Temperature-dependent modulus of glass fiber/epoxy composite laminates was studied at temperatures ranging from room temperature up to 120℃. The storage modulus, loss modulus, loss factor, and glass transition temperature of two layer-up composite laminates were investigated by dynamic mechanic analysis. Static flexural modulus was also measured by control force mode in dynamic mechanic analysis. A new and simple temperature-dependent model both for the dynamic storage modulus and static flexural modulus was developed. This model depends only on one parameter which has specific physical meaning. The model prediction showed excellent agreement with our own experimental results over the full range of transition region. Furthermore, comparing our model’s prediction and other experimental data of many types of composites, which were studied by other researchers, we point to the fact that our model can be applied to many different polymer matrix composites.
KarbhariVM. Use of composite materials in civil infrastructure in Japan, Maryland: International Technology Research Institute, 1998.
2.
EindeLVDZhaoLSeibleF. Use of FRP composites in civil structural application. Constr Build Mater2003; 17(6–7): 389–403.
3.
BakisCE. Guide for the design and construction of externally bonded FRP systems for strengthening concrete structures, Michigan: Farmington Hills, 2002.
4.
HilalASAbousehlyAMDessoukyMT. Measurement of thermophysical properties of polyester cured with styrene in the range 300–450 K. J Appl Polym Sci1993; 49(4): 559–563.
5.
CaoSHWangXWuZS. Evaluation and prediction of temperature-dependent tensile strength of unidirectional carbon fiber-reinforced polymer composites. J Reinf Plast Compos2011; 30(9): 799–807.
6.
VlasveldDPNDaudWBerseeHEN. Continuous fibre composites with a nanocomposite matrix: Improvement of flexural and compressive strength at elevated temperatures. Composites Part A2007; 38(3): 730–738.
7.
OdegardGKumosaM. Elastic-plastic and failure properties of a unidirectional carbon/PMR-15 composite at room and elevated temperatures. Compos Sci Technol2000; 60(16): 2979–2988.
8.
MurayamaTBellPJ. Relation between the network structure and dynamic mechanical properties of a typical amine-cured epoxy polymer. J Polym Sci A21970; 8(3): 437–445.
9.
Van KrevelenDW. Properties of polymers, The Netherlands: Elsevier BV, 1990, pp. 399–402.
10.
GuPAsaroRJ. Structural buckling of polymer matrix composites due to reduced stiffness from fire damage. Compo Struct2005; 69(1): 65–75.
11.
DuttaPKHuiD. Creep rupture of a GFRP composite at elevated temperatures. Comput Struct2000; 76(1–3): 153–161.
12.
MahieuxCAReifsniderKL. Property modeling across transition temperatures in polymers: a robust stiffness temperature model. Polymer2001; 42(7): 3281–3291.
13.
ReifsniderKLMahieuxCA. Property modeling across transition temperatures in polymers: Application to filled and unfilled polybutadiene. J Elastomers Plast2002; 34(1): 79–89.
14.
GibsonAGWuYSEvansJT. Laminate theory analysis of composites under load in fire. J Compos Mater2006; 40(7): 639–658.
15.
Gibson AG, Browne TNA, Feih S, et al. Modeling composite high temperature behavior and fire response under load. J Compos Mater 2012; 46(16): 2005–2022.
16.
BaiYKellerT. Modeling of post-fire stiffness of E-glass fiber-reinforced polyester composites. Compos Part A2007; 38(10): 2142–2153.
17.
BaiYKellerTValleeT. Modeling of stiffness of FRP composites under elevated and high temperatures. Compos Sci Technol2008; 68(15–16): 3099–3106.
18.
BaiYKellerT. Time dependence of material properties of FRP composites in fire. J Compos Mater2009; 43(21): 2469–2484.
19.
Verhulst P-F. Notice sur la loi que la population poursuit dans son accroissement. Correspondance mathematique et physique 1838; 10: 113–121.
20.
FeihSMouritzAPMathysZ. Tensile strength modeling of glass fiber–polymer composites in fire. J Compos Mater2007; 41(19): 2387–2410.
21.
FeihSMathysZGibsonAG. Modeling the compression strength of polymer laminates in fire. Compos Part A2007; 38(11): 2354–2365.
22.
LiuJYZhouZGMaL. Temperature effects on the strength and crushing behavior of carbon fiber composite truss sandwich cores. Compos Part B2011; 42(7): 1860–1866.
23.
KandareEKandolaBKMylerP. Thermo-mechanical responses of fiber-reinforced epoxy composites exposed to high temperature environments. Part I: experimental data acquisition. J Compos Mater2010; 44(26): 3093–3114.
24.
KandareEKandolaBKMcCarthyED. Fiber-reinforced epoxy composites exposed to high temperature environments. Part II: modeling mechanical property degradation. J Compos Mater2010; 45(14): 1511–1521.
25.
Lee-SullivanPDykemanD. Guidelines for performing storage modulus measurements using the TA Instruments DMA 2980 three-point bend mode. I. Amplitude effects. Polym Test2000; 19(2): 155–164.
26.
ShaoQLee-SullivanP. Guidelines for performing storage modulus measurements using the TA Instruments DMA 2980 three-point bend mode. II. Contact stresses and machine compliance. Polym Test2000; 19(3): 239–250.
27.
AkayM. Aspects of dynamic mechanical analysis in polymer composites. Compos Sci Technol1993; 47(4): 419–423.
28.
TA instruments. Dynamic mechanical analyzer Q800 help, 2001.
29.
MenardK. Time-temperature scan: transition in polymers. Dynamic mechanical analysis: a practical introduction, chapter 5, Boca Raton FL: CRC Press, 1999.
30.
ASTM D790. Standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating materials, 2007.
31.
GoertzenWKKesslerMR. Dynamic mechanical analysis of carbon/epoxy composites for structural pipeline repair. Compos Part B2007; 38(1): 1–9.
32.
OnurCMustafaOTamerS. Effect of fiber orientation on viscoelastic properties of polymer matrix composites subjected to thermal cycles. Polym Compos2009; 31(3): 411–416.
33.
RayDSarkarBKDasS. Dynamic mechanical and thermal analysis of vinylester-resin-matrix composites reinforced with untreated and alkali-treated jute fibres. Compos Sci Technol2002; 62(7–8): 911–917.
34.
VilayVMariattiMMat TaibR. Effect of fiber surface treatment and fiber loading on the properties of bagasse fiber–reinforced unsaturated polyester composites. Compos Sci Technol2008; 68(3–4): 631–638.