Flat-pressed Wood Plastic Composite as an Alternative to Conventional Wood-based Panels

Abstract

This study evaluated physical and mechanical properties of the wood plastic composite panels made from dry-blended rubberwood fiber-polypropylene (PP) powder formulations using a conventional flat-press process under laboratory conditions. Three levels of rubberwood fibers (Hevea brasiliensis), 40%, 50%, and 60% based on the composition by weight, were mixed with the PP powder without and with 3% (based on weight) maleic anhydride grafted PP (MAPP) as a coupling agent. Water resistance of the panels was negatively influenced by the increasing wood fiber content. The modulus of rupture of the panels significantly increased with the increase in the wood fiber content from 40 to 50 wt% and then decreased as the fiber content reached 60 wt% but this decrease was not significant. The modulus of elasticity of the panels increased with the increase in fiber content from 40 to 60 wt%. Internal bond strength and screw withdrawal resistance declined with the increase in fiber content from 40% to 60 wt%. The formulations with MAPP were found to have higher strength and better water resistance.

Keywords

hot press molding polypropylene reinforced thermoplastic rubberwood water resistance wood plastic composite.

Get full access to this article

View all access options for this article.

References

Clemons, C.M. (2002). Wood-Plastic Composites in the United States: The Interfacing of Two Industries, Forest Products Journal, 52(6): 10-18.

Chaharmahali, M. , Mirbagheri, J. , Tajvidi , M. , Najafi, S.K. and Mirbagheri , Y. (2010). Mechanical and Physical Properties of Wood-Plastic Composite Panels , Journal of Reinforced Plastics and Composites, 29: 310-319.

Jarusombuti, S. and Ayrilmis, N. (2010). Surface Characteristics and Overlaying Properties of Flat-pressed Wood Plastic Composites, European Journal of Wood and Wood Products (in press).

Hiziroglu, S. , Jarusombuti, S. and Vallayuth, F. (2004). Surface Characteristics of Wood Composites Manufactured in Thailand, Building and Environment, 39(11): 1359-1364.

EN 317. (1993). Particleboards and Fiberboards - Determination of Swelling in Thickness After Immersion in Water, European Committee for Standardization, Brussel, Belgium.

EN 323. (1993). Wood-based Panels - Determination of Density, European Committee for Standardization , Brussel, Belgium.

EN 310. (1993). Determination of Modulus of Elasticity in Bending and Bending Strength, European Committee for Standardization, Brussel, Belgium .

EN 319. (1993). Particleboards and Fiberboards - Determination of Tensile Strength Perpendicular to the Plane of the Board, European Committee for Standardization, Brussel, Belgium.

EN 320. (1993). Fiberboards - Determination of Resistance to Axial Withdrawal of Screw, European Committee for Standardization, Brussel, Belgium .

10.

EN 312. (2003). Particleboards - Specifications, European Committee for Standardization , Brussel, Belgium.

11.

EN 622-5. (2006). Fiberboards Specifications - Requirements for Dry Process Boards (MDF), European Committee for Standardization, Brussel, Belgium .

12.

Akbulut, T. , Goker, Y. and Ayrilmis, N. (2002). Using OSB Panels Instead of Plywood, Review of the Faculty of Forestry: Part A, Istanbul University, 52(1): 65-79.

13.

Ayrilmis, N. ( 2000). The Effect of Tree Species on Technological Properties of MDF, MSc Thesis, Institute of Natural Sciences, Istanbul University, p. 256.

14.

Adhikary, K.B. , Pang, S. and Staiger, M.P. (2008). Dimensional Stability and Mechanical Behaviour of Wood-Plastic Composites Based on Recycled and Virgin High-density Polyethylene (HDPE), Composites Part B: Engineering, 39(5): 807-815.

15.

Gupta, B.S. , Reiniati, I. and Laborie, M.P.G. (2007). Surface Properties and Adhesion of Wood Fiber Reinforced Thermoplastic Composites , Colloids and Surfaces A: Physicochemical and Engineering Aspects, 302(1-3): 388-395.

16.

Inagaki, N. ( 1996). Plasma Surface Modification and Plasma Polymerization , Technomic Publication Company , Lancaster.

17.

Youngquist, J.A. (1999). Wood-Based Composites and Panel Products, Wood Handbook: Wood as an Engineering Material, General Technical Report FPL-GTR-113, Ch. 10, pp. 10.1-10.31, United States Department of Agriculture, Forest Service, Forest Products Laboratory, Madison WI.

18.

Chaharmahali, M. , Tajvidi, M. and Najafi, S.K. (2008). Mechanical Properties of Wood Plastic Composite Panels made from Waste Fiberboard and Particleboard , Polymer Composites, 29(6): 606-610.

19.

Caulfield, D.F. , Clemons, C. , Jacobson , R.E. , Rowell, R.M. (2005). Wood Thermoplastic Composites, In: Rowell, R.M. (ed.), Handbook of Wood Chemistry and Wood Composites , Ch. 13, pp. 365-380, CRC Press , Boca Raton.

20.

Nourbakhsh, A. and Ashori, A. (2009). Preparation and Properties of Wood Plastic Composites made of Recycled High-Density Polyethylene , Journal of Composite Materials, 43(8): 877-883.

21.

Maloney, T.M. (1977). Modern Particleboard and Dry-Process Fiberboard Manufacturing, Miller Freeman Publications , San Francisco.

22.

Walker, J. ( 2004). Primary Wood Processing: Principles and Practice , 2nd edn, Springer, Dordrecht.

23.

ANSI A208.2. (2002). Medium Density Fiberboard (MDF) for Interior Applications, American National Standards Institute, Gaithersburg .

24.

Falk, R.H. , Vos, D.G. , Cramer, S.M. and English, B.W. ( 2001). Performance of Fasteners in Wood Flour-Thermoplastic Composite Panels, Forest Products Journal, 51(1): 55-61.

25.

Razi, P.S. , Portier, R. and Raman, A. ( 1999). Studies on Polymer-Wood Interface Bonding: Effect of Coupling Agents and Surface Modification, Journal of Composite Materials, 33(12): 1064-1079.