Evaluation of the prestressing effects on the fatigue life of composite box sections

Abstract

Fatigue tests were conducted on non-prestressed and prestressed composite box sections. The approach to prestressing of composite structures seeks to eliminate compressive stress excursions under fatigue loading. This approach increased the fatigue life of composite structures; the experimental gains in fatigue life were in agreement with theoretical prediction. The tensile prestress developed in the composite structure mitigate compressive stress excursions under fatigue load, which significantly enhance the fatigue life of composites. Flexural fatigue tests were conducted through repeated application of a constant deformation, with the maximum load level monitored throughout the tests. The repeated (constant) deformation was selected to produce 70% of the ultimate (quasi-static) flexural strength of each of the prestressed and non-prestressed composite box sections. Two prestressed and two non-prestressed specimens were tested under (displacement controlled) fatigue loading–unloading conditions. The fatigue life of non-prestressed composite sections was reached upon local buckling of top flange (which experienced the maximum compressive stress). For both non-prestressed and prestressed composite sections, failure was defined as the number of cycles after which the peak load (at constant repeated deformation) dropped to 70% of the value in the first cycle. The fatigue life of prestressed composite sections was about 100% greater than that of non-prestressed sections. The residual strength of prestressed sections after fatigue loads was, on the average, 56% greater than that of non-prestressed sections. The experimental results indicated that contribution of prestressing to the fatigue life of composite sections was significant.

Keywords

Prestressing composite structures fatigue life compressive stress

Get full access to this article

View all access options for this article.

References

Buch

. Prediction of the comparative fatigue performance for realistic loading distributions. Prog Aerosp Sci 1997; 33(5–6): 391–430.

Riks

. Buckling and post-buckling analysis of stiffened panels in wing box structures. Int J Solids Struct 2000; 37(46): 6795–6824.

Goutianos

Peijs

Galiotis

. Comparative assessment of stress transfer efficiency in tension and compression. Composites Part A 2002; 33(10): 1303–1309.

Bai

Phoenix

. Compressive failure model for fiber composites by kink band initiation from obliquely aligned, shear-dislocated fiber breaks. Int J Solids Struct 2005; 42(7): 2089–2128.

Effendi

Barrau

Guedra-Degeorges

. Failure mechanism analysis under compression loading of unidirectional carbon/epoxy composites using micromechanical modelling. Compos Struct 1995; 31(2): 87–98.

Butler

Almond

Hunt

. Compressive fatigue limit of impact damaged composite laminates. Composites Part A 2007; 38(4): 1211–1215.

Kardomateas

Pelegri

Malik

. Growth of internal delaminations under cyclic compression in composite plates. J Mech Phys Solids 1995; 43(6): 847–868.

Van Paepegem

Degrieck

. Tensile and compressive damage coupling for fully-reversed bending fatigue of fibre-reinforced composites. Fatigue Fract Eng Mater Struct 2002; 25(6): 547–561.

Caprino

D’Amore

. Fatigue life of graphite/epoxy laminates subjected to tension-compression loadings. Mech Time-Depend Mater 2000; 4(2): 139–154.

10.

Butler

. Optimum design of composite stiffened wing panels - a parametric study. Aeronaut J 1995; 99(985): 169–177.

11.

Akerman

. Sustainable air transport - on track in 2050. Transp Res Part D: Transp Environ 2005; 10(2): 111–126.