Determining the through-thickness properties of thick glass fiber reinforced polymers at high strain rates

The use of thick fiber reinforced polymer (FRP) laminates in composite armor and naval structures requires thorough characterization of the through-thickness properties of said laminates, both quasi-statically and at high strain rates. Specimens cut from an E-Glass/vinyl ester FRP were tested in compression both quasi-statically and dynamically using a split Hopkinson pressure bar (SHPB). The SHPB tests utilized a conical striker for pulse shaping, to reduce the variation in strain rate during the test. The quasi-static through-thickness compressive strength was 417 MPa, while the SHPB tests produced a strength of 462 MPa at an average strain rate of 5.1 × 10² s⁻¹. A single HPB configured for spalling tests was used to determine the dynamic through-thickness tensile strength (interlaminar tension). The interlaminar tensile strength was 125 MPa at an average strain rate of 1.8 × 10³ s⁻¹.