An atmospheric pressure helium and oxygen plasma has been used for the surface preparation of 410 stainless steel and carbon-fiber epoxy laminates prior to bonding to themselves or to each other. Lap shear results for stainless steel coupons and carbon-fiber epoxy laminates demonstrated an 80% and a 150% increase in bond strength, respectively, after plasma activation. Following 7 days of aging, wedge crack extension tests revealed a crack extension length of 7.0 mm and 2.5 mm for the untreated and plasma-activated steel. The untreated stainless steel had 30% cohesive failure compared to 97% for steel activated with the plasma. Surface analysis by X-ray photoelectron spectroscopy showed that carbonaceous contamination was removed by plasma treatment, and specific functional groups, e.g. carboxylic acids, were formed on the surface. These functional groups promoted strong chemical bonding to the epoxy film adhesive. Atmospheric pressure plasmas are an attractive alternative to abrasion techniques for surface preparation prior to bonding.
BroadRFrenchJSauerJ. CLP – new, effective, ecological surface pretreatment for highly durable adhesively bonded metal joints. Int J Adhes Adhes1999; 19(2–3): 193–198.
2.
MatsumuraHTanakaTAtsutaM. Effect of acidic primers on bonding between stainless steel and auto-polymerizing methacrylic resins. J Dentist1997; 25(3–4): 285–290.
3.
McNamaraDKAhearnJS. Adhesive bonding of steel for structural applications. Int Mater Rev1987; 32(6): 292–306.
4.
SakataFYSantoAMEMiyakawaW. Influence of laser surface texturing on surface microstructure and mechanical properties of adhesive joined steel sheets. Surf Eng2009; 25(3): 180–186.
5.
HigginsA. Adhesive bonding of aircraft structures. Int J Adhes Adhes2000; 20(5): 367–376.
6.
ParkSYChoiWJChoiHS. Recent trends in surface treatment technologies for airframe adhesive bonding processing: a review (1995-2008). J Adhes2010; 86(2): 192–221.
7.
DavisMBondD. Principles and practices of adhesive bonded structural joints and repairs. Int J Adhes Adhes1999; 19(2–3): 91–105.
8.
GrujicicMSellappanVPanduranganB. Computational analysis of injection-molding residual-stress development in direct-adhesion polymer-to-metal hybrid body-in-white components. J Mater Process Technol2008; 203(1–3): 19–36.
9.
GrujicicMSellappanVOmarMA. An overview of the polymer-to-metal direct-adhesion hybrid technologies for load-bearing automotive components. J Mater Process Technol2008; 197(1–3): 363–373.
10.
GrujicicMSellappanVArakereG. The potential of a clinch-lock polymer metal hybrid technology for use in load-bearing automotive components. J Mater Eng Perform2009; 18(7): 893–902.
11.
FabrinPAHoikkanenMEVuorinenJE. Adhesion of thermoplastic elastomer on surface treated aluminum by injection molding. Polym Eng Sci2007; 47(8): 1187–1191.
12.
PetrieEM. Adhesive bonding of aluminum alloys. Metal Finish2007; 105(9): 49–56.
13.
ProlongoSGdel RosarioGUrenaA. Comparative study on the adhesive properties of different epoxy resins. Int J Adhes Adhes2006; 26(3): 125–132.
14.
HarrisEWMasseyJTChengD. Atmospheric plasma effects on structural adhesive bonding. SAMPE spring technical conference proceedings, Long Beach, CA, 23--26 May 20112011.
15.
CritchlowGWBrewisDM. Review of surface pretreatments for aluminium alloys. Int J Adhes Adhes1996; 16(4): 255–275.
16.
ZaldivarRJKimHISteckelGL. Effect of processing parameter changes on the adhesion of plasma-treated carbon fiber reinforced epoxy composites. J Compos Mater2010; 44(12): 1435–1453.
17.
RiderAN. Surface treatments for field level bonded repairs to aluminium and titanium structure, Fishermans Bend, Victoria: Defense Science and Technology Organization, 2008.
18.
J.D. Lincoln, Inc. Solution coated epoxy prepreg. MSDS No. L-929. Costa Mesa, CA: J.D. Lincoln, Inc., 2004.
19.
GonzalezEBarankinMDGuschlPC. Remote atmospheric-pressure plasma activation of the surfaces of polyethylene terephthalate and polyethylene naphthalate. Langmuir2008; 24(21): 12636–12643.
20.
GonzalezEBarankinMDGuschlPC. Ring opening of aromatic polymers by remote atmospheric-pressure plasma. IEEE Transact Plasma Sci2009; 37(6): 823–831.
21.
Hicks RF, Babayan SE, Penelon J, et al. Atmospheric plasma treatment of polyetheretherketone composites for improved adhesion. In: SAMPE fall technical conference proceedings, Dallas, TX, 6--9 November 2006.
