Experimental Study on Crack Defects Formation in Polyarylacetylene Composites and Modification Improvement of Resin

Abstract

Polyarylacetylene (PAA) resin is one among the ideal ablation materials, due to its high char yield and has been used to fabricate composite structures for solid rockets and missiles. However, the manufacturing quality of PAA composite is difficult to control. This article aims to reveal the formation mechanism of crack defect for PAA composite and presents an improvement method by resin modification. In this article, crack features and formation process of quartz fiber reinforced PAA composite were first studied, and the shrinkage and brittleness of PAA resin were evaluated to analyze the reason for crack formation. Furthermore, PAA resin modified by blending with phenolic resin was developed to reduce the crack defect. It is found that large curing shrinkage and extreme brittleness are the main reasons, which result in crack defect and poor mechanical performances of PAA. Moreover, PAA and phenolic (PF) blend was proved to be effective in raising ductility and reducing shrinkage, leading to the reduction of crack defect. Besides, the interlaminar shear strength of quartz fiber/PAA-PF blend composite increased twice as compared with quartz fiber/PAA composite.

Keywords

polyarylacetylene quartz fiber crack defect interfacial performance phenolic.

Get full access to this article

View all access options for this article.

References

Buvat, P. , Jousse, F. , Delnaud, L. and Levassort, C. ( 2001). Synthesis and Properties of New Processable Type Polyarylacetylenes , In: International SAMPE Symposium and Exhibition (Proceedings), Long Beach, USA, Vol. 46, pp. 134-144.

Sreejith, P.S. , Krishnamurthy, R. , Narayanasamy, K. and Malhotra, S.K. (1999). Studies on the Machining of Carbon Phenolic Ablative Composites, Journal of Materials Processing Technology, 88: 43-50.

Yan, L. , Zhang, X. , Li, H. and Cui, H. ( 2007). Carbon Cloth Reinforced Polyarylacetylene Ablative Materials , Journal of Advanced Materials, 39(3): 22-25.

Ishikawa, T. , Yamada, T. , Yokota, R. , Itoh, M. and Nogi, S. (2002). Thermal Response and Ablation Characteristics of Carbon Fiber Reinforced Composite with Novel Silicon Containing Polymer MSP, Journal of Composite Materials, 36(2): 143-157.

Zaldivar, R.J. ( 1992). Fundamental Studies on the Microstructural and Mechanical Behavior of Polyarylacetylene-derived Carbon/Carbon Composites, PhD Dissertation , University of California, Los Angeles.

Njugunal, J. , Pielichowski, K. and Desai, S. (2008). Nanofiller-reinforced Polymer Nanocomposites, Polymers for Advanced Technologies , 19: 947-959.

Zaldivar, R.J. , Rellick, G.S. and Yang, J.M. (1991). Processing Effects on the Mechanical Behavior of Polyarylacetylene-derived Carbon/Carbon Composites , SAMPE Journal, 27(5): 29-36.

Zaldivar, R.J. , Kobayashi, R.W. , Rellick, G.S. and Yang, J.M. (1991). Carborane-catalyzed Graphitization in Polyarylacetylene-derived Carbon-Carbon Composites, Carbon, 29(8): 1145-1153.

Sheaffer, G.A. and Katzman, H. ( 1991). Polyarylacetylene Adhesives for Carbon-Carbon Composites , In: Extended Abstracts and Program - Biennial Conference on Carbon, Santa Barbara, CA, 23-28 June.

10.

Zhang, X. , Huang, Y. , Wang, T. and Liu, L. ( 2006). Effects of Polyhedral Oligomeric Silsesquioxane Coatings on the Interface and Impact Properties of Carbon-Fiber/ Polyarylacetylene Composites, Journal of Applied Polymer Science, 102: 5202-5211.

11.

Zhang, X. , Huang, Y. , Wang, T. and Liu, L. ( 2007). Influence of Fiber Surface Oxidation-Reduction Followed by Silsesquioxane Coating Treatment on Interfacial Mechanical Properties of Carbon Fiber/Polyarylacetylene Composites, Composites Part A, 38: 936-944.

12.

Katzman, H.A. , Mallon, J.J. and Barry, W.T. (1995). Polyarylacetylene-Matrix Composites for Solid Rocket Motor Components, Journal of Advanced Materials, 4: 21-27.

13.

Wang, M. and Zhao, T. ( 2007). Polyarylacetylene Blends with Improved Processability and High Thermal Stability, Journal of Applied Polymer Science , 105: 2939-2946.

14.

Zhang, X. , Huang, Y. and Wang, T. ( 2007). Plasma Activation of Carbon Fibres for Polyarylacetylene Composites, Surface and Coatings Technology, 201: 4965-4968.

15.

Zhang, X.Z. , Song, Y.J. and Huang, Y.D. (2007). Properties of Silsesquioxane Coating Modified Carbon Fibre/Polyarylacetylene Composites, Composites Science and Technology, 67: 3014-3022.

16.

Liu, L. , Song, Y.J. , Fu, H.J. , Jiang, Z.X. , Zhang, X.Z. , Wu, L.N. and Huang, Y.D. (2008). The Effect of Interphase Modification on Carbon Fiber/Polyarylacetylene Resin Composites, Applied Surface Science, 254: 5342-5347.

17.

Jiang, Z.X. , Meng, L.H. , Huang, Y.D. , Liu, L. and Lu, C. ( 2007). Influence of Coupling Agent Chain Lengths on Interfacial Performances of Polyarylacetylene Resin and Silica Glass Composites, Applied Surface Science, 253: 4338-4343.

18.

Jiang, Z.X. , Huang, Y.D. , Liu, L. and Long, J. ( 2007). Effects of Roughness on Interfacial Performances of Silica Glass and Non-polar Polyarylacetylene Resin Composites, Applied Surface Science, 253: 9357-9364.