Experimental characterization of multistitched two-dimensional (2D) woven E-glass/polyester composites under low-velocity impact load

Abstract

The aim of this study was to understand the low-velocity impact energy absorption mechanism of the developed two-dimensional multistitched multilayer E-glass/polyester-woven composites. It was found that the specific front and back face damaged areas of the two-dimensional multistitched E-glass/polyester-woven composites were smaller than those of the two-dimensional unstitched structures. When the stitching density increases, the front and back face damaged areas generally decrease. In addition, when the number of stitching directions increased, the front and back face damaged areas decreased. Therefore, stitching density, stitching directions, stitching yarn, and stitching type on the composite structures were considered as important parameters. Impact load caused a small indentation in the center of front face and resulted in fiber splitting and fiber breakages in the center of the back face of the structure. On the surrounding area of the front and back face damaged zones of the structures, fiber-matrix debonding and matrix breakages were observed. These results indicated that multistitching suppressed the impact energy to a small area of the composite structure. Thus, the two-dimensional Kevlar®129 or E-glass-multistitched E-glass/polyester-woven composite structures showed better damage tolerance performance compared to the unstitched composite structures.

Keywords

Multistitched-woven composite low-velocity impact energy absorption damaged area E-glass woven fabric

Get full access to this article

View all access options for this article.

References

Kang

Lee

. Effect of stitching on the mechanical and impact properties of woven laminate composite. J Compos Mater 1994; 28: 1574–1587.

Mouritz

Gallagher

Goodwin

. Flexural and interlaminar shear properties of stitched GRP laminates following repeated impacts. Compos Sci Technol 1997; 57: 509–522.

Farley

Dickinson

. Removal of surface loop from stitched composites can improve compression and compression-after-impact strengths. J Reinf Plast Compos 1992; 11: 633–642.

Wang

. Behavior of stitched laminates under in-plane tensile and transverse impact loading. J Compos Mater 1995; 29: 2254–2279.

Tan

Watanabe

Iwahori

. Impact damage resistance, response, and mechanisms of laminated composites reinforced by through-thickness stitching. Int J Damage Mech 2012; 21: 51–80.

Tan

Watanabe

Iwahori

. X-ray radiography and micro-computed tomography examination of damage characteristics in stitched composites subjected to impact loading. Composites Part B 2011; 42: 874–884.

Chen

Kou

. Finite element analysis of low-velocity impact damage of stitched laminates. J Reinf Plast Compos 2004; 23: 987–995.

Xiaoquan

Al-Mansour

Zhengneng

. Compression strength of stitched laminates after low-velocity impact. J Reinf Plast Compos 2005; 24: 935–947.

Tan

Watanabe

Iwahori

. Understanding effectiveness of stitching in suppression of impact damage: an empirical delamination reduction trend for stitched composites. Composites Part A 2012; 43: 823–832.

10.

Hosur

Karim

Jeelani

. Experimental investigations on the response of stitched/unstitched woven S2-glass/SC15 epoxy composites under single and repeated low velocity impact loading. Compos Struct 2003; 61: 89–102.

11.

Baucom

Zikry

. Low-velocity impact damage progression in woven E-glass composite systems. Composites Part A 2005; 36: 658–664.

12.

Mouritz

. Ballistic impact and explosive blast resistance of stitched composites. Composites Part B 2001; 32: 431–439.

13.

Liu

. Delamination resistance in stitched and unstitched composite plates subjected to impact loading. J Reinf Plast Compos 1990; 9: 59–69.

14.

Yoshimura

Nakao

Yashiro

. Improvement on out-of-plane impact resistance of CFRP laminates due to through-the-thickness stitching. Composites Part A 2008; 39: 1370–1379.

15.

Hosur

Karim

Jeelani

. Studies on stitched woven S2 glass/epoxy laminates under low velocity and ballistic impact loading. J Reinf Plast Compos 2004; 23: 1313–1323.

16.

Hosur

Abraham

Jeelani

. Studies on the influence of through-the-thickness reinforcement on low-velocity and high strain rate response of woven S2-glass/vinyl ester composites. J Compos Mater 2001; 35: 1111–1133.

17.

Liau

. Impact of unstitched and stitched laminates by line loading. J Compos Mater 1994; 28: 1640–1658.

18.

Gellert

Cimpoeru

Woodward

. A study of the effect of target thickness on the ballistic perforation of glass-fiber-reinforced plastic composites. Int J Impact Eng 2000; 24: 445–456.

19.

Naik

Shrirao

. Composite structures under ballistic impact. Compos Struct 2004; 66: 579–590.

20.

Hosur

Adya

Alexander

. Studies on impact damage resistance of affordable stitched woven carbon/epoxy composite laminates. J Reinf Plast Compos 2003; 22: 927–952.

21.

Hosur

Vaidya

Ulven

. Performance of stitched/unstitched woven carbon/epoxy composites under high velocity impact loading. Compos Struct 2004; 64: 455–466.