Biodegradability of wood fiber/poly(lactic acid) composites

Abstract

Wood fiber/poly(lactic acid) composites with 70 wt% wood fiber were prepared using a super mixing-hot press method. The biodegradability of composite panels made with one unmodified and three types of modified poly(lactic acid) was evaluated by comparing the mechanical strength, molecular weight, thermal properties and microstructures of composite wood fiber/poly(lactic acid) and 100% poly(lactic acid) panels before and after burial in soil. We found that wood fiber/poly(lactic acid) composites degraded more readily than 100% poly(lactic acid) panels during burial. The type of poly(lactic acid) used in wood fiber/poly(lactic acid) composites affected biodegradability. The flexural strength and modulus of wood fiber/poly(lactic acid) panels decreased sharply after burial in soil for 6 months. The molecular weight of poly(lactic acid) in wood fiber/poly(lactic acid) composites decreased more rapidly than 100% poly(lactic acid) panels that had been buried in soil for 6 months. Changes were observed in both the amorphous and crystalline structure of specimens buried in soil. The wood fiber/poly(lactic acid) composites prepared with unmodified poly(lactic acid) have better mechanical properties and degraded more easily during burial than did composites made with modified poly(lactic acid).

Keywords

Biodegradability burial test wood fiber poly(lactic acid)composites

Get full access to this article

View all access options for this article.

References

Garlotta

. A literature review of poly(lactic acid). J Polymer Environ 2001; 9(2): 63–84.

Lunt

. Lagre-scale production, properties and commercial applications of polylactic acid polymers. Polymer Degrad Stabil 1998; 59: 145–152.

Plackett

Andersen

Pedersen

. Biodegradable compsites based on L-polylactide and jute fibres. Compos Sci Technol 2003; 63: 1287–1296.

Huda

Drzal

Misra

. Wood-fiber-reinforced poly(lactic acid) composites: evaluation of the physicomechanical and morphological properties. J Appl Polym Sci 2006; 102: 4856–4869.

Oksman

Skrifvars

Selin

J-F

. Natural fibres as reinforcement in polylactic acid (PLA) composites. Compos Sci Technol 2003; 63: 1317–1324.

Nishino

Hirao

Kotera

. Kenaf reinforced biodegradable composite. Compos Sci Technol 2003; 63: 1281–1286.

Lee

Wang

. Biodegradable polymer/bamboo fiber biocomposite with bio-based coupling agent. Compos Part A 2006; 37: 80–91.

Teramoto

Urata

Ozawa

. Biodegradation of aliphatic polyerster composites renforced by abaca fiber. Polym Degrad Stabil 2004; 86: 401–409.

Tserki

Matzinos

Panayiotou

. Effect of compatibilization on the performance of biodegradable composites using cotton fiber waste as filler. J Appl Polym Sci 2003; 88: 1825–1835.

10.

Kim

Lee

. Biodegradability of bio-flour filled biodegradable poly(butylene succinate) bio-composites in natural and compost soil. Polymer Degrad Stabil 2006; 91: 1117–1127.

11.

Peterson

Jayaraman

Bhattacharyya

. Forming performance and biodegradability of woodfibre-Biopol ™ composites. Compos Part A 2002; 33: 1123–1134.

12.

McCarthy

. Further investigations on the hydrolytic degradation of poly(DL-lactide). Biomaterials 1999; 20: 35–44.

13.

Guo

Bao

Wang

. Effects of compounding modes on structure and properties of wood fiber-poly(lactic acid) bio-composites. J Beijing Forestry University 2009; 31(4): 106–111.

14.

Kulinski

Piorkowska

. Crystallization, structrure and properties of plasticized poly(L-lactide). Polymer 2005; 46: 10290–10300.

15.

Chen

Dong

. Macromolecular physics [M] , Shanghai: Fudan University Press, 2004, pp. 252–256.