In this study, the buckling and compressive failure of adhesively-bonded stepped-lap joints (with/without composite patches) composed of pultruded glass fiber-reinforced polymer composite laminates was investigated experimentally and numerically. Two-component epoxy adhesive was used for bonding purposes. Composite patches were woven glass-epoxy layer. They were added onto the conventional stepped-lap joints so that additional load transfer paths were created and localized stress concentrations near joint edge were reduced. The axial compression tests were performed and the results revealed that the buckling and failure load of new stepped lap composite joints with composite patches were significantly higher than the conventional stepped lap joints. The influence of the overlap length was evaluated. For both types of joints, a small increase was observed in failure loads by increase of the overlap length. Numerical results showed a very good agreement with experimental results.
SahaMPrabhakaranRWatersWA. Compressive behavior of pultruded composite plates with circular hole. Compos Struct2006; 65: 29–36.
2.
ParkYBSongMGKimJJ. Strength of carbon/epoxy composite single-lap bonded joints in various environmental conditions. Compos Struct2009; 92: 2173–2180.
3.
AvilaAFBuenoPO. An experimental and numerical study on adhesive joints for composites. Compos Struct2004; 64: 531–537.
4.
HerSC. Stress analysis of adhesively-bonded lap joints. Compos Struct1999; 47: 673–678.
5.
BanCSLeeYHChoiJH. Strength prediction of adhesive joints using the modified damage zone theory. Compos Struct2008; 86: 96–100.
6.
LiGLee-SullivanPThringRW. Nonlinear finite element analysis of stress and strain distributions across the adhesive thickness in composite single-lap joints. Compos Struct1999; 46: 395–403.
7.
SongMGKweonJHChoiJH. Effect of manufacturing methods on the shear strength of composite single-lap bonded joints. Compos Struct2010; 92: 2194–2202.
8.
NakanoKSawaTTorataniH. A two-dimensional stress analysis of single-lap adhesive joints subjected to tensile loads. J Adhes Sci Technol1997; 11: 1039–1062.
9.
ReisPNBAntunesFJVFerreiraJAM. Influence of superposition length on mechanical resistance of single-lap adhesive joints. Compos Struct2005; 67: 125–133.
10.
TsaiMYMortonJ. The effect of a spew fillet on adhesive stress distributions in laminated composite single-lap joints. Compos Struct1995; 32: 123–31.
HiguchiISawaTOkunoH. Three-dimensional finite element analysis of stress response in adhesive butt joints subjected to impact tensile loads. J Adhes1999; 69: 59–82.
13.
OchsnerAGracioJ. An evaluation of the elastic properties of an adhesive layer using the tensile-butt joint test: procedures and error estimates. Int J Adhes Adhes2007; 27: 129–135.
14.
SeoDWLimJK. Tensile, bending and shear strength distributions of adhesive-bonded butt joint specimens. Compos Sci Technol2005; 65: 1421–1427.
15.
ChaudhuriRAChiuSHJ. Three-dimensional asymptotic stress field in the vicinity of an adhesively bonded scarf joint interface. Compos Struct2009; 89: 475–483.
16.
GunnionAJHerszbergI. Parametric study of scarf joints in composite structures. Compos Struct2006; 75: 364–376.
17.
BakerAAChesterRJHugoGR. Scarf repairs to highly strained graphite/epoxy structure. Int J Adhes Adhes1999; 19: 161–171.
18.
SuzukiY. Three-dimensional finite element analysis of adhesive scarf joints of steel plates loaded in tension. J Solid Mech Mater Eng1984; 27: 1836–1845.
19.
KimJHParkBJHanYW. Evaluation of fatigue characteristics for adhesively-bonded composite stepped lap joint. Compos Struct2004; 66: 69–75.
20.
KimHSLeeSJLeeDG. Development of a strength model for the cocured stepped lap joints under tensile loading. Compos Struct1995; 32: 593–600.
21.
FredricksonBMSchoeppnerGAMollenhauerDH. Application of three-dimensional spline variational analysis for composite repair. Compos Struct2008; 83: 119–130.
22.
KimHSLeeSJLeeDG. Development of a strength model for the co-cured stepped lap joints under tensile loading. Compos Struct1995; 32: 593–600.
23.
IchikawaKShinYSawaTA. Three-dimensional finite-element stress analysis and strength evaluation of stepped-lap adhesive joints subjected to static tensile loadings. Int J Adhes Adhes2008; 28: 464–470.
24.
KimJ-SKimCGHongCS. Practical design of tapered composite structures using the manufacturing cost concept. Compos Struct2001; 51(3): 285–299.
