Abstract

Many years ago, free edge effects were studied extensively, perhaps excessively, for ordinary tape laminate composites. Various techniques were used to show that the free edge effects extended only a short distance from the free edge and that stacking sequence had a significant impact on interlaminar stresses, which could cause premature failure. In contrast, the analytical study of woven composites has focused on periodic analysis of unit cells. Since such analyses assume an infinite array of unit cells, free edge effects were not considered. This article investigates the significance of traction free surfaces on stresses in woven composites. Effects due to both free edge and free lateral surfaces (due to finite thickness) were investigated. The significance of the free edge effect was found to be sensitive to the waviness of the plain weave mat. Also, the stress distribution is quite different for finite and infinitely thick stacks of woven mats.

Keywords

finite element analysis woven composite finite thickness free edge effects stacking sequence effect micromechanics.

Get full access to this article

View all access options for this article.

References

Pipes, R.B. and Pagano, N.J. ( 1970). Interlaminar Stresses in Composite Laminates Under Uniform Axial Extension, Journal of Composite Materials, 4: 538-548.

Wang, J.T. and Dickson, J.N. ( 1978). Interlaminar Stresses in Symmetric Composite Laminates , Journal of Composite Materials, 12: 390-402.

Whitcomb, J.D. and Raju, I.S. ( 1985). Analysis of Interlaminar Stresses in Thick Composite Laminates With and Without Edge Delamination, In: Johnson, W.S. (ed.), Delamination and Debonding of Materials, ASTM STP 876, pp. 69-94, American Society for Testing and Materials , Philadelphia.

Whitcomb, J.D. ( 1991). Three-dimensional Stress Analysis of Plain Weave Composites , In: O’Brien, T.K. (ed.), Composite Materials: Fatigue and Fracture, ASTM STP 1110, pp. 417-438, American Society for Testing and Materials, Philadelphia .

Whitcomb, J.D. , Chapman, C.D. and Tang, X. (2000). Derivation of Boundary Conditions for Micromechanics Analyses of Plain and Satin Weave Composites , Journal of Composite Materials, 34(9): 724-747.

Goyal, D. , Tang, X. , Whitcomb, J.D. and Kelkar, A. ( 2005). Effect of Various Parameters on Effective Engineering Properties of 2×2 Braided Composites, Mechanics of Advanced Materials and Structures, 12(2): 113-128.