In this study, Al–Cu-based three-layered metal matrix composites reinforced with TiC particles were produced successfully by a conventional hot pressing method under argon (Ar) atmosphere. To evaluate the effect of heat treatment, the composites were treated for 24 h at 530°C and then aged in an oil bath at 180°C for various aging periods. The multi-layered composite was characterized by SEM, EDS, XRD, and the Vickers microhardness test. It was concluded that the peak hardness for the multi-layered composite was observed, when the aging period was extended up to approximately 12 h. The hardness of the middle layer increased from approximately 140 to 291 HV within 12 h. The corrosion resistance of the composites decreased with increasing aging time and some preferential corrosion attack was detected in the composite layers. In addition, it was found that the pitting susceptibility of unaged composites was also higher than that of all the aged specimens.
DikiciBGavgaliMTekmenC. Corrosion behavior of an artificially aged (T6) Al-Si-Mg based metal matrix composite. J Compos Mater2006; 40(14): 1259–1269.
2.
BedirF. Characteristic properties of Al–Cu–SiCp and Al–Cu–B4Cp composites produced by hot pressing method under nitrogen atmosphere. Mater Des2007; 28: 1238–1244.
3.
da SilvaAntonio AMdos SantosJorge FStrohaeckerTelmo R. Microstructural and mechanical characterisation of a Ti6Al4V/TiC/10p composite processed by the BE-CHIP method. Compos Sci Technol2005; 65(11-12): 1749–1755.
4.
HudaMDHashmiMSJEl-BaradieMA. MMCs: Materials, manufacturing and mechanical properties. Key Eng Mater1995; 104–107: 37–64.
PengLMLiHWangJH. Processing and mechanical behavior of laminated titanium–titanium tri-aluminide (Ti–Al3Ti) composites. Mater Sci Eng A2005; 406(1–2): 309–318.
HwuKLDerbyB. Fracture of metal/ceramic laminates—II. Crack growth resistance and toughness. Acta Mater1999; 47(2): 545–563.
10.
ZhuH. Reactive processing and characterization of nickel aluminide-alumina functionally gradient composites. PhD Dissertation, University of Florida, 1999, 1–5.
11.
LiuGZhuDShangJK. Temperature dependence of fracture toughness in TiC-particulate reinforced Ti-1b6Al-1b4V matrix composite. Scr Metall1993; 28(6): 729–732.
GavgaliMDikiciBBedirF. Corrosion susceptibilities of Al—Cu/TiC MMCs fabricated by conventional hot pressing. Ind J Eng Mater Sci2007; 14: 303–308.
14.
AashishRDavidJHKennethSVKennethPH. Resistance-curve and fracture behavior of Ti–Al3Ti metallic–intermetallic laminate (MIL) composites. Acta Metall2003; 51(10): 2731–3036.
15.
TiezhengLGrignonFBensonDJVecchioKSOlevskyEAJiangF. Modeling the elastic properties and damage evolution in Ti–Al3Ti metal–intermetallic laminate (MIL) composites. Mater Sci Eng A2004; 374(1–2): 10–26.
16.
SrivatsanTSIbrahimIAMohamedFALaverniaEJ. Processing techniques for particulate-reinforced aluminium metal matrix composites. J Mater Sci1991; 26: 5965–5978.
17.
BedirF. Fabrication of two-layered Al-B4C composites by conventional hot pressing under nitrogen atmosphere and their characterization. J Mech Sci Technol2006; 20(7): 1002–1011.
18.
KayaG. Mechanical Properties of PM Al-SiC composites produced by conventional hot-pressing method. Master Thesis, Middle East Technical University, 1999, 1–80.
19.
Tsangaraki-KaplanoglouITheohariSDimogerontakisTYar-MingWHong-Hsiang(Harry) KSheilaK. Effect of alloy types on the anodizing process of aluminium. Surf Coat Technol2006; 200: 2634–2641.
20.
TrowsdaleAJNobleBHarisSJGibbinsISRThompsonGEWoodGC. The influence of silicon carbide reinforcement on the pitting behaviour of aluminium. Corros Sci1996; 38(2): 177–191.
21.
GavgaliMDikiciBTekmenC. The effect of SiCp reinforcement on the corrosion behaviour of Al based metal matrix composites. Corros Rev2006; 24(1–2): 27–37.
22.
TrzaskomaPPMcCaffertyECroweCR. Corrosion behavior of SiC/Al metal matrix composites. J Electrochem Soc1983; 130(9): 1804–1809.
