The Effect of Functionalized-TiO2 on the Mechanical Properties of PP/PA6/Functionalized-TiO2 Nanocomposites Prepared by Reactive Compatibilization Technology

Abstract

Polymeric nanocomposites consisting of the thermoplastic blend of PP and PA6 (70/30 by weight) and the varied amount of the TDI-functionalized TiO₂ nanoparticles varied from 0 to 7 phr as a compatilizer, were prepared via melt compounding method. The mechanical performances of the prepared nanocomposites are examined on injection-molded specimens in terms of the tensile and flexural tests. The results showed that the mechanical strength of the nanocomposites increases with the content of functionalized-TiO₂ and the best result is achieved when its content is 3 phr. However, for TiO₂ content to exceed 3 phr, the nanocomposites become increasingly brittle, as indicated by the decrease in both tensile and flexural strength. The enhanced mechanical strength may be attributed to improved compatibilization of PA6 in PP matrix by virtue of functionalized-TiO₂. This conclusion is strongly supported by the evidence from the SEM photographs of the fracture of the nanocomposites, where the better dispersion of the PA6 phase in the PP can be clearly observed. In addition, the dispersion of TiO ₂ in the nanocomposites was also investigated using a TEM. The result of TEM suggests that the functionalized-TiO₂ was well dispersed in the nanocomposites in a nanoscale, because the —NCO groups located at the surface of the TiO₂ can chemically associate with PA6, thus improving the compatibility between the TiO₂ and the PA6.

Keywords

TiO2 nanoparticle functionalization polypropylene/polyamide 6 blends nanocomposites.

Get full access to this article

View all access options for this article.

References

Lee, J.W. , Lim, Y.T. and Park, O.O. (2000). Thermal Characteristics of Organoclay and their Effects upon the Formation of Polypropylene/Organoclay Nanocomposites, Polymer Bulletin , 45: 191-198.

Hong, C.K. , Kim, M.J. , Oh, S.H. , Lee Y.S. and Nah, C. (2008). Effects of Polypropylene-g-(maleicanhydride/styrene) Compatibilizer on Mechanical and Rheological Properties of Polypropylene/Clay Nanocomposites, Journal of Industrial and Engineering Chemistry , 14(2): 236-242.

Park, J.H. , Lee, H.M. , Chin, I.J. , Choi, H.J. , Kim, H.K. and Kang, W.G. (2008). Intercalated Polypropylene/Clay Nanocomposite and its Physical Characteristics, Journal of Physics and Chemistry of Solids, 69(5-6): 1375-1378.

Ding, C. , He, H. , Guo, B.C. and Jia, D.M. (2008). Structure and Properties of Polypropylene/ Clay Nanocomposites Compatibilized by Solid-phase Grafted Polypropylene, Polymer Composites, 29(6): 698-701.

Monticelli, O. , Musina, Z. , Frache , A. , Bellucci, F. , Camino, G. and Russo, S. (2007). Influence of Compatibilizer Degradation on Formation and Properties of PA6/Organoclay Nanocomposites, Polymer Degradation and Stability, 92(3): 370-378.

Wilkinson, A.N. , Man, Z. , Stanford , J.L. , Matikainen, P. , Clemens, M.L. , Lees, G.C. and Liauw, C.M. (2007). Tensile Properties of Melt Intercalated Polyamide 6-Montmorillonite Nanocomposites , Composites Science and Technology, 67(15-16): 3360-3368.

Chow, W.S. , Mohd Ishak, Z.A. , Karger Kocsis, J. , Apostolov, A.A. and Ishiaku, U.S. (2003). Compatibilizing Effect of Maleated Polypropylene on the Mechanical Properties and Morphology of Injection Molded Polyamide 6/Polypropylene/Organoclay Nanocomposites, Polymer, 44: 7427-7440.

Chow, W.S. , Mohd Ishak, Z.A. , Ishiaku, U.S. , Karger-Kocsis, J. and Apostolov, A.A. (2004). The Effect of Organoclay on the Mechanical Properties and Morphology of Injection-molded Polyamide 6/Polypropylene Nanocomposites , Journal of Applied Polymer Science, 91: 175-189.

Chow, W.S. , Abu Bakar, A. , Mohd Ishak, Z.A. , Karger Kocsis, J. and Ishiaku, U.S. (2005). Effect of Maleic Anhydride-grafted Ethylene-propylene Rubber on the Mechanical, Rheological, and Morphological Properties of Organoclay Reinforced Polyamide 6/Polypropylene Nanocomposites, European Polymer Journal, 41: 687-696.

10.

Holsti Miettinen, R.M. , Perttilä, K.P. , Seppälä , J.V. and Heino, M.T. (1995). Oxygen Barrier Properties of Polypropylene/Polyamide 6 Blends, Journal of Applied Polymer Science, 58(9): 1551-1560.

11.

Li, S.X. and Liu, J.Y. (1998). Polyurethane Adhesive, Chemical Industry Press, Beijing, China, pp. 13-15.

12.

Zhang, S.L. , Zhou, J.F. , Zhang, Z.J. , Du, Z.L. , Vorontsov, A.V. and Jin, Z.S. (2000). Morphological Structure and Physicochemical Properties of Nanotube TiO2, Chinese Science Bulletin, 45(16): 1533-1536.

13.

Li, H.R. , Lin, J. , Zhang, H.J. , Fu, L.S. , Meng, Q.G. and Wang, S.B. (2002). Preparation and Uminescence Properties of Hybrid Materials Containing Europium (III) Complexes Covalently Bonded to a Silica Matrix, Chemistry of Materials, 14(9): 3651-3655.

14.

Reichert, P. , Nitz, H. , Klinke , S. , Brandsch, R. , Thomann, R. and Mülhaup, R. (2000). Poly(propylene)/Organoclay Nanocomposite Formation: Influence of Compatibilizer Functionality and Organoclay Modification, Macromolecular Materials Engineering, 275(1): 8-17.

15.

Cho, J.W. and Paul, D.R. (2001). Nylon 6 Nanocomposites by Melt Compounding, Polymer, 42(3): 1083-1094.

16.

Huang, J.C. , Zhu, Z.K. , Ma , X.D. , Qian, X.F. and Yin , J. (2001). Preparation and Properties of Montmorillonite/Organo-soluble Polyimide Hybrid Materials Prepared by a One-step Approach, Journal of Materials Science, 36: 871-877.

17.

Akkapeddi, M.K. (2000). Glass Fiber Reinforced Polyamide-6 Nanocomposites, Polymer Composites, 21(4): 576-585.

18.

Kornmann, X. , Berglund, L.A. , Sterte , J. and Giannelis, E.P. (1998). Nanocomposites Based on Montmorillonite and Unsaturated Polyester, Polymer Engineering Science, 38(8): 1351-1358.

19.

Shelley, J.S. , Mather, P.T. and DeVries, K.L. (2001). Reinforcement and Environmental Degradation of Nylon-6/Clay Nanocomposites , Polymer, 42(13): 5849-5858.

20.

Kim, G.M. , Lee, D.H. , Hoffmann , B. , Kressler, J. and Stöppelmann , G. (2001). Influence of Nanofillers on the Deformation Process in Layered Silicate/Polyamide-12 Nanocomposites, Polymer, 42(3): 1095-1100.

21.

Liu, X.H. , Wu, Q.J. , Berglund , L.A. , Fan , J.Q. and Qi , Z.N. (2001). Polyamide 6-clay Nanocomposites/Polypropylene-grafted-maleic Anhydride Alloys , Polymer, 42(19): 8235-8239.