PLA/clay/wood nanocomposites: nanoclay effects on mechanical and thermal properties

Abstract

Poly(lactic acid) (PLA)/clay/wood nanocomposites were prepared by melt extrusion of PLA, nanoclay, and wood flour (WF). The clay particles exhibit an intercalated structure in the PLA matrix and the addition of WF slightly increases the spacing in the galleries of the intercalated structure. The intercalated clay particles and WF in the PLA matrix restrict the motion of the PLA molecules and crystals. The tensile and flexural moduli of PLA/clay/wood nanocomposites with 30 wt% WF, respectively, increase from 3.75 to 7.08 GPa and from 3.83 to 6.01 GPa compared to neat PLA by adding up to 5 wt% nanoclay. Voids around clay particles, observed via scanning electron microscopy are associated with the negative effect of the clay particles on the interfacial adhesion between the WF and the PLA matrix. Clay particles improve the thermal decomposition temperature (T_d) of PLA/clay/wood nanocomposites by about 10^°C compared to that of PLA/wood composites. The effects of clay particles on other thermal properties such as glass transition temperature (T_g), melting temperature (T_m), and linear thermal expansion are also discussed in this article.

Keywords

poly(lactic acid)nanoclay wood nanocomposite material properties

Get full access to this article

View all access options for this article.

References

Andreopoulos AG , Hatzi E. and Doxastakis M. Synthesis and properties of poly(lactic acid) . J Mater Sci: Mater Med 1999; 10: 29-33.

Baiardo M. , Frisoni G. , Scandola M. , Rimelen M. , Lips D. , Ruffieux K. , et al. Thermal and mechanical properties of plasticized poly(L-lactic acid). J Appl Polym Sci 2003; 90: 1731-1738.

Bandyopadhyay S. , Chen R. and Giannelis EP Biodegradable organic-inorganic hybrids based on poly(L-lactide). Polymer 1999; 81: 159-160.

Celli A. and Scandola M. Thermal-properties and physical aging of poly(l-lactic acid). Polymer 1992; 33: 2699-2703.

Chang JH , An YU , Cho D. and Giannelis EP Polylactide nanocomposites: comparison of their properties with montmorillonite and synthetic mica (II). Polymer 2003; 44: 3715-3720.

De Oca HM and Ward IM Structure and mechanical properties of poly(L-lactic acid) crystals and fibers. J Polym Sci Part B-Polym Phys 2007; 45: 892-902.

Feng JT , Sui JH , Cai W. and Gao ZY Microstructure and mechanical properties of carboxylated carbon nanotubes/poly(L-lactic acid) composite. J Compos Mater 2008; 42: 1587-1595.

Ray SS and Bousmina M. Biodegradable polymers and their layered silicate nanocomposites: in greening the 21st century materials world. Prog Mater Sci 2005; 50: 962-1079.

Huda MS , Drzal LT , Misra M. and Mohanty AK Woodfiber-reinforced poly(lactic acid) composites: evaluation of the physicomechanical and morphological properties. J Appl Polym Sci 2006; 102: 4856-4869.

10.

Lee SH and Wang SQ Biodegradable polymers/bamboo fiber biocomposite with bio-based coupling agent . Compos Part A 2006; 37: 80-91.

11.

Lee S-Y. , Kang I-A. , Don G-H. , Yoon H-G. , Park B-D. and Wu Q. Thermal and mechanical properties of wood flour/ talc-filled polylactic acid composites: effect of filler content and coupling treatment. J Thermoplast Compos Mater 2008; 21: 209-223.

12.

Lin LH , Liu HJ and Yu NK Morphology and thermal properties of poly(L-lactic acid)/organoclay nanocomposites . J Appl Polym Sci 2007; 106: 260-266.

13.

Murariu M. , Ferreira AD , Degee P. , Alexandre M. and Dubois P. Polylactide compositions. Part 1: effect of filler content and size on mechanical properties of PLA/ calcium sulfate composites. Polymer 2007; 48: 2613-2618.

14.

Paul MA , Alexander M. , Degee P. , Henris C. , Rulmont A. and Dubois P. New nanocomposite materials based on plasticized poly(L-lactide) and organo-modified montmorillonites: thermal and morphological study. Polymer 2003; 44: 443-450.

15.

Pilla S. , Gong S. , O’Neill E. , Rowell RM and Krzysik AM Polylactide-pine wood flour composites. Polym Eng Sci 2008; 48: 578-587.

16.

Pluta M. , Jeszka JK and Boiteux G. Polylactide/montmorillonite nanocomposites: structure, dielectric, viscoelastic and thermal properties. Eur Polym J 2007; 43: 2819-2835.

17.

Graupner N. , Herrmann AS and Mussig J. Natural and man-made cellulose fibre-reinforced poly(lactic acid) (PLA) composites: an overview about mechanical characteristics and application areas. Composites Part A 2009 ; 40: 810-821.

18.