22.
GonzalezEHicksRF. Surface analysis of polymers treated by remote atmospheric pressure plasma. Langmuir2010; 26(5): 3710–3719.
23.
ASTM D 3165-07. Standard test method for strength properties of adhesives in shear by tension loading of single-lap-joint laminated assemblies. Annual Book of ASTM Standards. Philadelphia, PA: ASTM International, 2001, pp.221–224.
24.
ASTM D 7136. Standard test method for measuring the damage resistance of a fiber-reinforced polymer matrix composite to a drop-weight impact event. Annual Book of ASTM Standards. Philadelphia, PA: ASTM International, 2001, 479–494.
25.
ASTM D 3762-03. Standard test method for adhesive-bonded surface durability of aluminum (wedge test). Annual Book of ASTM Standards, 277-280. Philadelphia, PA: ASTM International, 2001.
26.
ZaldivarRJNokesJSteckelGL. The effect of atmospheric plasma treatment on the chemistry, morphology and resultant bonding behavior of a pan-based carbon fiber-reinforced epoxy composite. J Compos Mater2010; 44(2): 137–156.
27.
WagnerCDRiggsWMDavisLE. Handbook of X-ray photoelectron spectroscopy, Eden Prairie, MN: Perkin-Elmer Corporation, 1979, pp. 38–76.
28.
KurbatovGDarquecerettiEAucouturierM. Characterization of hydroxylated oxide film on iron surfaces and its acid-base properties using XPS. Surf Interf Anal1992; 18(12): 811–820.
29.
Tien-ChihLSeshadriGKelberJA. A consistent method for quantitative XPS peak analysis of thin oxide films on clean polycrystalline iron surfaces. Appl Surf Sci1997; 119(1–2): 83–92.
30.
MantelMWightmanJP. Influence of the surface chemistry on the wettability of stainless steel. Surf Interf Anal1994; 21(9): 595–605.
31.
TangSLuNMyungSW. Enhancement of adhesion strength between two AISI 316 L stainless steel plates through atmospheric pressure plasma treatment. Surf Coat Technol2006; 200(18–19): 5220–5228.
32.
KocijanADonikCJenkoM. Electrochemical and XPS studies of the passive film formed on stainless steels in borate buffer and chloride solutions. Corrosion Sci2007; 49(5): 2083–2098.
33.
DescostesMMercierFThromatN. Use of XPS in the determination of chemical environment and oxidation state of iron and sulfur samples: constitution of a data basis in binding energies for Fe and S reference compounds and applications to the evidence of surface species of an oxidized pyrite in a carbonate medium. Appl Surf Sci2000; 165(4): 288–302.
34.
StypulaBStochJ. The characterization of passive films on chromium electrodes by XPS. Corrosion Sci1994; 36(12): 2159–2167.
35.
GonzalezEBarankinMDGuschlPC. Surface activation of poly(methyl methacrylate) via remote atmospheric pressure plasma. Plasma Process Polym2010; 7(6): 482–493.
36.
LimHLeeYHanS. Surface treatment and characterization of PMMA, PHEMA, and PHPMA. J Vacuum Sci Technol A2001; 19(4): 1490–1496.
37.
BusscherHJVanpeltAWJDeboerP. The effect of surface roughening of polymers on measured contact angles of liquids. Coll Surf1984; 9(4): 319–331.
38.
WakeWC. Theories of adhesion and uses of adhesives: a review. Polymer1978; 19(3): 291–308.
39.
AllenKW. Some reflections on contemporary views of theories of adhesion. Int J Adhes Adhes1993; 13(2): 67–72.
40.
BaldanA. Adhesively-bonded joints and repairs in metallic alloys, polymers and composite materials: adhesives, adhesion theories and surface pretreatment. J Mater Sci2004; 39(1): 1–49.
41.
WalterssonK. ESCA studies of carbon fibers: part II—surface reactions of carbon fibers with epoxides. Compos Sci Technol1985; 22(3): 223–239.
42.
WalterssonK. ESCA studies of carbon fibers: part III—surface reactions of carbon fibers with amines. Compos Sci Technol1985; 23(4): 303–321.
43.
KozlowskiCSherwoodPMA. X-ray photoelectron spectroscopic studies of carbon fiber surfaces VIII—a comparison of type I and type II fibers and their interaction with thin resin films. Carbon1987; 25(6): 751–760.
44.
NakazawaMSomorjaiGA. Coadsorption of water and selected aromatic molecules to model the adhesion of epoxy resins on hydrated surfaces of zinc oxide and iron oxide. Appl Surf Sci1995; 84(3): 309–323.
45.
GlazerJ. Monolayer studies of some ethoxylin resin adhesives and related compounds. J Polym Sci1954; 13(70): 355–369.