25.
da SilvaLFMAdamsRD. Techniques to reduce the peel stresses in adhesive joints with composites. Int J Adhes Adhes2007; 27(3): 227–235.
26.
KayeRHHellerM. Through-thickness shape optimisation of bonded repairs and lap-joints. Int J Adhes Adhes2002; 22(1): 7–21.
27.
MazumdarSKMallickK. Static and fatigue behavior of adhesive joints in SMC-SMC composites. Polym Compos1998; 19(2): 139–146.
28.
LangTMallickK. The effect of recessing on the stresses in adhesively bonded single-lap joints. Int J Adhes Adhes1999; 19(4): 257–271.
29.
LangTMallickK. Effect of spew geometry on stresses in single lap adhesive joints. Int J Adhes Adhes1998; 18(3): 167–177.
30.
WangCHHellerMRoseLRF. Substrate stress concentrations in bonded lap joints. J Strain Anal Eng Des1998; 33(5): 331–346.
31.
RisplerARTongLStevenGP. Shape optimisation of adhesive fillets. Int J Adhes Adhes2000; 20(3): 221–231.
32.
BelingardiGGoglioLTarditiA. Investigating the effect of spew and chamfer size on the stresses in metal/plastics adhesive joints. Int J Adhes Adhes2002; 22(4): 273–282.
33.
ZengQSunCT. Novel design of bonded lap joint. AIAA Journal2001; 39: 1991–1996.
34.
BaneaMDDASilva LFM. Adhesively bonded joints in composite materials: an overview. Proceedings of the Institution of Mechanical Engineers Part L Journal of Materials Design and Applications2009; 223(1): 1–18.
35.
ASTM D 3039-76. Standard test method for tensile properties of fiber-resin composites. West Conshohocken: American Society for Testing and Materials, 1989.
36.
ASTM D 3410-87. Standard test method for compressive properties of unidirectional or cross-ply fiber-resin composites. West Conshohocken: American Society for Testing and Materials, 1987.
37.
ASTM D 3846-79. Standard test method for in-plane shear strength of reinforced plastics. West Conshohocken: American Society for Testing and Materials, 1985.
38.
BaiYValleeTKellerT. Delamination of pultruded glass fiber-reinforced polymer composites subjected to axial compression. Compos Struct2009; 91: 66–73.
39.
KellerTValléeT. Adhesively bonded lap joints from pultruded GFRP profiles, Part II: Joint strength prediction. Composites Part B2005; 36: 341–350.
40.
ShrotriK. Development of tools for engineering analysis and design of high-performance FRP-composite structural elements. PhD Thesis, Georgia Institute of Technology, Georgia.
41.
KhosravanMRAzimpoorF. Numerical modeling of delamination in woven composites. In: The 16th International Conference of Composite Materials. Tokyo, 2007.
42.
ASTM D 2093-97. Preparation of surfaces of plastics prior to adhesive bonding. West Conshohocken: American Society for Testing and Materials, 1997.
43.
ASTM D1002. Apparent shear strength of single-lap-joint adhesively bonded metal specimens by tension loading. West Conshohocken: American Society for Testing and Materials, 1983.
44.
ASTM D3164-97. Strength properties of adhesively bonded plastic lap-shear sandwich joints in shear by tension loading. West Conshohocken: American Society for Testing and Materials, 1997.
45.
SukajitPSinghatanadgidP. Identification of buckling load of thin plate using the vibration correlation technique. In: The 21st Conference of Mechanical Engineering Network. Thailand, 2007.
46.
SharifiSChoupaniN. Stress analysis of adhesively bonded double-lap joints subjected to combined loading. J Eng Technol2008; 41: 758–763.
47.
TserpesKICinquinJPantelakisSp. On the mechanical performance of noncrimp fabric H-shaped adhesively bonded joints. J Compos Mater2011; 45(15): 1607–1619.
48.
TsaiSWHannHT. Introduction to composite materials. Lancaster, PA: Technomic, 1980.
49.
PanigrahiSKPradhanB. Three dimensional failure analysis and damage propagation behavior of adhesively bonded single lap joints in laminated FRP composites. J Reinf Plast Compos2007; 26: 183–201.
50.
RaghavaRSCadellRMYehGS. The macroscopic yield behavior of polymers. J Mater Sci1973; 8: 225–232.
51.
BeylergilBCunediogluYAktasA. Experimental and numerical analysis of single lap composite joints with inter-adherend fibers. Composites Part B2011; 42: 1885–1896.
52.
AktasAIrmekHCunediogluY. Experimental and numerical failure analysis of pinned-joints in composite materials. Compos Struct2009; 89: 459–466.