Compression after impact strength of thin laminates with various percentage of 0° plies

Abstract

Conventional wisdom dictates that adding more 0° plies in the load-bearing direction of a laminate will increase its stiffness and strength. While this is true for undamaged laminates, the compression strength of laminates with impact damage may not be as straightforward. In this study, compression after impact strengths of relatively thin laminates with 25%, 33% or 50% of plies aligned in the 0° load-bearing direction were measured for three different damage severity levels. Results show that the increase in compression strength of the laminates with a higher percentage of plies in the 0° direction is lessened as impact damage severity increases indicating that a laminate that is stronger in compression when undamaged may not be stronger in compression when impact damage is accounted for.

Keywords

Compression damage tolerance impact

Get full access to this article

View all access options for this article.

References

Nettles

Jackson

. Compression after impact testing of sandwich composites for usage on expendable launch vehicles. J Compos Mater 2010; 44: 707–738.

Kan HP, Cordero R and Whitehead RS. Advanced certification methodology for composite structures. Final Contract Report DOT/FAA/AR-96/111, April 1997.

Krober I. Effect of impacts on CFRP structures, results of a comprehensive test program for practical use. In: Proceedings AGARD CP-530, Patras, Greece, 24--29 May 1992, pp.29.1–29.6.

Guynn EG and O'Brien TK. The influence of lay-up and thickness on composite impact damage and compression strength. In: Proceedings of the 26th AIAA/ASME/ASCE/AHS/ASC structures, structural dynamics and materials conference, Orlando, FL, 15–17 April 1985, pp.187–196.

Reis

de Freitas

. Damage growth analysis of low velocity impacted composite panels. Compos Struct 1997; 38: 509–515.

Hitchen

Kemp

RMJ

. The effect of stacking sequence in impact damage in a carbon fiber/epoxy composite. Composites 1995; 26: 207–214.

Soutis

Curtis

Fleck

. Compressive failure of notched carbon fiber composites. Proc Math Phys Sci 1993; 1909: 241–256.

Nettles AT, Jackson JR and Gates TS. Compression after impact testing of sandwich structures using a four point bend test. In: Proceedings, SAMPE fall technical conference and exhibition, Memphis, TN, 8–11 September 2008.

Tomblin

Raju

. Material qualification and equivalency for polymer matrix composite material systems. Final Contract Report DOT/FAA/AR-00/47, April 2001,, Washington, DC: Office of Aviation Research, 2001.

10.

Nettles

Jackson

. Developing a material strength design value based on compression after impact (CAI) damage for the ARES I composite interstage, NASA/TP-2009-215634, Marshall Space Flight Center, AL 35812, USA, January 2009, 2009.

11.

ASTM D6484/D6484M. Standard test method for open-hole compressive strength of polymer matrix composite laminates. Annual Book of ASTM Standards, Vol. 15.03, West Conshohocken, PA: American Society for Testing and materials, 2007.

12.

ASTM D7137/D7137M. Standard test method for impact strength of polymer matrix composite laminates. Annual Book of ASTM Standards, Vol. 15.03, West Conshohocken, PA: American Society for Testing and materials, 2012.