, Y. and Ichikawa, H. (1999). Thermal Stability of the Low-oxygen-content Silicon Carbide Fiber, Hi-NicalonTM, Composite Science and Technology , 59(6): 813-819.

Ichikawa, H. (2000). Recent Advances in Nicalon Ceramic Fibres Including Hi-Nicalon Type S, Annales de Chimie - Science des Materiaux, 25: 523-528.

Wu, S.J. , Cheng, L.F. , Zhang, L.T. et al. (2006). Comparison of oxidation behaviors of 3D C/PyC/SiC and SiC/PyC/SiC composites in An O2-Ar Atmosphere, Materials Science and Engineering B, 130(1-3): 215-219.

Wu, S.J. , Cheng, L.F. , Zhang, L.T. et al. (2006). Oxidation Behavior of 3D Hi-Nicalon/SiC Composite, Materials Letters, 60(25-26): 3197-3201.

10.

Naslain, R. , Guette, A. , Rebillat, F. et al. (2004). Oxidation Mechanisms and Kinetics of SiC-matrix Composites and their Constituents, Journal of Materials Science, 39: 7303-7316.

11.

Evans, A.G. and Marshall, D.B. (1990). Mechanical Behavior of Ceramic Matrix Composites , In: K.S. Mazdiyasni (eds), Fiber Reinforced Ceramic Composites: Materials, Processing and Technology , pp. 1-26, Noyes Publications, Park Ridge, New Jersey.

12.

Beyerley, D. , Spearing, S.M. , Zok, F.W. and Evans, A.G. (1992). Damage, Degradation and Failure in a Unidirectional Ceramic-matrix Composite, Journal of the American Ceramic Society, 75(10): 2719-2725.