Effect of data reduction and fiber-bridging on Mode I delamination characterization of unidirectional composites

Abstract

Reliable delamination characterization data for laminated composites are needed for input in analytical models of structures to predict delamination onset and growth. The double-cantilevered beam specimen is used to measure fracture toughness, G_Ic, and strain energy release rate, G_Imax, for delamination onset and growth in laminated composites under Mode I loading. The current study was conducted as part of an ASTM Round Robin activity to evaluate a proposed testing standard for Mode I fatigue delamination propagation. Static and fatigue tests were conducted on specimens of IM7/977-3 and G40-800/5276-1 graphite/epoxies, and S2/5216 glass/epoxy double-cantilevered beam specimens to evaluate the draft standard “Standard Test Method for Mode I Fatigue Delamination Propagation of Unidirectional Fiber-Reinforced Polymer Matrix Composites.” Static results were used to generate a delamination resistance curve, G_IR, for each material, which was used to determine the effects of fiber-bridging on the delamination growth data. All three materials were tested in fatigue at a cyclic G_Imax level equal to 90% of the fracture toughness, G_Ic, to determine the delamination growth rate. Two different data reduction methods, a two-point and a seven-point fit, were used and the resulting Paris Law equations were compared. Growth rate results were normalized by the delamination resistance curve for each material and compared to the non-normalized results. Paris Law exponents were found to decrease by 5.7 to 47.6% due to normalizing the growth data. Additional specimens of the IM7/977-3 material were tested at three lower cyclic G_Imax levels to compare the effect of loading level on delamination growth rates. The IM7/977-3 tests were also used to determine the delamination threshold curve for that material. The results show that tests at a range of loading levels are necessary to describe the complete delamination behavior of this material.

Keywords

Composites fracture toughness fatigue Paris Law delamination strain energy release rate R-curve

Get full access to this article

View all access options for this article.

References

ASTM D 5528-01. Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites. In: Annual Book of ASTM Standards 2008; Vol. 15.03Philadelphia: American Society for Testing and Materials.

ASTM D 6115-97. Standard Test Method for Mode I Fatigue Delamination Growth Onset of Unidirectional Fiber-Reinforced Polymer Matrix Composites. In: Annual Book of ASTM Standards 2008; Vol. 15.03Philadelphia: American Society for Testing and Materials.

Standard Test Method for Mode I Fatigue Delamination Propagation of Unidirectional Fiber-Reinforced Polymer Matrix Composites. Draft standard, ASTM International, Committee D30 on Composites, 2009. West Conshohocken, PA, USA.

Martin

Murri

Characterization of Mode I and Mode II Delamination growth and thresholds in AS4/PEEK composites. In: Garbo

(eds). Composite materials: testing and design (ninth volume), ASTM STP 1059, Philadelphia: American Society for Testing and Materials, 1990, pp. 251–270.

O’Brien

Towards a damage tolerance philosophy for composite materials and structures. In: Garbo

(eds). Composite materials: testing and design (ninth volume), ASTM STP C1059, Philadelphia: American Society for Testing and Materials, 1990, pp. 7–33.

Russell

Street

A constant ΔG test for measuring Mode I interlaminar fatigue crack growth rates. In: Whitcomb

(eds). Composite materials: testing and design (eighth conference), ASTM STP 972, Philadelphia: American Society for Testing and Materials, 1988, pp. 259–277.

Johnson

Mangalgiri

. Investigation of fiber bridging in double cantilever beam specimens. J Compos Technol Res 1987; 9: 10–13.

Poursartip

Characterization of edge delamination growth in laminates under fatigue loading. In: Johnston

(eds). Toughened composites, ASTM STP 937, Philadelphia: American Society for Testing and Materials, 1987, pp. 222–241.

Fatigue fracture toughness. In: Composite materials handbook CMH-17, Rev. G, Vol. 1, Section 6.9.4, SAE International, 2012.

10.

Shivakumar

Chen

Abali

. A total fatigue life model for Mode I loaded composite laminates. Int J Fatigue 2006; 28: 33–42.

11.

ASTM D 5229/D 5229 M-92. Standard test method for moisture absorption properties and equilibrium conditioning of polymer matrix composite materials. In: Annual book of ASTM standards 2008; Vol. 15.03Philadelphia: American Society for Testing and Materials.

12.

ASTM E 647-00. Standard test method for measurement of fatigue crack growth rates. In: Annual book of ASTM standards 2000; Vol. 03.01Philadelphia: American Society for Testing and Materials.

13.

Giannis S, Hansen K and Martin RH. Accounting for the R-curve effects on the Mode I fatigue delamination growth characterisation of unidirectional composites. In: Proceedings of the American Society for composites, Twenty-fifth Technical Conference, September 20--22, 2010, Dayton, Ohio.