Krishnamachari P. , Zhang J. , Lou JZ , Yan JZ and Uitenham L. Biodegradable poly(lactic acid)/clay nanocomposites by melt intercalation: a study of morphological, thermal, and mechanical properties . Int J Polym Anal Charact 2009; 14: 336-350.

19.

Bledzki AK and Gassan J. Composites reinforced with cellulose based fibers. Prog Polym Sci 1999; 24: 221-274.

20.

Wu CS and Liao HT Modification of biodegradable polylactide by silica and wood flour through a sol-gel process. J Appl Polym Sci 2008; 109: 2128-2138.

21.

Ogata N. , Jimenez G. , Kawai H. and Ogihara T. Structure and thermal/mechanical properties of poly(l-lactide)-clay blend . J Polym Sci Part B - Polym Phys 1997; 35: 389-396.

22.

Krikorian V. and Pochan DJ Poly(L-lactic acid)/layered silicate nanocomposite: fabrication, characterization, and properties. Chem Mater 2003; 15: 4317-4324.

23.

Pluta M. Morphology and properties o polylactide modified by thermal treatment, filling with layered silicates and plasticization. Polymer 2004; 45: 8239-8251.

24.

Ray SS , Maiti P. , Okamot M. , Yamada K. and Ueda K. New polylactide/layered silicate nanocomposites. 1 preparation, characterization, and properties. Macromolecules 2002; 35: 3104-3110.

25.

Ray SS , Okamoto K. , Yamada K. and Okamot M. Novel porous ceramic material via burning of polylactide/layered silicate nanocomposite. Nano Lett 2002; 2: 423-425.

26.

Ray SS , Yamada K. , Okamot M. , Fujimoto Y. , Ogami A. and Ueda K. New polylactide/layered silicate nanocomposites. 5 designing of materials with desired properties. Polym Compos 2003 ; 44: 6633-6646.

27.

Ray SS , Yamada K. , Okamot M. , Ogami A. and Ueda K. New polylactide/layered silicate nanocomposites. 3 high-performance biodegradable materials. Chem Mater 2003; 15: 1456-1465.

28.

Ray SS , Yamada K. , Okamot M. , Ogami A. and Ueda K. New polylactide/layered silicate nanocomposites. 4 structure, properties and biodegradability. Compos Interfaces 2003; 10: 435-450.

29.

Ray SS , Yamada K. , Okamot M. and Ueda K. New polylactide-layered silicate nanocomposites. 2 concurrent improvements of materials properties, biodegradability and melt rheology. Polym Compos 2003; 44: 857-866.

30.

Ray SS , Yamada K. , Okamoto M. and Ueda K. Polylactide-layered silicate nanocomposite: a novel biodegradable material . Nano Lett 2002; 2: 1093-1096.

31.

Shibata M. , Someya Y. , Orihara M. and Miyoshi M. Thermal and mechanical properties of plasticized poly(L-lactide) nanocomposites with organo-modified montmorillonites. J Appl Polym Sci 2006; 99: 2594-2602.

32.

Ludvik CN , Glenn GM , Klamczynski AP and Wood DF Cellulose fiber/bentonite clay/biodegradable thermoplastic composites. J Polym Environ 2007; 15: 251-257.

33.

Serna C. , Ahlrichs JL and Serratosa JM Folding in sepiolite crystals. Clays Clay Miner 1975; 23: 119-124.

34.

Dinwoodie JM Wood: nature’s cellular polymeric fiber-composite. London: The Institute of Metals, 1989.

35.

English BW and Falk RH Factors that affect the application of wood fiber-plastic composites. Madison, WI: Forest Products Society, 1995.

36.

Kazayawoko M. and Balatinecz JJ Surface modification and adhesion mechanisms in woodfiber-polypropylene composits. J Mater Sci 1999; 34: 6189-6199.

37.

Cornelissen T. , Yperman J. , Reggers G. , Schreurs S. and Carleer R. Flash co-pyrolysis of biomass with polylactic acid. Part 1: Influence on bio-oil yield and heating value. Fuel 2008; 87: 1031-1041.

38.

Paul MA , Delcourt C. , Alexandre D. , Degee P. , Monteverde F. and Dubois P. Polylactide/montmorillonite nanocomposites: study of the hydrolytic degradation . Polym Degrad Stab 2005; 87: 535-542.

39.

Bandyopadhyay S. , Chen R. and Giannelis EP Biodegradable organic-inorganic hybrids based on poly(L lactic acid). Polym Mater Sci Eng 1999; 81: 159-160.

40.

Kopinke FD , Remmler M. , Mackenzie K. , Moder M. and Wachsen O.

Thermal decomposition of biodegradable polyesters-II. Poly(lactic acid)

Polym Degrad Stab 1996; 53: 329-342.

41.

Suming L. Hydrolytic degradation characteristics of aliphatic polyesters derived from lactic and glycolic acids. J Biomed Mater Res 1999; 48: 342-353.

42.

Wang G. and Li A. Thermal decomposition and kinetics of mixtures of polylactic acid and biomass during copyrolysis. Chin J Chem Eng 2008; 16: 929-933.