A comparison study on creep behavior of wood–plastic composite,solid wood,and polypropylene

Abstract

In this study, creep/recovery behavior of wood flour/polypropylene (PP) composite was compared with solid wood and PP. Wood flour–PP composite samples (strips with 10 mm thickness and 70 mm width) were made using a laboratory twin-screw extruder. Short-term flexural creep tests at 30% of ultimate bending load were performed using flexural creep equipment. Total time to complete every test was 120 min (60 min creep and 60 min recovery). Creep parameters (relative creep, fractional deflection, creep rate, etc.) were measured for all creep test samples. The result showed that the relative creep in wood–plastic composite (WPCs, with or without coupling agent) is significantly higher than solid wood and lower than PP. Also, it was observed that the creep rate in WPC (with or without coupling agent) is significantly lower than plastic, but is approximately equal to solid wood. The use of coupling agent decreased relative creep and fractional deflection in wood flour–PP composite panels. Findley creep model predicted creep strain with a high acceptable accuracy for studied materials.

Keywords

Wood–plastic composites flexural creep solid wood polypropylene

Get full access to this article

View all access options for this article.

References

Bengtsson

Oksman

. Silan cross linked wood plastic composite: processing and properties. Compos Sci Technol 2006; 66: 2177–2186.

Kobbe RG. Creep behavior of wood polypropylene composite. Master's thesis, Department of Civil and Environmental Engineering, Washington State University, Washington, August 2005, p.96.

Alvarez

Kenny

Vazquez

. Creep behavior of biocomposites based on sisal fiber reinforced cellulose derivatives/starch blends. Polym Compos 2004; 25(3): 280–288.

Park

Balatinez

. Short term flexural creep behavior of wood-fiber/polypropylene composites polymer composites. Polym Compos 1998; 1(4): 377–382.

Pomeroy

. Creep in engineering materials. London: Mechanical Engineering Publications Ltd, 1978.

Tissaoui J. Effects of long-term creep on the integrity of modern wood structures. PhD dissertation, Faculty of the Virginia Polytechnic Institute and State University, Virginia, December 1996, p.121.

American Society for Testing and Materials. Standard guide for evaluating mechanical and physical properties of wood–plastic composite products ASTM D 7031–04. West Conshohocken, PA: ASTM, 2004.

American Society for Testing and Materials. Standard test methods for small clear specimens of timber ASTM D 143–94. West Conshohocken, PA: ASTM, 2004.

American Society for Testing and Materials. Standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating materials ASTM D 790–03. West Conshohocken, PA: ASTM, 2004.

10.

Perez

Alvarez

Vazquez

. Creep behavior of layered silicate/starch-polycaprolactone blendes nanocomposites. Mater Sci Eng A 2008; 480: 259–265.

11.

Findley

. Mechanisms and mechanics of creep of plastics. SPEJ 1960; 16: 57–65.

12.

Sain

Balatinez

Law

. Creep fatigue in engineered wood fiber and plastic composition. J Appl Polym Sci 2000; 77: 260–268.

13.

Simonsen

Rochefort

. Mechanical properties and creep resistance in polystyrene/polyethylene blends. J Appl Polym Sci 2000; 76: 1100–1108.

14.

Lin

Pramanick

Sain

. Determination of material constants for nonlinear viscoelastic predictive model. J Compos Mater 2004; 38(1): 19–29.

15.

Hattotouwa

Premala

Ismail

Baharin

. Comparison of the mechanical properties of rice husk powder filled polypropylene composites with talc filled polypropylene composites. Polym Test 2002; 21(7): 833–839.

16.

Yang

Kim

Son

Lee

Hwang

. Rice-husk flour filled polypropylene composites. Mechanical and morphological study. Compos Struct 2004; 63(3): 305–312.

17.

Mcnabb

JRHS

. Chemical coupling in wood fiber and polymer composites. A review of coupling agents and treatments. Wood Fiber Sci 2000; 32(1): 88–104.

18.

Negluescu

. Influence of maleation on polymer adsorption and fixation, wood surface wetability and interfacial bonding strength in wood-PVC composites. Wood Fiber Sci 2002; 34(3): 434–459.

19.

Kazemi Najai

Mostafazadeh

Charmahali

Tajvidi

. The effect of filler content and water absorption on creep behavior of HDPE waste/MDF flour composites. Iran J Polym Sci Technol (Persian) 2008; 21: 53–59.

20.

Lee

Yang

Kim

Jong

Lim

Lee

. Creep behavior and manufacturing parameters of wood flour filled polypropylene composite. Compos Struct 2004; 65: 459–469.

21.

Brant WC. Load duration behavior of extruded wood plastic composite. Master's thesis, Department of Civil and Environmental Engineering, Washington State University, Washington, August 2001, p.221.

22.

Bledzki

Faruk

. Creep and impact properties of wood fiber-polypropylene composite: influence of temperature and moisture content. Compos Sci Technol 2004; 64: 693–700.