23.
DikiciBKiyakTTekmenCGavgaliM. SEM observations on the porosity activities during corrosion of Al–Si–Mg/SiCp metal matrix composites. Mater Sci Ind J2007; 3(1): 8–12.
24.
Fratila-ApachiteiLETerrynHSkeldonPThompsonGEDuszczykJKatgermanL. Influence of substrate microstructure on the growth of anodic oxide layers. Electrochim Acta2004; 49(7): 1127–1140.
25.
DikiciBBedirFGavgaliMKiyakT. Corrosion characteristics of Al-Cu/B4C (T6) MMCs and their microstructure evaluaton. Kovove Mater2009; 47(5): 317–323.
26.
DikiciBGavgaliMBedirF. Synthesis of in-situ TiC nanoparticles in liquid aluminum: The effect of sintering temperature. J Compos Mater2011; 45(8): 895–900.
27.
TekmenCCocenU. The effect of Si and Mg on age hardening behaviour of Al-SiCp composites. J Compos Mater2003; 37(20): 1791–1800.
28.
BedirFÖgelB. TiC ve SiC Katkılı Kompozitlerin Azot Atmosferi Altında Sıcak Preslenmesi. 10. Uluslararası Metalurji ve Malzeme Kongresi Bildiriler Kitabı. İstanbul2000; 3: 1713–1721.
29.
KimSWLeeUJHanSWKimDKOgiK. Heat treatment and wear characteristics of Al/SiCp composites fabricated by duplex process. Composites Part B2003; 34: 737–745.
30.
SalvadorMDAmigóVMartinezNBusquetsDJ. Microstructure and mechanical behaviour of Al–Si–Mg alloys reinforced with Ti–Al intermetallics. J Mater Process Technol2003; 143-144: 605–611.
31.
DasTMunroePRBandyopadhyayS. Effect of Al2O3 Particulates on the Precipitation Behavior of 6061 aluminum-matrix composites. J Mater Sci1996; 31(20): 5351–5361.
32.
McIntyreJFConradRKGolledgeSL. The effect of heat treatment on the pitting behaviour of SiCw/AA2124. Corrosion1990; 46(11): 902–905.
33.
De SalazarJMGUrenaAManzanedoSBarrenaMI. Corrosion behaviour of AA6061 and AA7005 reinforced with Al2O3 particles in aerated 3.5% chloride solutions: Potentiodynamic measurements and microstructure evaluation. Corros Sci1999; 41: 529–545.
34.
TurnbullA. Review of corrosion studies on aluminium metal matrix composites. Br Corros J1992; 27(1): 27–35.
35.
HollingsworthEHHunsickerYH. Corrosion of aluminum and aluminum alloys1987; 13, Ohio/USA: ASM Handbook, 583–609.
36.
LucasKAClarkeH. Corrosion of aluminium-based metal matrix composites. Research Studies Pres Ltd, 1993; England, 1–137.
YaghmaeeMSKaptayG. On the stability range of SiC in ternary liquid Al-Si-Mg alloy. Materials Worlds: Proceedings of Hungarian Materials Science Society 2001; 2(3), e-journal with ISSN 1586-0140, from http://materialworld.fw.hu.
39.
HiharaLHLatanisionRM. Galvanic corrosion of aluminum-matrix composites. Corrosion1992; 48(7): 546–552.
40.
KiourtsidisGSkolianosSM. Corrosion behavior of squeeze-cast silicon carbide-2024 composites in aerated 3.5 wt.% sodium chloride. Mater Sci Eng A1998; 248: 165–172.
41.
GalveleJR. Tafel’s law in pitting corrosion and crevice corrosion susceptibility. Corros Sci2005; 47: 3053–3067.
42.
SeguradoJGonzalezCLlorcaJ. A numerical investigation of the effect of particle clustering on the mechanical properties of composites. Acta Mater2003; 51: 2355–2369.
43.
OzdemirITekmenCToparliM. Recrystallization and particle growth in Al-based SiC particle-reinforced composites. Metallkd2003; 94(1): 41–43.
44.
TrzaskomaPP. Pit morphology of aluminum alloy and silicon carbide/aluminum alloy metal matrix composites. Corrosion1990; 46(5): 402–409.
45.
AhmedZAbdul AleemBJ. Degradation of aluminum metal matrix composites in salt water and its control. Mater Des2002; 23: 173–180.